The lamination influence on properties of agro-based particleboard

Abstract

Response surface methodology (RSM) based on a three-level, three-variable central composite rotatable design was applied to evaluate the effects of the parameters such as ratio of rice straw (Oryza sativa)/poplar (Populus deltoids) wood particle bonded with urea-formaldehyde resin in panels, species of wood veneer coating these panels and amount of adhesive in glue line on the modulus of rupture (MOR), internal bonding (IB), and thickness swelling (TS) of panels. Mathematical model equations were derived by computer simulation programming to optimize the properties of the particleboard. These equations that are second-order response functions representing MOR, IB, and TS were expressed as functions of three operating parameters of panel properties. Predicted values were found to be in a good agreement with experimental values (R ² values of 0.96, 0.98 and 0.98 for MOR, IB, and TS, respectively). This study has shown that the RSM could efficiently be applied for modeling panel properties. It was found that the variables affected the properties of panels. Straw usage up to 30% in the mixture did not cause a significant decrease in MOR, IB, and TS. Using beech veneer and 190 g/m² glue line had the highest MOR and lowest TS.     

Physical and mechanical properties of particleboard from roselle (Hibiscus sabdariffa) stalks and eucalyptus (Eucalyptus camaldulensis) wood particles

Abstract

The objective of this work was to evaluate the performance of particleboard manufactured from roselle (Hibiscus sabdariffa) stalks and eucalyptus (Eucalyptus camaldulensis) wood. The manufacturing parameters were various roselle (Hibiscus sabdariffa) ratios in the mixture (0, 25, 50, 75 and 100%) and press time (3, 5 and 7 min). Modulus of elasticity (MOE), modulus of rupture (MOR), internal bonding (IB) strength values and thickness swelling (TS) after 24-hour water soaking of the panels were determined according to the procedure of European Union (EN) Standard. The results of the study demonstrate that roselle stalks can be an alternative raw material source for particleboard industry. With an increase of roselle particles from 0% to 100%, the TS was reduced, and the IB, MOR and MOE were increased. The highest MOE, MOR, IB strength and TS values of the samples were found as 2754.18, 16.81, 0.89 N/mm² and 15.26% for the panels made using 100% roselle with a 7-min press time, respectively.     

Properties of kenaf core binderless particleboard reinforced with kenaf bast fiber-woven sheets

Kenaf composite panels were developed using kenaf bast fiber-woven sheets as top and bottom surfaces, and kenaf core particles as core material. During board manufacture, no binder was added to the core particles, while methylene diphenyldiisocyanate resin was sprayed to the kenaf bast fiber-woven sheet at 50 g/m² on a solids basis. The kenaf composite panels were made using a one-step steam-injection pressing method and a two-step pressing method (the particleboard is steam pressed first, followed by overlaying). Apart from the slightly higher thickness swelling (TS) values for the two-step panels when compared with the one-step panels, there was little difference in board properties between the two composite panel types. However, the two-step pressing operation is recommended when making high-density composite panels (>0.45 g/cm³) to avoid delamination. Compared with single-layer binderless particleboard, the bending strengths in dry and wet conditions, and the dimensional stability in the plane direction of composite panels were improved, especially at low densities. The kenaf composite panel recorded an internal bond strength (IB) value that was slightly low because of the decrease of core region density. The kenaf composite panel with a density of 0.45 g/cm³ (one-step) gave the mechanical properties of: dry modulus of rupture (MOR) 14.5 MPa, dry modulus of elasticity (MOE) 2.1 GPa, wet MOR 2.8 MPa, IB 0.27 MPa, TS 13.9%, and linear expansion 0.23%.     

Manufacture of Light-weight Composite Panel from Kenaf

Light-weight composite panels were manufactured using kenaf core particles as core material and kenaf bast fiber-woven sheets as top and bottom surfaces. Methylene diphenyldiisocyanate （MDI） resin was used as the adhesive with the resin content of 4% for core particles and 50 g/m^2 for bast fiberwoven sheets. The target board densities were set at 0.35.0.45 and 0.55 g/cm^3. The composite panels were evaluated With Japanese Industrial Standard for Particleboards （JIS A 5908- 2003）.The results show that the composite panel has high modulus of rupture and internal bonding strength. The properties of 0.45 g/cm^3 density composite panel are： MOR 20.4 MPa. MOE 1.94 MPa, IB 0.36 MPa, WA142%, TS 21%. Kenaf is a good raw material for making light-weight composite panels.     

Effects of five additive materials on mechanical and dimensional properties of wood cement-bonded boards

There is a growing desire to improve the properties and use of nonwood plant materials as supplements to wood materials for wood cement-bonded boards (WCBs). This study was conducted to determine the comparative properties of WCBs containing various amounts of discontinuous inorganic fiber materials, such as alkali-resistant glass fiber, normal glass fiber, mineral wool, and nonwood plant materials such as retted flax straw and wheat straw particles. Tested cement-bonded boards were made at wood/additive compositions of 100/0, 90/10, 80/20, 70/30, 60/40, and 50/50 (weight percentages). Seventy-eight laboratory-scale WCBs were produced. Various board properties, such as the modulus of rupture (MOR), internal bonding strength (IB), water absorption (WA), thickness swelling (TS), and linear expansion (LE), were studied. The test results showed that three types of discontinuous inorganic fiber used as reinforcing materials in composites significantly enhanced and modified the performance of WCBs. The mechanical properties and dimensional stability of cement-bonded board were significantly improved with increasing amounts of the additives. MOR and IB were increased; and WA, TS, and LE of boards were reduced by combination with the inorganic fiber materials. The results also indicated that combination with retted flax straw particles only slightly increased the MOR of boards, and wheat straw particles led to marked decreases in all the mechanical properties and the dimensional stability of WCBs.Part of this report was presented at the 50th Annual Meeting of the Japan Wood Research Society, Kyoto, April 2000     

Improvement on the properties of gypsum particleboard by adding cement

Gypsum particleboard (GPB) has high thickness swelling (TS), high water absorption (WA), and low mechanical properties compared with cement-bonded particleboard. The properties of GPB were improved by adding cement. The experimental results showed that GPB with the added cement had good physical and mechanical properties compared with those of gypsum particleboard with no added cement. The TS and WA of gypsum particleboard with added cement were reduced by 10%. The mechanical properties of GPB, such as internal bond strength (IB), modulus of rupture (MOR), and modulus of elasticity (MOE), increased when the GPB was made with added cement. The properties of GPB improved relative to the quantity of cement added. With an increase of cement content from 5% to 10%, the TS and WA were reduced, and the IB, MOR, and MOE were increased. In contrast, the TS and WA increased and the IB, MOE, and MOR decreased when the cement content was increased from 15% to 30%. Thus the physical and mechanical properties of GPB were successfully improved when the added cement content was 10%.An outline of this paper was presented at the 47th Annual Meeting of the Japan Wood Research Society in Kochi, April 1997     

生物酶预处理对秸秆中密度纤维板性能的影响

针对稻草和麦秸原料的特点,分别用木聚糖酶、漆酶／碳源系统(LCS)和脂肪酶对原料进行生物酶预处理用机械磨浆方法制备纤维,以木质纤维板用脲醛树脂作胶黏剂,压制秸秆中密度板,并探讨酶处理对秸秆纤维板性能的影响。结果表明:各种生物酶预处理对稻草和麦秸纤维板的性能都有一定的改善,同软化处理相比,经三种生物酶处理后的长纤维的比例明显增加,而细小纤维的含量则明显降低,IB均有不同程度的改进,其中木聚糖酶对此两项指标的改进效果更好。经木聚糖酶预处理后压制的密度达到0．8 g／cm3以上的纤维板的性能如下:麦草纤维板的IB为0．75 MPa,MOE为3 960 MPa,MOR为37．60 MPa,TS为21．29％。除TS外,均优于GB／T11718-1999标准要求。而稻草纤维板的IB为0．73 MPa,MOE为2 618 MPa,MOR为21．35 MPa,TS为21．19％,其中MOR与TS均离标准要求还有一定的差距。     

Development of binderless fiberboard from kenaf core

Binderless fiberboards with densities of 0.3 and 0.5 g/cm³ were developed from kenaf core material using the conventional dry-manufacturing process. The effects of steam pressure (0.4–0.8 MPa) and cooking time (10–30 min) in the refining process, fiber moisture content (MC) (10%, 30%), and hot-pressing time (3–10 min) on the board properties were investigated. The results showed that kenaf core binderless fiberboards manufactured with high steam pressure and long cooking time during the refining process had high internal bond (IB) strength, low thickness swelling (TS), but low bending strength values. The binderless fiberboards made from 30% MC fibers showed better mechanical and dimensional properties than those from air-dried fibers. Hot-pressing time was found to have little effect on the IB value of the binderless board at the refining conditions of 0.8 MPa/20 min, but longer pressing time resulted in lower TS. At a density of 0.5 g/cm³, binderless fiberboard with the refining conditions of 0.8 MPa/20 min recorded a modulus of rupture (MOR) of 12 MPa, modulus of elasticity (MOE) of 1.7 GPa, IB of 0.43 MPa, and 12% TS under the optimum board manufacturing conditions. Part of this article was presented at the 54th Annual Meeting of the Japan Wood Research Society, Hokkaido, August 3–5, 2004     

Water resistance properties of kenaf core binderless boards

Abstract Binderless boards were prepared from kenaf core under various manufacturing conditions and their water resistance properties were evaluated. The board properties evaluated were retention ratios of modulus of rupture (MOR) and modulus of elasticity (MOE), internal bonding strength after water treatment (IB), thickness swelling (TS), water absorption (WA), and linear expansion (LE). These values were then compared with those of boards bonded with urea-formaldehyde (UF), urea melamine formaldehyde (UMF), and phenol-formaldehyde (PF) resins, and their water resistance properties were assessed. We found that pressing temperature was one of the most important conditions for the improvement of water resistance properties. The retention ratios of MOR, MOE, and IB of kenaf core chip binderless boards (pressing temperature 200°C, target density 0.8g/cm³, and the three-step pressing of 6MPa for 10min, then 4MPa for 3min, and 2MPa for 3min) were 37.1%, 49.9%, and 55.7%, respectively, compared with values for UMF-bonded boards of 22.5%, 27.1%, and 40.7%, and values for PF-bonded boards of 42.8%, 41.8%, and 54.1%, respectively. The results showed that the water resistance properties of binderless boards were higher than those of UMF-bonded boards and almost as high as those of PF-bonded boards. Part of this article was presented at the 53rd Annual Meeting of the Japan Wood Research Society, Fukuoka, March 2003     

Physical and Mechanical Properties of Flakeboard Reinforced with Bamboo Strips

The objective of this study was to investigate the physical and mechanical performance of flakeboard reinforced with bamboo strips. The study investigated three different bamboo strip alignment patterns and an experimental control. All panels were tested in static bending both along parallel and perpendicular to the lengths of the bamboo strips. Internal bond strength (IB), thickness swelling (TS), linear expansion (LE), and water absorption (WA) were also examined. As expected, modulus of rupture (MOR) and modulus of elasticity (MOE) were substantially greater for all three experimental panel types as compared to the control group. LE was also improved for all three experimental panel groups. The bamboo strip alignment patterns had no significant effect on TS, WA and IB. The sample means for MOR, MOE and LE tested perpendicular to the bamboo strip lengths yielded slightly lower mean values than corresponding samples tested parallel to the bamboo strips lengths. This difference in mechanical properties is largely attributed to low panel density in the failure zones.     

Manufacture of oriented board using mild steam treatment of plant fiber bundles

This study investigated the effects of mild steam treatment (0.1 MPa for 2 h) of natural bio-based fibers and orientation (0° and 90°) of those fibers in various fiberboards. Ramie bast, pineapple leaf, and sansevieria fiber bundles were used as materials. The composite fiberboards were prepared using phenol-formaldehyde (PF) resin. To investigate the effect of mild steam treatment on wettability, contact angles of PF resin to the fiber were measured. The mechanical properties of the boards were examined as well as their dimensional stability. The contact angle data showed that mild steam treatment was effective in improving the wettability of fibers. Unioriented steam-treated boards showed better performance of internal bond (IB), moduli of rupture (MOR) and elasticity (MOE), thickness swelling (TS), and water absorption (WA) than other boards. Unioriented steam-treated sansevieria board with longitudinal fiber direction showed higher average values of MOR (403 MPa), MOE (39.2 GPa), and IB (1.33 MPa) and lower values of TS (5.15%) and WA (8.68%) than other boards. The differences in the mechanical properties and dimensional stability of boards were found mainly due to the differences in the ratios of fiber fraction of the boards to the density of the fiber bundles.     

Effect of thermo-mechanical refining on properties of MDF made from black spruce bark

The effects of thermo-mechanical refining conditions on the properties of medium density fiberboard (MDF) made from black spruce (Picea mariana) bark were evaluated. The bark chips were refined in the MDF pilot plant of Forintek Canada Corporation under nine different refining conditions in which preheating retention time was adjusted from 3 to 5 to 7 min and steam pressure was set at either 0.6, 0.9 or 1.2 MPa. The resulting bark fibers were blended with 12% UF resin (based on oven-dry fiber weight) using a mechanical blender. The resinated fibers were manually formed into fiber mats and hot-pressed into MDF panels using consistent parameters. Two panels for each refining condition were produced, resulting in a total of 18 panels. Analysis of variance (ANOVA) was used to analyze the significance of factors. Regression coefficients and 3D contour plots were used to quantify the relationship between panel properties and the two test factors. The results from this study indicated that the preheating retention time was a significant factor for both modulus of rupture (MOR) and modulus of elasticity (MOE), the steam pressure was a significant factor for internal bond strength (IB), MOR and MOE, whereas both factors were insignificant for thickness swelling, water absorption and linear expansion. The properties of MDF panels were quadratic functions of retention time and steam pressure. Compared to the ANSI standard for 120-grade MDF, most panels with a nominal density of 950 kg/m³ had very high IB (>1 MPa) and acceptable MOR, MOE and dimension stabilities. These results suggest that black spruce bark residues can be considered as a potentially suitable raw material for manufacturing MDF products.     

Effects of wood species,particle sizes and dimensions of residue obtained from trimming of wood–cement composites on physical and mechanical properties of cement-bonded particleboard

Abstract

The present work was conducted to study the effects of wood species, particle size and residue particle size obtained from trimming of wood–cement composites on physical and mechanical properties of cement-bonded particleboard (CBPB). Particleboard was manufactured with a wood/cement ratio of 1:3 and specific gravity 1200 kg m^?3. After manufacturing, the boards were tested. The second order plan was used to test the significant difference between factors and levels. It was shown that slenderness and compaction ratio increased and bulk density and specific surface decreased with the increase of particle size. With the increase in slenderness ratio and compaction ratio and decrease in bulk density and specific surface, thickness swelling and mechanical properties improved, but water absorption by the board increased. The addition of 6% of 5/3 fraction size of particle obtained from trimming of boards improved significantly the properties of the boards. The optimized panel properties, obtained using poplar particles with a fraction size of 7pass/on5, exceeded the BISON type HZ and EN Standard for Wood Particleboard. CBPB made of alder or poplar particles with 5/3 fraction size of residue exceeded the BISON type HZ. All CBPB with 5/3 fraction size of residue showed lower mean values of thickness swelling, well below the maximum requirements of both standards. In addition, wood species, fraction size of particles and residue size are believed to have been the main cause of change in the properties of the boards.     

Durability characteristics of cement-bonded particleboards manufactured from maize stalk residue

Cement-bonded particleboards of 6 mm in thickness were manufactured using maize stalk (Zea mays) particles of uniform sizes at three levels of board density and additive concentrations respectively. The bending strength and dimensional properties were assessed. Increase in board density and additive concentration caused increase in Modulus of rupture (MOR), Modulus of elasticity (MOE), and decrease in Thickness swelling (TS) and Water absorption (WA). The MOR, MOE and TS of the boards were significantly affected by board density except for WA, but additive concentration affected all the boards’ properties examined at p ≥ 0.05. Strong and dimensional stable cement-bonded boards could be manufactured from maize stalk particles with Portland cement as the binder after hot water treatment. Although the dimensional stability and mechanical strength properties of the boards were affected by the board density and additive concentration, the study revealed that cement-bonded particleboards could be manufactured from maize stalk (Zea mays) particles. However, the increase in board density and additive concentration could cause the increase in MOR and MOE, and cause the decrease in TS and WA of boards.     

大豆蛋白胶稻草碎料板制备关键工艺参数研究

采用自制大豆蛋白胶,通过热压法对稻草碎料板的制备工艺参数进行了系列试验的结果表明：稻草碎料板的静曲强度（MOR）在施胶量为71%时（相当于粗蛋白添加量为12%）最强,接近GB/T 21723-2008的要求;稻草碎料板的内结合强度（IB）随着施胶量的增大而增强,在施胶量为82%时（相当于粗蛋白添加量为18%）,内结合强度接近GB/T 21723-2008的要求;稻草碎料粒径对稻草板的静曲强度和内结合强度影响不显著,稻草碎料板的静曲强度和内结合强度随板材表观密度增大而显著增强。     

UF/PDMI组合胶黏剂在刨花板生产中的应用

采用脲醛树脂(UF)/聚合异氰酸酯(PDMI)组合胶黏剂,以不同的组合配比在较低热压温度(160℃)条件下用高含水率(9.0%)杂木刨花制备刨花板,检测其静曲强度、内结合强度以及2h和24h吸水厚度膨胀率。结果表明:聚合异氰酸酯(PDMI)的引入,可以显著提高刨花板的物理力学性能和耐水性能;将刨花终含水率提高至9.0%可节约刨花干燥能耗达13.0%以上;与脲醛树脂胶黏剂(UF)相比,使用PDMI/UF配比为1∶9的(10.0wt%PDMI)组合胶黏剂可以提高刨花板静曲强度80%,提高内结合强度150%;在不添加防水剂的条件下,可以将板材的2h吸水厚度膨胀率由31.0%提高至21.0%。该研究可为刨花板节能环保生产提供新思路。     

Development of binderless particleboard from kenaf core using steam-injection pressing

Binderless particleboards were successfully developed from kenaf core using the steam-injection press. The effects of board density, steam pressure, and treatment time on the properties of the board were evaluated. The target board densities were relatively low, ranging from 0.40 to 0.70g/cm³. The properties [i.e., moduli of rupture (MOR) and elasticity (MOE) in both dry and wet conditions, internal bonding strength (IB), and water absorption (WA)] of the boards increased linearly with increasing board density. Steam pressure and treatment time also affected the board properties. The bending strength and IB were improved with increased steam pressure. A long steam treatment time contributed to low thickness swelling (TS) values and thus better dimensional stability. The appropriate steam pressure was 1.0MPa, and the treatment time was 10–15min. The properties for 0.55g/cm³ density boards under optimum conditions were MOR 12.6MPa, MOE 2.5GPa, IB 0.49MPa, TS 7.5%, and wet MOR 2.4MPa. Compared with the requirement of JIS 5908, 1994 for particleboard, kenaf binderless boards showed excellent IB strength but relatively poor durability.Part of this report was presented at the 19th Annual Meeting of the Japan Wood Technological Association, Tokyo, October 2001     

Development of high-performance UF-bonded reed and wheat straw medium-density fiberboard

Urea formaldehyde resin-bonded reed and wheat straw fiberboards were produced from the fibers made under different steam cooking conditions in refining processes at densities of 500 and 700kg/m³. The effect of steam cooking conditions on the board properties was examined. The steam pressure and cooking time for reed and wheat straws were 0.4MPa/10min and 0.4MPa/5min, respectively, and 0.6MPa/3min and 0.6MPa/10min for both straws. The effect of steam cooking treatment before the fiber refining process on the wettability and weight losses of the straws was also investigated. The results indicated that the mechanical properties and linear expansion of the straw medium-density fiberboard (MDF) were improved with increasing steam cooking pressure and time during the refining process, whereas the thickness swelling (TS) did not vary much. The wettability of the straws was improved by cooking treatment. The steam cooking conditions had little effect on the wettability of the straw surfaces. For reed and wheat straws, the weight losses increased with increasing steam pressure and cooking time. In addition, it was found that the properties of MDF were significantly higher than those of particleboard, especially the internal bond (IB), where the IB values of MDF were more than 10 times higher than those of particleboard. All the properties of the straw MDF, except the TS of wheat board, can meet the requirement of JIS fiberboard standard. The high performances of MDF could be due to the improved wettability and the removal of extractives during the refining process.     

蔗髓含量对蔗渣碎料板性能的影响研究

研究了蔗髓含量（质量分数）分别在10%、20%、30%、40%4种不同情况下蔗渣碎料板的密度、静曲强度、弹性模量、内结合强度、吸水厚度膨胀率和板面握钉力等物理力学性能的变化规律.结果发现，随蔗髓含量的增加，板材的密度增加，弹性模量和板面握钉力下降；在蔗髓含量低于20%以下时，蔗髓的存在对板材的静曲强度无明显影响，而随蔗髓含量增加，吸水厚度膨胀率影响显著上升；在蔗髓含量高于20%以上时，蔗髓的含量增加使板材静曲强度明显下降，而对吸水厚度膨胀率无影响；蔗髓的含量对板材的内结合强度影响不明显.     

Cyanoethylation of several fiber materials and their utilization as adhesive in wood-based panels

This study examines the cyanoethylation and thermoplasticity of several cyanoethylated fiber materials. Cyanoethylated pulps with a degree of substitution of 1.43 have the lowest Vicat softening point. Cyanoethylated poplar with a weight gain of 18.2 % has the lowest melting temperature. Instead of traditional adhesives, cyanoethylated materials can be used to produce wood-based panels because of their good thermoplasticity. Plywood bonded with cyanoethylated pulp has a bonding strength of 2.06 MPa and an average wood failure of 62.7 %. Wheat straw particle board containing 40 % cyanoethylated pulp has an internal bonding strength of 0.49 MPa, a modulus of rupture (MOR) of 33 MPa, and a density between 0.5 and 0.6 g cm^?3. Fiberboard containing 40 % cyanoethylated pulp has an internal bonding strength of 0.53 MPa, MOR of 38 MPa, modulus of elasticity of 4,200 MPa, and a density between 0.7 and 0.8 g cm^?3. Its swelling in thickness is 41 %.