化学镀铜杨木单板的导电性与电磁屏蔽效能分析

为了给电热式化学镀铜地热地板研究提供参考,对化学镀铜杨木单板的导电性与电磁屏蔽效能进行测试,分 析镀层厚度与吸收损耗、反射损耗、趋肤效应的关系。结果表明:镀铜杨木单板屏蔽效能主要以反射损耗为主,属 于反射型电磁屏蔽材料;表面电阻率随镀层厚度的增加呈减小趋势,横纹方向的表面电阻率是顺纹方向的3 倍左 右;频率越高,电磁波在镀铜层中传导时的趋肤深度越小,通过计算趋肤深度确定化学镀铜层的厚度,可以节省镀 铜时间并节约成本。      

木材纤维/铜纤维复合中密度纤维板

试验分析了铜纤维的施加比例对木材纤维／铜纤维复合中密度纤维板物理力学性能和电磁屏蔽效能的影响。结果表明，铜纤维的施加比例对复合中密度纤维板的力学性能影响显著，在木材纤维／铜纤维混合原料中施加一定量的异氰酸酯胶，可显著改善复合中密度纤维板的胶合性能，其胶合强度可以达到国家标准的要求。铜纤维施加比例对复合中密度纤维板的电磁屏蔽效能影响显著，铜纤维在中密度纤维板中的复合位置对电磁屏蔽效能影响较显著，当中密度纤维板双表面复合铜纤维且施加比例为3时其电磁屏蔽效能可达到60dB以上。     

温度对桦木单板表面化学镀Ni—Cu—P三元合金的影响

利用化学镀方法在桦木单板表面沉积Ni—Cu—P三元合金,考查施镀温度对镀后单板表面电阻率和电磁屏蔽效能的影响,采用扫描电镜(SEM)观察镀后单板的表面形貌,利用EDS和XPS分析镀层成分,利用X射线衍射(XRD)分析镀层的组织结构,采用直拉法测定镀层与木材表面的结合强度。结果表明:当温度从80℃升高到90℃时,镀层平均表面电阻率从0.451Ω/cm2降低至0.301Ω/cm2;继续升高温度,表面电阻率小幅升高;在90℃时,施镀单板的电磁屏蔽效能在9 k Hz~1.5 GHz频段达到55~60 d B。SEM观察发现镀层连续、致密且具有金属光泽;EDS分析可知镀层中存在Ni、Cu和P元素,XPS分析可知镀层组成为Ni、Cu、P,其质量分数分别为79.84%、11.82%和8.34%;XRD分析表明镀层为微晶态结构;镀层与木材表面结合牢固。     

不锈钢纤维填充导电膜片的性能研究

为探究不锈钢纤维长度与填充量对导电膜片导电性能与电磁屏蔽性能的影响,将不锈钢纤维均匀地铺撒在涂有脲醛树脂和丙烯酸树脂的表层纸上热压,制备具有电磁屏蔽功能的不锈钢纤维填充导电膜片。首先通过微观结构表征,分析不锈钢纤维在导电膜片平面和断面内的搭接状况;然后采用四电极法与同轴线法测试导电膜片的体积电阻率及电磁屏蔽效能;最后通过理论模拟探究不锈钢纤维填充导电膜片的电磁屏蔽机理。结果表明:1)随着不锈钢纤维填充量的增加,导电膜片平面和断面内不锈钢纤维之间交叉排列的混乱程度不断增加,并以随机排列的形式相互交织形成了有效的“三维导电网络”。2)随着不锈钢纤维长度和填充量的不断增加,导电膜片的体积电阻率逐渐减小,而其电磁屏蔽效能逐渐增大。3)不锈钢纤维的填充量、导电膜片厚度对导电膜片的导电性能影响显著。4)当不锈钢纤维长度为15 mm、填充量为250 g/m2时,导电膜片的体积电阻率降低为6.493×10-3 Ω·cm,电磁屏蔽效能为37.77～51.42 dB,达到中等屏蔽效果,适用于对电磁兼容要求较高的场合。5)理论模拟结果表明,吸收损耗在导电膜片对电磁辐射的屏蔽效果中占有很大的比重,导电膜片表现出了很好的吸波特性。      

杨木单板表面化学镀镍的工艺条件对镀层性能的影响

研究了杨木单板表面化学镀镍过程中pH值和温度变化对镀层的电磁屏蔽性能和表面导电性能影响。用扫描电镜和能谱分析了镀层结构和含磷量。结果表明,pH值和温度升高,电磁屏蔽性能和表面导电性提高,但达到一定值后,电磁屏蔽性能和表面导电性又有所下降。杨木单板经表面化学镀镍后,表面完全被金属镍覆盖,金属感增强,并且镀层中磷含量较低,镀层为晶体结构。     

木纤维/铁丝网复合中密度纤维板

重点研究了不同目数的铁丝网和木纤维压制具有电磁屏蔽效能的复合中密度纤维板的生产工艺。结果表明,采用异氰酸酯涂刷铁丝网,可显著改善复合中密度纤维板的胶合性能,其胶合强度可以达到国家标准的要求。铁丝网的层数对复合中密度纤维板的电磁屏蔽效能影响显著,铁丝网在复合板中的放置位置对复合板的电磁屏蔽效能影响较显著,复合中密度纤维板双表面放置铁丝网时其电磁屏蔽效能可达到60dB以上。     

镀膜木材的耐候性

用气密性氨基树脂和硅烷偶联剂封闭桐木胶合板,真空磁控溅射镀膜镍钛合金原子膜,使镀膜木材经过了紫外灯光照射,较高室内温度、湿度的环境老化.试验结果显示:屏蔽效能保持在58 dB以上,老化后镀膜木材电磁屏蔽效能稳定.附着强度在老化前300 h内没有变化,保持2.0 MPa不变;从400～ 600 h稍有下降,每100h衰减...     

电刷镀工艺新研究

本文研究了快速镍刷镀层的耐磨性及工艺参数对镀层磨性的影响，结果表明：快速镍刷镀层耐磨性高于４５＃淬火和低温镀铁层，与球墨铸铁等温淬火相近，抗粘着磨损和抗冲击负荷的能力远远高于低温镀铁层。最佳工艺参数为：电压１４Ｖ，镀液温度４０℃，相对速度为１２ｍ／ｍｉｎ。     

孔洞对直埋式农用屏蔽电缆耦合效应影响研究

以直埋式农用屏蔽电缆的开孔屏蔽壳体为研究对象,应用线性边界元法（LBEM）分析了不同的孔洞尺寸对屏蔽效能的影响。根据工程实例计算得到,双芯屏蔽电缆各芯线间的耦合电容随屏蔽层孔深及孔宽变化的关系曲线,对有效地利用钢塑复合带防御因屏蔽层的孔洞导致的电磁干扰,提高直埋式电缆屏蔽效能具有指导意义。     

化学镀Ni-P工艺在高温铜焊接件中应用的研究

本文以发动机喷油泵中的高温铜焊接件为研究对象,着重研究了高温铜焊接对Ni-P镀层的影响。试验表明,铜焊接前先镀覆 Ni-P合金,不影响铜焊质量,经高温(约 1000℃)铜焊接后,表面镀层尚保持相当于镀态的硬度;此外,工作在焊接后再镀覆Ni-P时,铜、镍润湿性好,有助于化学镀覆的进行,加快沉积速度。因此,本研究结果对需采用高温铜焊接工艺,而又要求具有高硬度和一定耐磨性的零件制造,有较大的实用价值。     

木材化学镀镍老化镀液的再生与回用

采用可溶性钙盐沉淀去除施镀木材的化学镀镍废液中的亚瞵酸根离子,再用氟化物去除残余的钙离子。主要研究了pH值、钙离子与亚磷酸根的浓度比、处理温度和时间对亚磷酸根去除率的影响。采用再生处理后的镀液施镀木材,可以得到具有良好导电性和电磁屏蔽性能的镀层。     

Comparison Between Electrolysis and Reduction for Treatment of Spent Electroless Nickel Plating Bath

There are lots of residual nickel and organic compounds in the spent electroless nickel plating bath. It not only wastes resource but also causes environmental pollution if the wastewater is discharged without treatment. In this paper, electrolytic method and reduction method for treating spent electroless nickel plating bath were compared. The factors studied included reaction time, pH, temperature, effectiveness and cost. It was found that the recovery rate of nickel by reduction was 99.9% under the condition ofpH 6, 50℃ for 10 min. The purity of reclaimed nickel was 66.1%. This treatment needed about 16 g NaBH4 for a liter spent solution, which cost RMB 64 Yuan. For electrolysis method, with pH 7.6, 80℃, 0.45 A （current intensity） for 2 h, the recovery rate reached 97.3%. The purity was 88.5% for the reclaimed nickel. Moreover, it was found that through electrolysis, the value of TOC （Total Organic Carbon） decreased from 114 to 3.08 g·L^-1 with removal rate of 97.3%. The main cost of electrolysis came from electric energy. It cost about 0.09 kWh （less than RMB 0.1 Yuan） per liter wastewater. Compared with reduction, electrolysis had more advantages, so the priority of selection should be given to the electrolysis method for the treatment of spent electroless nickel plating bath.     

木材的化学镀研究

木材是重要的再生资源 ,化学镀的木材可以具有良好的导电性和装饰性 .为了使化学镀这一金属加工技术更好地应用于木材行业 ,提高木材的利用率和使用价值 .该文归纳、分析了木材化学镀的理论基础和国内外的研究现状 ,提出了木材化学镀需要进一步研究的一些问题 ,指出木材化学镀是木材表面改性和开发电磁波屏蔽、抗静电等新型木质复合材料的有效途径之一 .     

镀镍桦木单板的物理性能分析

利用化学镀法在桦木单板表面沉积Ni-P合金镀层制得镀镍桦木单板。测试了镀层与单板表面的结合强度,对比分析测试了镀镍前后单板的抗拉强度、胶合强度、表面润湿性及导热性,同时还分析了其环境适应性(如抗低温、耐高温和耐腐蚀等性能)。结果表明,镀层与单板表面的结合非常牢固,经表面镀镍后,抗拉强度和表面耐磨性有所提高,胶合强度和表面润湿性稍有下降,导热性能显著提高。镀镍桦木单板具有良好的抗低温、耐高温和耐腐蚀性能,能够满足实际应用的要求。     

镀液组成对木材化学镀镍金属沉积速率的影响

为了确定镀液组成对木材化学镀镍金属沉积速率的影响,本文用点滴法加入镀液的方法进行了木材化学镀镍实验,分析了木材化学镀镀镍镀液的主盐浓度、还原剂浓度、络合剂浓度等对金属镍沉积速率的影响,从而得出木材化学镀镍比较理想的镀液组成。这对于利用化学镀镍这一金属加工技术对木材进行化学镀,对进一步研究木材与金属的复合以及开发功能性木质复合材料具有重要的实际意义。     

木材化学镀镍的镍活化工艺对镀层均匀度的影响因素分析

为了确定镍活化工艺在木材化学镀镍活化过程中的可行性,本文分析了活化液的镍盐浓度、还原剂浓度、酸和碱的浓度以及活化时间等对活化后木材表面镀镍层均匀度的影响,从而得出木材化学镀镍比较理想的活化液组成和活化工艺,这对于在木材化学镀镍领域开展非贵金属活化新工艺的进一步研究有重要的意义。     

化学镀Fe-Al-P合金初探

利用化学镀方法在铜基片上施镀了Ｆｅ－Ａｌ－Ｐ合金镀层。通过改变金属盐比率ＡｌＣｌ３／（ＡｌＣｌ３＋ＦｅＳＯ４）、金属盐ＡｌＣｌ３和还原剂ＮａＨ２ＰＯ２的浓度等参数，研究了合金镀层的沉积速率，成分，表面形貌及结构的变化规律，得到了最佳镀液配方，发现络合剂和还原剂的选择是提高镀层含Ａｌ量的关键。     

Deposition of conformal copper and nickel films from supercritical carbon dioxide

Device-quality copper and nickel films were deposited onto planar and etched silicon substrates by the reduction of soluble organometallic compounds with hydrogen in a supercritical carbon dioxide solution. Exceptional step coverage on complex surfaces and complete filling of high-aspect-ratio features of less than 100 nanometers width were achieved. Nickel was deposited at 60 degrees C by the reduction of bis(cyclopentadienyl)nickel and copper was deposited from either copper(I) or copper(II) compounds onto the native oxide of silicon or metal nitrides with seed layers at temperatures up to 200 degrees C and directly on each surface at temperatures above 250 degrees C. The latter approach provides a single-step means for achieving high-aspect-ratio feature fill necessary for copper interconnect structures in future generations of integrated circuits.