漆酶-介体系统处理麦草化学浆全无氯漂白性能的研究

采用漆酶－介体系统对麦草化学浆进行预处理，研究了几种全无氯漂白（TCF漂白）[氧碱脱木质素配合两段过氧化氢漂白（OEPP），两段过氧化氢漂白（QPP）和过乙酸配合一段过氧化氢漂白(PaP)]对漆酶处理后纸浆漂白性能的作用，结果表明，麦草浆经过漆酶预处理后，白度上升了12．9个白度单位（%,ISO)，漆酶处理浆氧碱脱木质素配合过氧化氢漂白后比原浆在相同条件下漂白后白度高14个白度单位以上，经两段过氧化氢漂白后白度比原浆在相同条件下（过氧化氢用量4％）漂白后白度高18．3个白度单位，经过乙酸过氧化氢漂白后比原浆在相同条件下漂白后白度高8．1个白度单位。漆酶处理浆漂白后强度比原浆漂白后的低，但是其白度高，如漂至相同的白度可以节约大量漂剂，有利于改善浆的质量，降低漂白废水的污染负荷。     

新型绿色糖单孢菌复合胞外酶对比纯木聚糖酶助漂杨木KP浆研究

用绿色糖单孢菌复合胞外酶和纯木聚糖酶分别对三倍体毛白杨KP浆进行单段酶预处理及后续ECF、TCF漂白,结果发现,绿色糖单孢菌复合胞外酶助漂效果明显,接后续漂白可制得白度均高于85%ISO,粘度保持在1000mL/g左右的高白度、高强度、低氯和无氯全漂浆.相对传统纯木聚糖酶助漂,复合胞外酶在提高纸浆白度方面表现更佳,在保持纸浆粘度方面效果稍差.此外,三倍体毛白杨制浆漂白性能良好,ECF碱抽提段加入0.5%的H2O2可强化碱抽提效果,氧脱木素作用明显,是TCF漂白必不可少的组成部分.     

E－An－76在桦木KP浆及麦草Soda－AQ浆CEH三段漂中的应用

研究了半纤维素酶Ｅ－Ａｎ－７６作为漂白助剂对桦木硫酸盐浆及麦草烧碱蒽醌浆ＣＥＨ三段漂的影响。结果表明：桦木ＫＰ浆用Ｅ－Ａｎ－７６预处理后再经ＣＥＨ三段漂，其白度明显高于相同用氯量下未用酶预处理的漂白浆。另一方面在保持白度不变的情况下酶处理浆的漂白可节省近５０％的用氯量。麦草Ｓｏｄａ－ＡＱ浆经Ｅ－Ａｎ－７６预处理后再经ＣＥＨ三段漂与酶未处理浆的ＣＥＨ三段漂比较亦可明显提高白度，但得率下降严重。通过对桦木ＫＰ浆酶解液中还原糖以及单糖组成分析，发现浆中再沉积或回吸的木聚糖在Ｅ－Ａｎ－７６助剂漂白中起着重要作用。     

碱性木聚糖酶在中小径竹KP浆漂白中的应用

探讨碱性木聚糖酶用于中小径竹KP浆漂白预处理的最佳工艺条件及碱性木聚糖酶预处理对中小径竹KP浆ECF漂白的影响.结果表明,碱性木聚糖酶Unikfect 100处理浆的最佳工艺为:浆浓度4%,pH值9.0,温度65℃,时间20 min,酶用量15.0×10-7 mol·s-1g-1浆;对ECF漂白的影响为:O-X-D1-EOP-D2漂序的漂白效果优于O-D/C-EOP-D2,在白度相近的情况下,纸浆的粘度及物理强度较高.     

漂白稳定剂的研究

对改性蛋白石用作纸浆H2O2漂白稳定剂的可能性进行了考察，结果表明，纸浆H2O2漂白过程中采用改性蛋白石替代Na2SiO3作稳定剂是可行的。在相同用量下，麦草浆和脱墨浆的白度均可提高3％(ISO)以上。与蛋白石相比，改性蛋白石对纸浆H2O2漂白的稳定效能显著增强。对于改性蛋白石作稳定剂的纸浆H2O2漂白，在一定范围内提高温度和延长时间对漂白有利。适宜的工艺条件为：浆浓10％，H2O23％，NaOH1．5％，改性蛋白石3％，时间60min，温度70℃以上。在此条件下漂白麦草浆，白度增值可达16％(ISO)以上。此外，改性蛋白石用作纸浆H2O2漂白稳定剂时，添加少量MgSO4对漂白有利，添加0．05％MgSO。可提高纸浆白度约1％(ISO)。     

E—An—76在桦木KP浆及麦草Soda—AQ浆CEM三段漂中的应用

研究了半纤维素酶Ｅ－Ａｎ－７６作为漂白助剂对桦木硫酸盐浆及麦草烧碱蒽醌浆ＣＥＨ三段漂的影响。结果表明，桦木ＫＰ浆用Ｅ－Ａｎ－７６处理后再经ＣＥＨ三段漂，其白度明显高于相同用氯量下未用酶预处理的漂白浆。另一方面在保持白主东变的情况下酶处理浆的漂白节省近５０％的用氯量。     

内切木聚糖酶与木糖苷酶预处理对麦草浆漂白性能的影响

研究了内切木聚糖酶与木糖苷酶预处理对麦草浆漂白性能的影响。结果表明，无论是内切木聚糖酶还是木糖苷酶预处理漂白浆的白度均比对照浆高，分别高出对照浆的2．5和1．9个百分点，同时漂白浆的强度也好于对照浆的强度。内切木聚糖酶和木糖苷酶混合预处理漂白浆的白度分别比内切木聚糖酶和木糖苷酶高出0．9和1．5个百分点，这表明内切木聚糖酶和木糖苷酶在纸浆预处理过程中具有协同作用。通过电镜观察发现经内切木聚糖酶和木糖苷酶预处理后纸浆的表面和横断面有许多孔隙，其中经内切木聚糖酶预处理后纸浆的孔隙比木糖苷酶要多而且大。通过X-射线衍射分析发现内切木聚糖酶和木糖苷酶均不能破坏纸浆的结晶度。     

马尾松TMP漂白性能的研究

对马尾松热磨机械浆(TMP)进行了过氧化氢(H2O2)、甲脒亚磺酸盐(FAS)单段漂白以及H2O2-FAS两段漂白实验的研究。结果表明,H2O2漂白马尾松TMP较适宜的工艺条件为H2O2用量2.5%,NaOH用量1.3%,Na2SiO3用量2.5%,浆浓20%,温度80℃,时间60min;FAS漂白马尾松TMP较适宜的工艺条件为FAS用量2.5%,NaOH用量0.625%,浆浓15%,温度80℃,时间75min。H2O2、FAS单段漂白后纸浆白度分别为72.6%ISO和58.2%ISO,H2O2-FAS两段漂白后纸浆白度可达76.3%ISO。     

麦草氧碱法纸浆压力/温度过氧化氢漂白

麦草氧碱法纸浆经压力/温度H2O2(Ppt)漂白时,纸浆的卡伯值随H2O2用量和氧压的提高而下降,卡伯值从17.3下降至2.38,下降幅度达86.2 %,表明Ppt漂白时,脱木质素效果明显.若采用氧脱木质素 -鳌合处理 -压力温度H2O2漂白(OQPpt)和氧脱木质素 -酸处理 -压力温度H2O2(OAPpt)漂程,当H2O2用量为原料质量的3 %～4 %时,均可将麦草氧碱纸浆漂至白度80 %(SBD,以下同)左右,而采用OAPpt漂白比OQPpt漂白的纸浆的白度高2.0 %左右,且聚合度达到1 038左右.     

新疆杨幼龄材带皮硫酸盐法化学浆漂白性能的研究

研究了新疆杨木１～３年生带皮硫酸盐法化学浆的漂白规律。结果表明：采用单段和二段次氯酸盐漂白，漂后浆白度较低，分别为６３．１％和６６．７％（ＳＢＤ）；采用常规次氯酸盐三段漂白（ＣＥＨ），漂白度可达７５％（ＳＢＤ）以上；采用少量过氧化氢结合常规次氯酸盐多段漂白，漂后浆白度达８０％（ＳＢＤ）以上。     

麦草爆破制浆漂白性能研究(英文)

本文就麦草浆漂白的性能进行了探讨，以期改善纸浆白度．Ｈ２Ｏ２漂白剂因漂白损失小、漂后白度稳定性好，从而常用于纸浆漂白，特别是高得率浆的漂白．为寻找Ｈ２Ｏ２的漂白规律，本文对Ｈ２Ｏ２漂白过程的影响因素进行了研究．漂白剂Ｈ２Ｏ２在水中电离生成ＯＯＨ－作为漂白的有效成分，其浓度的提高使反应顺利进行．因此增加Ｈ２Ｏ２用量将获得较好的漂白效果．Ｈ２Ｏ２在碱ｐＨ缓冲剂存在的环境中电离，将产生一个较稳定的ＯＯＨ－浓度，使漂白反应稳定．但是过高的ｐＨ值会导致Ｈ２Ｏ２分解，同时碱与浆中木素的反应生成新的发色基因，使纸浆白度下降．适当的温度会促使Ｈ２Ｏ２的电离，使漂白反应顺利进行．但温度过高则使Ｈ２Ｏ２分解，失去漂白作用．为消除重金属离子对Ｈ２Ｏ２的催化分解作用，加入了螯合剂．根据ＭｏｎｉｃａＬｕｎｄｑｕｉｓｔ的研究模型，本文对麦草爆破浆的Ｈ２Ｏ２漂白进行了研究，白度值可表示为ｄＷｄｔ＝ｋ［Ｈ２Ｏ２］０．２３４０［ＮａＯＨ］１．２６１９Ｗ－１．８１７６．公式表明：较高的Ｈ２Ｏ２浓度、ＮａＯＨ浓度及较少的发色因素对白度提高有利．从公式中还可看出在保证必需的Ｈ２Ｏ２用量的情况下，ｐＨ值的控制对白度的提高是一个关键因素．由于漂白反应     

DMD的活化预处理及其全无氯漂序的研究

研究了桉木硫酸盐浆对氧脱木质素段和过氧化氢漂段的活化作用以及ＤＭＤ用量对氧段和过氧化氢段浆性能的影响,使经ＭＯＱＭＰ多段漂白的纸浆最终白度达８０％以上,纸浆粘度满足要求,可以实现桉木硫酸盐浆的全无氯漂白。     

马尾松硫酸盐浆过氧化氢强化氧漂的研究

探讨了预处理和过氧化氢强化氧漂对氧漂浆性能的影响,结果表明：采用酶、螯合预处理能较多地提高氧漂的选择性和脱木素程度,而对漂后浆的白度影响较小。在氧漂过程中添加过氧化氢能大幅度提高预处理浆的白度,而浆的卡伯值和粘度下降较小。     

Modeling hydrogen peroxide bleaching to predict optical properties of bleached hardwood CMP

Due to the variations in opacity and brightness of peroxide bleached pulp at Mazandaran Wood and Paper Industries Company (MWPI), empirical models were developed to predict chemimechanical pulp (CMP) brightness and opacity from peroxide bleaching conditions and to drive the optimum operating conditions. To overcome the inconsistency problem, a multi-variate regression analysis method was used for model building. The models were then validated using a new data set from the bleach plant at MWPI, assessing the models’ predictive ability and performance. The results show that there is a relationship between bleaching variables and such dependent variables as pulp brightness and opacity. In addition to the hydrogen peroxide charge and pulp initial brightness, the initial opacity had a significant reverse effect on the final CMP brightness. It was also found that the concentration of total Na⁺ in the CMP tower was the most important variable affecting the final pulp opacity. The validation results demonstrated that these models can be employed as useful tools for process optimization purposes.     

TCF Bleaching of Populus tomentosa Kraft Pulps with H2O2 Pretreatment under Acid Condition

The process of peroxide bleaching of Populus tomentosa kraft pulp with H2O2 pretreatment under acid condition was studied. The variations of pulp characteristics such as brightness, Kappa number and viscosity during the peroxide bleaching process were discussed and the concept of the A/B value was presented for the first time. The results show that acid pretreatment with H2O2 is essential to improve pulp brightness and avoid viscosity loss. The conclusion is reached that the A/B value has great influence on pulp properties when the total amount of peroxide used in the bleaching process is 2%–5%. Pulp with a high viscosity and brightness can be obtained when A/B is about 0.15.     

桉树制浆综述

本文介绍了(1)用桉木生产漂白化学浆,包括硫酸盐法和碱一蒽醌法制浆;(2)用按木生产漂白半化学浆,主要是中性亚硫酸盐半化学高得率浆;(3)用桉木生产漂白化学机械浆,包括冷碱法和亚硫酸盐法制浆;(4)用桉木生产漂白化学热磨机械浆。     

Use of hemicellulase in sequence with hydrogen peroxide and laccase for improvement of teak veneer surface color

Teak veneer was treated with a commercial hemicellulase from Thermomyces lanuginosus in sequence with hydrogen peroxide or a hydrogen peroxide-laccase mixture to improve the veneer surface color and at the same time to reduce the necessary amount of hydrogen peroxide. The removal of a small portion of hemicellulose from the teak veneer surface could be carried out after treatment with the hemicellulase preparation as 0.05 xylanase unit/ml for 30 min. The veneer samples immediately after the hemicellulase treatment were subjected to the designated concentration of hydrogen peroxide or hydrogen peroxide-laccase mixture at 60°C at pH 6.5 for 4 h. The changes in veneer color were measured by using imaging technology as percentage change in gray scale. A treatment combination of hemicellulase containing xylanase, hydrogen peroxide, and laccase yielded a color improvement close to that achieved using 20% hydrogen peroxide. The results showed that hemicellulase pretreatment could improve the bleachability of teak veneer surfaces treated with hydrogen peroxide or hydrogen peroxide-laccase mixture.     

杨木制浆技术的新进展

本文介绍了用杨木生产漂白化学浆,包括硫酸盐法,硫酸盐-蒽醌法,烧碱-蒽醌法和碱性亚硫酸钠-蒽醌法制浆;用杨木生产漂白化学热磨机械浆;用杨木生产碱性过氧化氢机械浆;特别是杨木碱性过氧化氢机械浆是90年代发展研制成功的高得率、高白度和强度性好的新化学机械浆种,它适用于配抄低定量胶印新闻纸、低定量涂布纸等。     

甲脒亚磺酸用于麦草Soda-AQ浆漂白的研究

对甲脒亚磷酸（ＦＡＳ）用于麦草Ｓｏｄａ－ＡＱ浆漂白的可能性进行了研究，重点考察了麦草Ｓｏｄａ－ＡＱ浆过氧化氢（Ｐ）和甲脒亚磺酸（Ａ）两段漂白中的几个过程变量（Ｈ２Ｏ２和ＦＡＳ用量、温度、时间）对漂白的影响，找出了较佳的ＰＦ漂白工艺条件。结果表明，Ｐ段Ｈ２Ｑ用量２％～３％（对绝干浆）、Ｆ段ＦＡＳ用量０．５％（对绝干浆）、温度７０℃、时间３（）ｎｄ为较佳的漂白工艺条件。研究中发现，Ｌ＊与白度呈线性正相关。ａ＊与Ｌ＊呈线性负相关，而ｂ＊与Ｌ＊之间无明确的相关性。     

麦草氧碱蒸煮浆的低温压力过氧化氢漂白

对麦草在低温(85℃)下氧碱蒸煮,所得草浆在较低温度(80℃)下进行压力过氧化氢漂白。漂白后浆料卡伯值从17.9降至9.4～11.9;黏度比漂白前浆料黏度稍有增加,从1 042 mL/g增加到1 158～1 192 mL/g;纸浆白度(ISO)从37.1%升高至45.6%～60.6%,且与卡伯值之间具有一定的线性关系:白度增加=卡伯值降低×1.57;浆料得率在86.6%～89.5%之间,同时得率降低与卡伯值减少之间具有较为标准的线性关系:浆料得率降低=卡伯值降低×0.19。