初步探讨了实验室条件下烟秆/木材刨花板的生产工艺,研究了热压时间、施胶量、密度、木刨花加入量等因素对板材的静曲强度、内结合强度、吸水厚度膨胀率的影响.实验结果表明,烟秆/木材刨花板的静曲强度和吸水厚度膨胀率较纯烟秆刨花板有所提高,内结合强度相差不大.     

竹材刨花板蠕变性能的研究

结构用刨花板由木质刨花和胶粘剂热压而成,属高分子材料,具有粘弹性。在负荷作用下产生弹性变形,在长期负荷下发生蠕变。试验表明,竹材制成的酚醛胶刨花板,在高湿环境下,比竹材脲醛胶刨花板有较好的抗蠕变能力;如在竹材刨花板上贴上一层竹席,则抗蠕变性能进一步提高。竹材脲醛胶刨花板比木材脲醛胶刨花板有较好的抗蠕变性能。在低湿度环境下,所有板材的蠕变性能差别较小。     

热压工艺参数对三聚氰胺饰面刨花板甲醛释放量的影响

以市售刨花板和三聚氰胺浸渍纸为原料,制备三聚氰胺饰面刨花板.采用L9（34）正交试验考察热压温度、热压时间、热压压力3个热压工艺参数对三聚氰胺板甲醛释放量的影响.采用国家标准（GB/T 17657-1999）《人造板及饰面人造板理化性能试验方法》干燥器法检测甲醛的释放量.试验结果表明,热压温度对甲醛释放量影响最大、热压时间其次、热压压力影响最小,其中热压温度对甲醛释放量有显著影响,热压时间和热压压力的影响并不显著.热压工艺参数提高,会引起热压后的三聚氰胺板前期的甲醛释放量明显升高.确定饰面刨花板甲醛低释放的最优化生产工艺参数为热压温度170℃、热压时间40s、热压压力2.5 MPa.     

刨花板用快速固化酚醛树脂胶的研究

本研究采用不同于传统合成工艺的方法研制成低毒，高分子量的刨花板用快速固化酚醛树脂胶，试验结果表明，该胶的固人速度较普通酚醛树脂胶提高了４０％左右，用此胶压制成的刨花板，其胶合性能达到了德国ＤＩＮ ６８７６３Ｖ１００耐水刨花板标准，且热压时间较普通酚醛树脂刨花板可缩短２５％左右。     

UF/PDMI组合胶黏剂在刨花板生产中的应用

采用脲醛树脂(UF)/聚合异氰酸酯(PDMI)组合胶黏剂,以不同的组合配比在较低热压温度(160℃)条件下用高含水率(9.0%)杂木刨花制备刨花板,检测其静曲强度、内结合强度以及2h和24h吸水厚度膨胀率。结果表明:聚合异氰酸酯(PDMI)的引入,可以显著提高刨花板的物理力学性能和耐水性能;将刨花终含水率提高至9.0%可节约刨花干燥能耗达13.0%以上;与脲醛树脂胶黏剂(UF)相比,使用PDMI/UF配比为1∶9的(10.0wt%PDMI)组合胶黏剂可以提高刨花板静曲强度80%,提高内结合强度150%;在不添加防水剂的条件下,可以将板材的2h吸水厚度膨胀率由31.0%提高至21.0%。该研究可为刨花板节能环保生产提供新思路。     

LARCH BARK TANNIN ADHESIVE FOR EXTERIOR PARTICLEBOARD

INTR0DUCTI0NChinaisacountrywhichhasnotade-quateforestresources.Itsforestcoverson-lyaboutl3%ofthewh01ecountry.Inor-dertomeetthedevelopmentofnationaleconomy,wemustmakegreateffortstodevelopman-madepanelindustryandmoreefficientlyusetheforestresources.Inthepresent,becauseoftheshortsupplyofchemicalmaterials,thepriceofphenolinthemarketcontinuestogoupwhichledtheincreaseofadhesivemanufacturecost.Findingnewphenolicmateria1sinplaceofphenolisaneffectivemethodtoreducetheadhesivecost.Vegetab1etanninsar…     

异氰酸酯胶麦秸刨花板密度对力学性能的影响

着重讨论了密度对异氰酸酯胶麦秸刨花板各项力学性能的影响。得出试验结论，密度与各项力学性能呈多项式回归关系；当施胶量为４％时，密度为０．６ｇ／ｃｍ３的麦秸刨花板的力学性能完全满足国家标准要求；生产０．６ｇ／ｃｍ３的麦秸刨花板，在技术上是可靠的，在经济上是合理的。     

硅灰石矿物粉改性脲醛树脂胶黏剂的研究

用未改性硅灰石[Ca_3(Si_3O_9)]矿物粉和硅烷类改性硅灰石矿物粉改性脲醛树脂胶黏剂,研究了硅灰石对脲醛树脂胶黏剂性能的影响和改性脲醛树脂制备的刨花板的胶合性能。研究结果表明,硅灰石矿物粉及其添加量对UF胶的固体含量、pH值、黏度、接触角、固化时间均有一定的影响,所制备的刨花板与用原胶相比胶合性能有不同程度的降低,随着硅灰石添加量的增加,刨花板的吸水厚度膨胀率增加,内结合强度有一定程度下降,但可以达到刨花板国家标准的要求。硅灰石矿物粉作为脲醛树脂胶黏剂改性剂是可行的。     

单层浸渍纸贴面葵花秆刨花板的研究

本文论述了葵花秆刨花板的生产工艺、产品性能，分析了单层浸渍纸贴面用基材板的性能，并与国家标准进行了比较，填补了几项指标要求。研究中对国产刨花板设备及其生产工艺进行了调整，生产出了符合单层浸渍纸贴面板性能要求的基材板，同时研制了改性三聚氰胺树脂胶、改性脲醛树脂胶，制定了单层浸渍纸贴面工艺，贴面板各项性能达到国家标准。     

轻质豆秸刨花板工艺的研究

从UF胶制造轻质豆秸刨花板的初步研究,分析了板的密度、施胶量、热压时间等工艺因子对板性能的影响。试验结果表明,利用豆秸制造轻质刨花板是完全可行的,其产品主要物理力学性能为:密度0.483 g/cm 3、吸水厚度膨胀率11.2 % 、内结合强度0.303 MPa、静曲强度8.98 MPa,均达到日本JISA 5908 的技术指标。     

芦苇-稻草原料球磨处理生产刨花板

选择芦苇和稻草为原料,以脲醛树脂为黏结剂制备了芦苇-稻草刨花板。在芦苇碎料中加入一定量的矿物材料,然后采用机械球磨进行处理,应用正交设计对施胶量、热压压力、碎料球磨处理3个因素对板材各项性能的影响进行了研究。实验结果表明,球磨处理可以明显改善芦苇／树脂的结合强度,提高刨花板的各项性能。在施胶量16％,热压压力3．4MPa,对碎料进行球磨处理后制板,除内结合力较低外,板的静曲强度、弹性模量和握钉力都可以达到GBT 4897．3-2003对在干燥状态下使用的家具及室内装修用板的性能要求。     

异氰酸酯树脂胶粘剂刨花板制板工艺研究

研究了用异氰酸酯树脂胶粘剂制造刨花板的工艺条件,详细讨论了热压温度、热压时间、密度含水率、施胶量和施蜡量和对刨花板为物理力学性能的影响。结果表明：刨花含水率是继热压工艺三个因素之后的重要影响因子。研究中还发现了“厚度膨胀率平行性”现象,对其进行的深入分析研究揭示了不可逆厚度膨胀率为２４ｈ吸水厚度膨胀率的关系,总结出板材２４ｈ吸水厚度膨胀率的改善只能通过改善不可逆度膨胀率获得。研究结果还表明,利用Ｙ     

热压工艺对刨花板甲醛及其他有机挥发物释放总量的影响

以兴安落叶松刨花和脲醛树脂胶黏剂为原料,采用正交试验法研究热压温度、热压时间、施胶量、密度工艺因子对刨花板甲醛和其他挥发性有机化合物释放量的影响.结果表明:热压温度、热压时间、施胶量和密度4个工艺因子对刨花板甲醛的释放及其他有机挥发物的释放均影响显著;提高热压温度、延长热压时间、降低板密度能显著降低甲醛及有机挥发物的释放量;综合考虑甲醛及其他有机挥发物释放量确定优化工艺因子为热压温度180℃,热压时间37.5 s·min-1,施胶量11%,密度0.6 g·cm-3,压制出的刨花板甲醛及其他有机挥发物释放量明显下降,满足GB 18580-2001的要求.     

Upgrading of urea formaldehyde-bonded reed and wheat straw particleboards using silane coupling agents

Reed and wheat straw particleboards bonded with urea formaldehyde (UF) resin were manufactured from two different material configurations (i.e., fine and coarse particles). The board densities were in the range of 0.550–.90g/cm³. The effects of particle size and board density on the board properties were examined. The properties of particleboard produced from fine particles were better than those made from coarse particles. An increase in board density resulted in a corresponding improvement in the board properties. The properties of OF bonded reed and wheat straw particleboards were relatively lower than those of commercial particleboards. Three silane coupling agents were used to improve the bondability between the reed and wheat particles and OF resin. Results of this study indicate that all the board properties were improved by the addition of silane coupling agent. The degree of improvement achieved from each coupling agent was different; epoxide silane was found to be more effective for reed straw particleboard, and amino silane was better for wheat straw particleboard.     

改善E1级刨花板预压性能的研究

针对E1级刨花板生产过程中出现板坯铺装时散坯的问题进行了研究。结果表明,在一定范围内,提高树脂粘度、面粉用量和固化剂用量,可以提高胶粘剂初粘性,使刨花板预压性能得到一定程度的改善,但效果有限。调胶时加入聚乙烯醇能显著改善预压性能。当所用树脂粘度为0.17Pa.s、固化剂用量1.9％、面粉用量4％时,再添加0.5％聚乙烯醇,就可以使得刨花板铺装过程中没有散坯问题,具有很好的预压性能。     

纳米蒙脱土对脲醛树脂性能的影响

探讨纳米蒙脱土对脲醛树脂胶黏剂性能的影响。试验表明,将未处理的纳米蒙脱土直接加入到脲醛树脂中,基本不能改善脲醛树脂的性能。纳米蒙脱土通过插层处理使之变为有机纳米蒙脱土后,能显著改善脲醛树脂的综合性能,用其生产出的胶合板、刨花板、MDF的主要性能指标均有较大提高。     

复合工艺对竹/塑复合刨花板性能的影响

利用聚乙烯(PE)粉末取代部分脲醛树脂(UF)胶黏剂,与竹刨花制备三层结构竹/塑复合刨花板。通过正交试验探讨PE添加量、UF施胶量、热压温度及热压时间对竹/塑复合刨花板主要物理力学性能的影响。结果表明:较优工艺组合为PE添加量6%、UF施胶量2%、热压温度205℃、热压时间12s/mm,竹/塑复合刨花板达到LY/T1842—2009《竹材刨花板》A类理化性能指标要求;2h吸水厚度膨胀率和甲醛释放量分别为2.6%和2.4mg/100g,与普通竹材刨花板对比,分别减少了54.4%和54.7%;静曲强度达到19.6MPa,提高了14.0%。采用PE粉末替代部分UF胶黏剂生产竹/塑复合刨花板可行,且具有广泛的应用前景。     

The influence of silane coupling agent and poplar particles on the wet-tability,surface roughness,and hardness of UF-bonded wheat straw （Triticum aestivum L.）/poplar wood particleboard

We used silane coupling agents to improve the bonding ability between wheat straw particles and UF resin, and investigated surface properties （wettability and surface roughness） and hardness of parti-cleboard made from UF-bonded wheat straw （Triticum aestivum L.） combined with poplar wood as affected by silane coupling agent content and straw/poplar wood particle ratios. We manufactured one-layered particleboard panels at four different ratios of straw to poplar wood par-ticles （0%, 15%, 30% and 45% wheat straw） and silane coupling agent content at three levels of 0, 5% and 10%. Roughness measurements, average roughness （Ra）, mean peak-to-valley height （Rz）, and root mean square roughness （Rq） were measured on unsanded samples by using a fine stylus tracing technique. We obtained contact angle measurements by using a goniometer connected to a digital camera and computer sys-tem. Boards containing greater amounts of poplar particles had superior hardness compared to control samples and had lower wettability. Panels made with higher amounts of silane had lower Rq values.     

刨花板阻燃酚醛树脂胶及其制板工艺

研制了一种刨花板用阻燃酚醛树脂胶 ,并对制板工艺进行了优化。经测定 ,制成的刨花板的物理力学性能达到刨花板国家标准 GB/ T4 897- 92中 A类板优等品的性能指标要求 ;氧指数值达到热固性树脂装饰层压板标准 GB7911.6 -87规定的要求 (>37)     

酸碱处理对制备再生桉木颗粒板的影响

废弃人造板中的胶黏剂影响人造板的回收利用。笔者利用化学法对废弃桉木颗粒板中的胶黏剂进行处理,分别探究不同浓度的硫酸、甲酸、硝酸、氢氧化钾分解废弃木颗粒板中脲醛树脂的最佳条件。结果表明,在90℃,水浴处理2 h条件下,甲酸浓度大于60%,硫酸浓度大于25%,或硝酸浓度大于25%可完全分解固化后的脲醛胶黏剂;对酸处理后的木颗粒的颜色、形貌、化学性质进行分析,甲酸对木颗粒的形态、颜色影响较小。用酸处理后制得的再生木颗粒板,力学性能相对于未经处理的再生木颗粒板得到显著提高。