Physical and mechanical properties of Pinus leucodermis wood

Abstract

The present work reports on the main physical and mechanical properties of Pinus leucodermis mature wood, one of the least studied coniferous species in south-east Europe. Pinus leucodermis heartwood specimens were found to have average density values of 0.73 g cm^?3 at equilibrium moisture content of 11.5% and average density of 0.64 g cm^?3 under oven-dry conditions. The overall tangential shrinkage was 3.4% and the radial shrinkage was 1.9%. The modulus of rupture was on average 77 N mm^?2, while the static modulus of elasticity averaged 7087 N mm^?2. The hardness of P. leucodermis heartwood using the modified Janka test was 33.4 N mm^?2 in the transverse direction and 48.0 N mm^?2 in the longitudinal direction, while its compression strength parallel to grain was approximately 41.6 N mm^?2.     

Chemical characterization of Pinus halepensis sapwood and heartwood

ABSTRACT

This paper describes the chemical composition of sapwood (SW) and heartwood (HW) of Pinus halepensis Mill stem. Extractives were first isolated by accelerated solvent extraction and then analysed by gas chromatography-mass spectrometry (GC-MS). The cellulosic polysaccharide content present in the pre-extracted wood samples was determined with acid hydrolysis and GC. The hemicelluloses content was determined with acid methanolysis and GC. Free monomers were additionally analysed by GC. The amount of lignin was determined gravimetrically by the Klason lignin method and the acid-soluble lignin was determined by a UV method. Formic and acetic acids in wood were determined after alkaline hydrolysis and analysed by HP-SEC. It was found that lipophilic and hydrophilic extractives were more abundant in heartwood (1.6% and 2.5%) than in sapwood (1.1% and 1.8%). Celluloses content was higher in sapwood (42.5%) than in heartwood (39.7%), whereas lignin, hemicelluloses and sugar monomer contents were more abundant in heartwood (28.9%, 26.8% and 0.3%) than in sapwood (28.0%, 24.5% and 0.2%). The variation in acetic and formic acids and ash contents between sapwood (0.7%, 0.2% and 0.5%) and heartwood (0.6%, 0.1% and 0.4%) was small. The acetylation degrees were found to be slightly similar in sapwood (0.4) and heartwood (0.3).     

Dependence of shear strength on wood properties in cultivated Larix sibirica

Abstract

Mechanical properties are very important in structural uses of wood. In the case of larch wood, shear strength (SS) may be a limiting property, because the wood is brittle and it splinters easily. In this study, SS of Siberian larch (Larix sibirica) wood was studied in relation to its axial and radial location and to some other wood properties in the part of the trunk that produces logs of good carpentry quality. SS increased by 21–23% from the pith to the outer heartwood at each studied height (butt, 4.5 and 9 m), and it was at its most approximately 7% higher at the butt than at the other studied heights. The main reason for the radial increase in SS was the increase in density caused by wood maturation, but other factors also affected SS, depending on the grouping mode (combined material, radial/axial location). An exception was sapwood, for which no factors affecting SS could be identified. Thus, sapwood may behave differently from heartwood regarding use, even unexpectedly. The results suggest that mature heartwood, but not juvenile wood and sapwood, of Larix sibirica should primarily be used in products that require high SS.     

The influence of heartwood on the pulping properties of Acacia melanoxylon wood

The pulping wood quality of Acacia melanoxylon was evaluated in relation to the presence of heartwood. The sapwood and heartwood from 20 trees from four sites in Portugal were evaluated separately at 5% stem height level in terms of chemical composition and kraft pulping aptitude. Heartwood had more extractives than sapwood ranging from 7.4% to 9.5% and from 4.0% to 4.2%, respectively, and with a heartwood-to-sapwood ratio for extractives ranging from 1.9 to 2.3. The major component of heartwood extractives was made up of ethanol-soluble compounds (70% of total extractives). Lignin content was similar in sapwood and heartwood (21.5% and 20.7%, respectively) as well as the sugar composition. Site did not influence the chemical composition. Pulping heartwood differed from sapwood in chemical and optical terms: lower values of pulp yield (53% vs 56% respectively), higher kappa number (11 vs. 7), and lower brightness (28% vs 49%). Acacia melanoxylon wood showed an overall good pulping aptitude, but the presence of heartwood should be taken into account because it decreases the raw-material quality for pulping. Heartwood content should therefore be considered as a quality variable when using A. melanoxylon wood in pulp industries     

Clonal variation of carbon content in wood of Larix kaempferi (Japanese larch)

Variations in carbon content in wood among 102 clones, selected from almost the entire natural distribution area, were investigated in Larix kaempferi. The average carbon content was 50.50%, 50.94%, and 50.80% in sapwood, heartwood, and whole wood, respectively. The difference in carbon content between clones was significant. The clonal repeatabilities were 0.46, 0.38, and 0.44 in heartwood, sapwood and whole wood, respectively. The coefficients of variation in the clonal mean carbon content were only 0.43%, 0.42%, and 0.41% in heartwood, sapwood, and whole wood, respectively. This small genetic variation and resulting small relative genetic gain of carbon content indicate that the genetic improvement of carbon content by selection has a small effect on the genetic improvement of carbon sequestration capacity by selection in L. kaempferi.     

Some factors influencing susceptibility to discoloring fungi and water uptake of Scots pine (Pinus sylvestris), Norway spruce (Picea abies) and Oriental spruce (Picea orientalis)

Abstract

The heartwood and sapwood from Scots pine (PS), Norway spruce (PA), and Oriental spruce (PO) were tested for susceptibility to discoloring fungi and water uptake. In addition, annual ring width and density were measured. The methods used were Mycologg for testing growth of fungi and a modified version of EN 927-5 to investigate water uptake. For pine, the heartwood showed a lower water uptake and no discoloring fungi growing in the tests. The heartwood had a significantly higher density and smaller annual ring width than the sapwood. In PA the heartwood had significantly lower discoloration than sapwood. The total water uptake in g/m² was significantly higher in sapwood, but not the calculated moisture content. As for wood properties, the density was significantly higher in sapwood compared to heartwood, although there were no differences in annual ring width. Regarding PO, differences in water uptake could be seen between sapwood and heartwood although the densities were similar. These results show that susceptibility to discoloring fungi and water uptake is hard to correlate to a single inherent property when looking at different wood species.     

End grain water absorption and redistribution in slow-grown and fast-grown Norway spruce (Picea abies (L.) Karst.) heartwood and sapwood

Abstract

Wood is susceptible to decay by rot fungi if it is exposed to high-moisture contents during long periods of time and it is therefore important to limit the duration of such periods. Critical points in outdoor wood structures are, for example, end grain surfaces in joints where water can get trapped after a rain. It is therefore of interest to study both absorption and redistribution of moisture in wood. This paper presents moisture content profiles during end grain water absorption and redistribution in Norway spruce (Picea abies (L.) Karst.) measured by computed tomography with the specimens in individual climate boxes. Heartwood and sapwood of two provenances (slow-grown and fast-grown wood) were included. No major differences were seen between the water uptake of the slow-grown and the fast-grown wood since the densities were similar despite of the large difference in growth ring width. However, for the sapwood specimens, the moisture content was higher further into the specimens than for the heartwood specimens in agreement with previous studies. For the slow-grown wood, the redistribution was also generally more rapid for the sapwood specimens than for the heartwood specimens.     

Separating Norway spruce heartwood and sapwood in dried condition with near-infrared spectroscopy and multivariate data analysis

Norway spruce [Picea abies (L.) Karst.] heartwood and sapwood have differing wood properties, but are similar in appearance. An investigation was made to see whether near-infrared spectroscopy (NIRS) could be used with multivariate statistics for separation between heartwood and sapwood in dry state on tangential longitudinal surfaces. For classification of wood into sapwood and heartwood, partial least square (PLS) regression was used. Orthogonal signal correction (OSC) filtering was used on the spectra. This study shows that a separation of sapwood and heartwood of spruce is possible with NIR spectra measured in a laboratory environment. The visible-wavelength spectra have significant influence on the predictive power of separation models between sapwood and heartwood of spruce. All 44 specimens in the calibration set were correctly classified into heartwood and sapwood. Validation of the model was done with a prediction set of 16 specimens, of which one was classified incorrectly.     

广西融水特色红心杉木优树材质性状变异规律研究

[目的]通过测定和分析广西融水种源红心杉木优树材质性状指标,以了解该地区红心杉木材性状变异规律。[方法]以广西融水种源60株20年生的红心杉木优树为研究材料,测定单株材积、红心率、基本密度、组织比量、管胞性状、微纤丝角等10个材质性状指标,分析各材性性状指标分布和变异规律及性状间的相关关系。[结果]表明:红心率、基本密度、木射线比量、管胞比量、管胞长、管胞宽、管胞长宽比等性状数据分布服从正态分布。融水两个地区红心杉优树轴向薄壁细胞比量的变异系数分别为35.08%和44.97%,变异较大。管胞比量变异系数分别为3.28%和3.56%,变异较小。红心率、木射线比量、管胞长、管胞宽、微纤丝角等性状差异极显著(P0.01),轴向薄壁细胞比量差异显著(P0.05)。10个材质性状间存在12对表型显著相关。[结论]测定的10个性状均是连续性数量性状。早、晚材的管胞长度、管胞宽度和管胞长宽比等性状数据呈从心材至边材逐渐增加的规律。作为重要经济性状的红心率与木射线比量呈极显著正相关(P0.01),单株材积与轴向薄壁细胞比量呈显著正相关(P0.05),而单株材积与基本密度的相关性不显著,这使红心杉木生长量与材性相结合的遗传改良成为可能。     

Degradation of Norway spruce (Picea abies) heartwood and sapwood during 5.5 years’ above-ground exposure

Abstract

Differences in durability between heartwood and sapwood of Norway spruce [Picea abies (L.) Karst.] were investigated to determine wood qualities most favourable for use in outdoor constructions above ground. Trees grown on sites with either good or poor access to water were used. Seventy-eight specimens measuring 20 × 50 × 300?mm³ separated into heartwood and sapwood, half untreated, half painted, were exposed horizontally outdoors above ground for 5.5?years with the pith side up and the bark side down. Crack length and crack number were measured. Fungus growth and surface changes were visually estimated. Fungus type was determined by microscopic analysis. The main finding was that spruce heartwood had fewer and shorter cracks and less surface-discolouring fungus growth than sapwood. This was valid for both painted and untreated wood. After 2?years’ exposure, the cracks in sapwood (upper surface) were more than three times longer and about five times more numerous than in heartwood for both painted and untreated boards. Microscopic study showed that surface discoloration was due mainly to Aureobasidium pullulans, together with a few other discolouring fungi. After 5.5?years, initial decay was established on the surface and in the end grain of four untreated test objects.     

Polysaccharides in some industrially important softwood species

The content and composition of carbohydrates comprising polysaccharides in sapwood and heartwood of 12 industrially important pulpwood species were analysed. The polysaccharide content was between 60% and 80% (w/w) for all species, with cellulose as the predominant polysaccharide type. The carbohydrate composition suggested that the main non-cellulose polysaccharides were galactoglucomannans, except in Larix heartwood, where arabinogalactans were predominant, while the content of xylans were in the same range as the mannans in Pinus resinosa heartwood and Thuja occidentalis heartwood and sapwood. Pectins, i.e. polygalacturonic acids, were the main acidic polysaccharides in all species. The amount and composition of water-soluble carbohydrates from ground wood samples were also analysed, since these are important in mechanical pulping and as a possible source of bioactive polymers. The main polysaccharides released from the spruce species were mannans, together with starch from sapwood. Especially Abies balsamea stemwood, but also Abies sibirica heartwood, released considerable amounts of pectins, suggesting that fir species may release more troublesome anionic polysaccharides than spruce species. Heartwood of Larix lariciana, Larix decidua, Pinus banksiana, and Pinus resinosa released considerable amounts of acidic arabinogalactans. Thuja occidentalis released mainly arabinogalactans and pectins. Pseudotsuga menziesii heartwood released a large amount of arabinogalactans.     

Outdoor exposure of untreated Scots pine (Pinus sylvestris L.) and Norway spruce [Picea abies (L.) Karst.] wood samples

Abstract

Untreated Scots pine (Pinus sylvestris) and Norway spruce (Picea abies) samples were exposed above ground in a durability test for 6 years. The samples consisted of three pieces of wood, 22×95×500 mm, screwed together; two pieces lengthwise with a third piece overlapping. Weight was measured, to calculate moisture content (MC), and samples checked regularly for cracks and fungal growth. Parameters investigated were heartwood/sapwood (pine), annual ring orientation (spruce), stand site, annual ring width and density. Stand site, annual ring width and density had no influence on MC or fungal growth for either pine or spruce. Spruce samples with vertical annual rings had fewer cracks than samples with horizontal annual rings. Pine sapwood samples had a high MC and a large amount of rot fungi, while heartwood had a lower MC and no rot. Most spruce samples were similar to pine heartwood, except from a few samples that had high MC and fungal growth. Those were all sawn from the outer part of the log. Therefore, it can be stated that spruce sawn from the inner part has almost the same properties as pine heartwood, while spruce from the outer part of the log has similar properties to pine sapwood.     

The influence of different soil substrates on the service life of Scots pine sapwood and oak heartwood in ground contact

Abstract

The durability of wood in ground contact is affected by numerous influences, such as substrate quality, climate and microflora of the soil, which need to be considered for the prediction of service life of wooden components to be used in the ground. In this study the influence of different soil substrates on the service life of Scots pine sapwood (Pinus sylvestris L.) and oak heartwood (Quercus petraea Liebl.) was investigated. Mini-stakes were exposed in six different soils at the test site of the Federal Research Centre for Forestry and Forest Products (BFH) in Hamburg, Germany. The effect of partly embedding the test samples in concrete or polyethylene films was also examined. After 3 years of exposure the decay rates for both wood species differed significantly between the soil substrates. Compost soil and fertilized test field soil induced the highest decay activity, whereas in pure sand the lowest decay rates were observed. Surprisingly, exposure in gravel also led to higher decay ratings than sand. Protective measures by means of concrete embedding and polyethylene films performed well during the first 2 years of exposure, but showed increasing decay rates in the third year. The overall decay rating for all soil types was higher for oak heartwood than for pine sapwood. The meaning of different soils, independent of other site influences, for service life prediction of wood is discussed, and the need for further studies on this topic is highlighted.     

Peroxidase activity, isoenzymes and histological localisation in sapwood and heartwood of Scots pine (Pinus sylvestris L.)

Peroxidase activity and isoenzymes of fresh wood samples of the third shoot of 12-year old trees and from the sapwood, transition zone and heartwood of c. 60-year old stems of Scots pine (Pinus sylvestris L.) were investigated. Wood samples were ground at −30°C, extracted, and the extracts concentrated c. 20-fold for peroxidase activity assays (guaiacol method) and for IEF-PAGE. At least 11 major isoenzymes could be found in the gels. Even the heartwood contained some peroxidase isoenzymes. Isoenzyme patterns of the juvenile wood did not change with the season. However, juvenile wood showed the highest peroxidase activity at the end of the growing season. Peroxidase activity decreased from the outer sapwood towards the heartwood. Thin sections of different wood zones stained for peroxidase revealed activity in ray parenchyma and resin canal epithelial cells. Intensive staining was localised in the bordered pits of vertical and ray tracheids, and in the end walls of ray parenchyma cells.     

Fungal decomposition of sapwood and heartwood of European aspen,Populus tremula L.

In contrast to the woodrotting fungi which can only attack Populus tremula after felling, Phellinus tremulae successfully invades the central part of the living tree. Possible causes for this difference were investigated. It was found that sterile wood samples were decomposed more rapidly by saprophytic fungi than by parasitic fungi. With both types of fungi, heartwood was more resistant to decay than sapwood. It is postulated that living sapwood inhibits infection by most woodrotting fungi, but that P. tremulae can successfully overcome this barrier. This postulate cannot be confirmed by experiments using sterilized wood samples.     

Modeling of sapwood and heartwood delignification kinetics of <Emphasis Type="Italic">Eucalyptus globulus</Emphasis> using consecutive and simultaneous approaches

Eucalyptus globulus sapwood and heartwood were delignified at 130°, 150°, or 170°C by kraft pulping. Pulp yields of heartwood were lower than those of sapwood (46.5% vs. 50.4% at 170°C). Delignification was modeled using consecutive and simultaneous kinetic models. The modeling was similar for heartwood and sapwood, and either approach could be used, with both yielding good correlations between experimental and model data. The consecutive model identified two delignification phases with similar reaction rates and activation energies for heartwood and sapwood at 150° and 170°C. At 130°C only one phase was identified. Three reactive types of lignin fractions were identified using the simultaneous model, without differences between heartwood and sapwood. Their reaction rates were 0.152, 0.138, and 0.003 min⁻¹ at 170°C, and the activation energies were 132, 119, and 102 kJ.mol⁻¹. The presence of heartwood did not influence the kinetic development of delignification. The negative impact of heartwood in pulping is related to the higher content of extractives (9.8% vs. 3.9% in heartwood and sapwood) and to their influence on the process, namely in the heating-totemperature phase when a substantial mass loss occurs (30% vs. 20% for heartwood and sapwood).     

柚木种源生长和与材质有关特性的遗传变异及综合评价

对海南岛乐东尖峰岭27年生柚木6个种源的生长及与材质有关特性进行测定与分析,结果表明:种源间树皮厚度、心材宽度、基本密度差异极显著,树高、材积、枝下高、边材宽度差异显著,而胸径、边材年轮数及心材率差异不显著,说明在种源水平上对柚木进行生长和与材质有关特性的改良具有较大的潜力,尤其进行木材生长性状、基本密度和心材宽度的种...     

H-NMR studies of water interactions in sitka spruce and western hemlock: moisture content determination and second moments

Summary The purpose of this study was to examine the influence of the moisture level on the cell-wall material in wood using pulsed proton nuclear magnetic resonance. The wood species used were western hemlock (Tsuga heterophylla (Raf.) Sarg.) and sitka spruce (Picea sitchensis (Bong.) Carr.), distinguishing between heartwood and sapwood regions. The moisture contents of the specimens were below the fibre saturation point and they were conditioned to equilibrium moisture contents based on initial desorption, adsorption and secondary desorption processes. From the FID experiments, the NMR-based moisture contents and the solid-wood lineshape second moments were determined. Average relative proton-spin densities, which were needed to calculate the NMR-based moisture contents, were determined from known moisture contents and they were: hemlock sapwood: 0.616; hemlock heartwood: 0.537; spruce sapwood: 0.679; and, spruce heartwood: 0.446. The average RSD value, considering both heartwood and sapwood, for western hemlock species was 0.577 and for sitka spruce was 0.563; these are close to published RSD values for other species. The condition as to how the equilibrium moisture content was attained did not influence the second moment for hemlock; however, for spruce sapwood, the second moments were sorption dependent. The hemlock M₂ decreased from about 5.1 × 10⁹ s^-2 at low M_NMR to 4.5 × 10⁹ s^-2 (heartwood) and 4.3 × 10⁹ s^-2 (sapwood) at higher m_nmr. The adsorption and secondary desorption M₂ for the spruce sapwood region decreased from about 5.0 × 10⁹ s^-2 at low m_nmr to about 4.1 × 10⁹ s^-2 near the M_F, whereas M₂ for the spruce heartwood decreased from about 4.3 × 10⁹ s^-2 at low M_NMR to about 3.5 × 10⁹ s^-2 near M_F. Extractives may have a key role in obtaining the RSD and second moments.This project was financially supported by the Science Council of British Columbia, MacMillan Bloedel Research. The Natural Sciences and Engineering Research Council of Canada is acknowledged for their support of the NMR spectrometer measurements     

Wood drying process: impact on Scots pine lumber durability

There are indications that the drying process may have negative effects on the natural durability of wood. The impact of various drying processes on the durability of Scots pine lumber has been evaluated with mass loss in a decay test with brown rot fungus, Coniophora puteana, as measure of the decay resistance of sapwood and inner and outer heartwood. Drying with or without steam conditioning was performed in six different series: air drying, kiln drying at temperature ranges commonly used in Swedish sawmills at 70°C and 90°C with two different regulation principles, and one high-temperature drying at 110°C. Durability varied considerably both between and within boards. Sapwood showed considerable less durability than heartwood. No difference in durability was found between inner heartwood and outer heartwood. Air-dried heartwood showed the highest durability compared to other drying series. The lowest durability in sapwood and heartwood was found for series dried at the 90°C temperature level with high material temperature early in drying. The interpretation is that the duration of high material temperature at high moisture content (MC) is the critical combination for decay resistance in heartwood. Steam conditioning after drying decreased durability in sapwood.     

Heartwood and sapwood variation in Eucalyptus globulus Labill. trees at the end of rotation for pulp wood production

The amount of heartwood and sapwood in Eucalyptus globulus Labill. wood was determined in commercial pulpwood plantations at harvest age (12 to 15 years) in four ites in central portugal. twelve trees were sampled in each site at nine stem height levels. Heartwood was present in all the trees up to 82%–87% of the total tree height and amounted to 38%–41% of the total tree volume. The heartwood proportion in the stem cross-section decreased from the base upwards, representing 53.3% and 26.1% of the total area respectively at the base and 55% height level. The sapwood width remained relatively constant along the stem at a mean 38 mm up to the 55% height level. The trees within the site, the height level and their interaction were highly significant sources of variation for heartwood proportion and sapwood width. The heartwood diameter and sapwood width were positively correlated with radial tree growth.