Stiffness of normal, opposite, and tension poplar wood determined using micro-samples in the three material directions

Mechanical tests on micro-samples were performed in the three material directions in normal, opposite, and tension wood collected from a poplar tree. Two custom micro-devices were designed and built in the laboratory to test samples under pure tension in the transverse direction and under 4-point bending conditions in the longitudinal direction. Both devices were designed to handle samples with a small transverse section (a few square mm), which allowed to select zones with homogenous anatomical features. The results indicate a very high longitudinal stiffness in tension wood (up to 35 GPa compared to an average of 18 GPa for normal wood). Considering wood density, the value represents a specific modulus that is nearly 70 % crystalline cellulose. However, tension wood is slightly less stiff in the tangential and radial directions (1,150 vs. 1,500 MPa for normal wood in the radial direction and 430 vs. 530 MPa in the tangential direction).     

Investigation on transversal variation of poplar tension wood quality using ultrasound wave parameters

Transversal variations of some ultrasound wave parameters (phase velocity, group velocity, attenuation coefficient and acoustic radiation) were measured from the pith to the bark of poplar tension wood discs in different orthotropic directions. Over 80 cubic specimens of 2 × 2 × 10 cm³ (radial, tangential and longitudinal, respectively) were prepared and tested acoustically. Samples containing tension woods were separated from normal ones using anatomical experiments. Results showed acoustical behaviour of normal and tension wood improved in longitudinal direction while the distance between pith and bark increased; also, wave parameter variations were less important in radial and tangential directions. In addition, phase velocity and acoustic radiation – which significantly varied – were the best parameters for quality assessment of poplar wood compared with group velocity and attenuation coefficients. Since samples near the bark were acoustically better than counterparts near the pith, they could be used in products requiring more strength, like lumber. Finally, acoustic radiation and phase velocity were correlated more strongly with density than group velocity and attenuation.     

Effects of semi-isostatic densification of wood on the variation in strength properties with density

The variation in strength properties with density was compared between semi-isostatically densified and non-densified wood. Strength properties were compared with published data from earlier studies using other methods for densification. Small clear specimens of eight species were analysed for compression strength in axial, radial and tangential direction, three-point bending and Brinell hardness. After densification, all tested strength properties increased with density, but especially strength perpendicular to grain became lower than expected from the density of non-densified wood. Strength of densified wood relative to what could be expected for non-densified wood of similar density was denoted as ‘strength potential index’. For axial compression strength and bending strength, strength potential index of individual wood species varied between 0.7 and 1.0, i.e. densified wood is slightly weaker than what could be expected from its density. Strength potential index was lower for properties much determined by strength perpendicular to grain. In radial direction, densified wood was rubbery with low modulus of elasticity and nearly no proportional limit or modulus of rupture. Generally, wood was apparently weakened in proportion to the degree of compression in respective direction. Strength potential index also increased with increasing original density of the species.     

Variability of fracture toughness by the crack tip position in an annual ring of coniferous wood

The effects of the location of the crack tip in an annual ring and the direction of crack propagation on the fracture toughness of the TR crack propagation system of coniferous wood (T, direction normal to the notch plane; R, propagation direction) were analyzed by the finite element method in regard of the changes in elastic modulus and strength within an annual ring. The critical point of the fracture was defined as the state where the stress of a square element (0.125 × 0.125 mm) in contact with the crack tip equals the tensile strength. The distribution of specific gravity was measured by soft X-ray densitometry. The elastic moduli in the T and R directions were estimated by the sound velocity. The tensile strengths in the T and R directions were measured by the tensile test using small specimens of l mm span length. Regarding the variability of fracture toughness (K _IC), the experimental and calculated results had the same tendency. Therefore, it was concluded that the variability ofK _IC is caused by the (1) heterogeneity of the elastic modulus and strength within an annual ring; and (2) changes in the degree of stress concentration at the crack tips, according to the direction of crack propagation.Part of this work was presented at the 40th annual meeting of the Japan Wood Research Society, Tsukuba, April 1990 and at the 6th International Conference on Mechanical Behavior of Materials, Kyoto, July 1991     

Effect of grain direction on transmittance of 100-GHz millimeter wave for hinoki (<Emphasis Type="Italic">Chamaecyparis obtusa</Emphasis>)

The attenuation coefficients of 100-GHz millimeter waves polarized linearly were measured for cross-cut, quarter-sawn, and flat-sawn boards of hinoki (Chamaecyparis obtusa) that were 0.2–2.0 cm thick. This was done to examine the applicability of free-wave propagation theory for applying electromagnetic waves to wood. It was found that the transmittance of a millimeter wave through the specimen boards was lower when the fiber direction of a board was parallel to the direction of the electric field of the incident wave than when the fiber direction was perpendicular to the electric field, and there was little difference in the transmittance between the tangential and radial directions for the former case. These findings can be quantitatively explained by using propagation theory and the dielectric properties of wood.     

人工林落羽杉力学性能研究

对江汉平原人工林落羽杉物理力学性能进行了研究,结果表明:落羽杉的气干密度为0.413 g/cm3,气干密度等级为轻;综合强度为74 MPa,强度等级为Ⅰ级;径向横纹抗压强度略大于弦向横纹抗压强度;端面硬度最高,弦面硬度与径面硬度差别不大。落羽杉南北面近树皮处木材的密度、抗弯强度、弹性模量、顺纹抗压强度均大于近髓心处,南北方向对落羽杉的密度、顺纹抗压强度在5%水平上差异均不显著,而对其抗弯强度、弹性模量在1%水平上差异显著。     

Withdrawal strength of nailed joints with decay degradation of wood and nail corrosion

Nailed timber joints are widely used in timber structures, and their deterioration may cause significant damage. We investigated the withdrawal strength of joints using steel wire nails in specimens exposed to a brown-rot fungus. We also examined the effects of nail corrosion on withdrawal strength, because high humidity conditions accelerate not only wood decay but also the corrosion of nails. We found that nail corrosion increased the withdrawal strength. The ratios of withdrawal strength of nailed joints with rusted nails to that of joints with a minimally rusted nails were 1.47 and 1.56 in joints nailed in radial and tangential directions to annual rings, respectively. Withdrawal strength, excluding the effects of nail corrosion, had a negative correlation with mass loss and Pilodyn-pin-penetration-depth-ratio. We estimated the withdrawal strength of the nailed joint with decayed wood and rusted nails by multiplying the values from the empirical formula (obtained from mass loss and Pilodyn-pin-penetration-depth-ratio) by 1.47 and 1.56 for joints nailed in radial and tangential direction to annual rings, respectively.     

Indented rings (hazel growth) of Norway spruce reduce anisotropy of mechanical properties

This study presents three-point bending test results of Norway spruce clear wood specimens loaded on the radial-longitudinal plane in two different load cases. The tested samples were graded as resonance wood for instrument making and were characterised by narrow annual rings and relatively low density. The modulus of elasticity (MOE) and the corresponding modulus of rupture (MOR) are illustrated separately for the samples with straight grain and the group showing the specific growth pattern of indented rings (‘hazel growth’). With the longitudinal wood anatomical direction parallel to span width, the fibre deviation caused by the indents reduces MOE and MOR values, whereas a ‘reinforcing’ effect of the indents could be observed for the load case with span width parallel to the radial direction. Both aspects lead to a reduction in anisotropy for hazel-growth Norway spruce (anisotropy MOE: indented rings 11.6, straight grain 14.7, anisotropy MOR: indented rings 6.9, straight grain 8.9), which partly explains the exceptional position of this growth pattern for the construction of high-class musical instruments with outstanding mechanical and acoustical performance.     

Evaluation of end-check propagation based on mode I fracture toughness of sugi (<Emphasis Type="Italic">Cryptomeria japonica</Emphasis>)

The relation between crack propagation based on fracture mechanics and end-check propagation during drying was evaluated in this study. Corresponding to the direction of end-check propagation, the mode I fracture toughness of air-dried sugi specimens in TR, TL, and intermediate systems was examined by single-edge-notched bending tests. The occurrence and propagation of end checks on sugi (Cryptomeria japonica D. Don) blocks during drying were observed at the scale of the annual rings. It was found that the critical stress intensity factor (K _IC) decreased as the crack propagation changed from TL to TR. The value of K _IC in the TR system was significantly lower than that in the TL system. As a measure of fracture energy, the area under the load-crack opening displacement curve in the TR system was more than twice that in the TL and intermediate systems. These results indicate that cracks perpendicular to the tangential direction initiate radially with ease, and then crack arrest occurs to prevent growing. This finding provides a consistent interpretation of the end-check propagation observed during drying as follows: tiny end checks, as an analog of TR cracks, occur easily and selectively in latewood or transition wood and propagate toward the pith during drying. When there is no corresponding secondary check in the forward latewood, the checks are arrested and do not propagate further.     

Radial variation in partial compression properties perpendicular to the grain of Japanese larch (Larix kaempferi)

This study investigated the densities, average width of annual rings, and partial compression stresses at 5 % strain perpendicular to the grain of air-dried wood specimens, which were continuous in the radial direction from the pith and were obtained from Japanese larch (Larix kaempferi) trees with different diameters at breast height in the same stand, to evaluate the radial variations in partial compression properties perpendicular to the grain. The air-dried densities of the wood increased with the distance from the pith. The average width of annual rings of the wood tended to decrease with increasing distance from the pith and those of medium- and large-diameter trees seemed to increase near the pith. The partial compression stresses at 5 % strain in the tangential loading direction tended to increase with the distance from the pith and with air-dried wood density. However, in the radial loading direction, this tendency was not observed. The partial compression stresses at 5 % strain in the radial loading direction tended to be low in wood with a small average width of annual rings. These results indicate that the factors affecting the radial variations in the partial compression stress at 5 % strain differ depending on the loading directions.     

马尾松木材横向液体渗透性的研究

分析和讨论了影响马尾松木材横向液体渗透性及其各向异性的机理.对马尾松木材的径向液体渗透性和弦向液体渗透性进行了测量.结果表明,马尾松木材的径向液体渗透性大于弦向液体渗透性,并且,马尾松木材的径向液体渗透性和弦向液体渗透性都是从边材向心材逐渐减小,并随着含水率的下降而升高.其原因是径向液体流动的主要通道是木射线和水平树脂道,弦向主要是管胞壁和交叉场上的纹孔.     

A statistical analysis of the impact of nematode attack symptomatology on the mechanical behaviour of <Emphasis Type="Italic">Pinus pinaster</Emphasis> Ait. wood

An appraisal was made about the impact of pinewood nematode (Bursaphelenchus xylophilus, Nickle) attack symptomatology on the mechanical behaviour of wood from Pinus Pinaster Ait. Two sets of 200 wood specimens were obtained for the study of both mechanical and other physical properties. The specimens, about half of which presented symptoms of nematode, were obtained from a set of 66 wood planks, cut from an equal number of trees, originating from the Setúbal Peninsula (Portugal). Logistic analysis using symptomatology as a binary dependent variable showed adequacy of models containing compression tension to rupture and number of wood rings per unit radial length for the prediction of nematode attack. Analysis of variance revealed that the presence of the disease symptoms was correlated to static bending rupture, modulus of elasticity, work to maximum bending load, and axial compression rupture, causing their decrease at a significance level of 5%.     

Response of colour and hygroscopic properties of Scots pine wood to thermal treatment

The effect of heat treatment on the surface colour and hygroscopic properties of pine wood were investigated in this study. Boards of Scots pine wood (Pinus sylvestris L.) were subjected to thermal treatment at 200°C, for 4, 6, and 8 h. The change of equilibrium moisture content and density values of the specimens in order to facilitate the understanding of the treated material behavior. The colour parameters L*, a* and b*, used to depict the total colour change (Δ E) of wood surface, were shown to change proportionally to the treatment intensity. Moreover, swelling in the tangential and radial directions and absorption of the specimens appeared to be enhanced in great extent by the thermal treatment process. The mean value of swelling percentage in the tangential direction decreased 10.26%, 17.22%, and 19.60% for specimens treated for 4, 6, and 8 h, respectively, referring to the final measurement after 72 h of immersion. In radial direction, mean value of swelling percentage decreased 19.56%, 32.75%, and 34.65% for treated for 4, 6 and 8 h, respectively, after 72 h immersion, which attests the decrease in swelling and improvement in the hygroscopic behavior of Scots pine wood.     

Dielectric anisotropy of oven- and air-dried wood evaluated using a free space millimeter wave

To evaluate the dielectric anisotropy caused by wood structure at a millimeter wave frequency of 100 GHz, the dielectric parameters for flat-sawn specimens of nine wood species at 0 and 11 % moisture content (MC) were measured using a free space method devised for reducing the multiple reflections under an electric field of millimeter waves parallel to longitudinal and tangential directions of wood, and those in radial direction were estimated using a conventional approximation theory. The dielectric parameters in the tangential and radial directions were almost identical and constantly smaller than those in the longitudinal direction. All the dielectric parameters increased with wood density and were larger at 11 than 0 % MC. The dielectric parameters in the longitudinal and transverse directions and the dielectric anisotropy between them were well fitted to the regression lines based on a dielectric mixture model composed of pores and dielectric isotropic wood substance, and a parallel capacitor and Lichtenecker’s exponential formulas were employed to represent the dielectric parameters of the mixture in the longitudinal and transverse directions, respectively. It was concluded that the dielectric anisotropy at 100 GHz is caused by the pore alignment and that the dielectric parameters are almost unaffected by anatomical structures, such as the rays. It was also confirmed that the free space method was effective for the measurement of the dielectric parameters for the flat-sawn specimens.     

Characterization of viscoelastic,shrinkage and transverse anatomy properties of four Australian hardwood species

Abstract

Several key wood properties of four Australian hardwood species: Corymbia citriodora, Eucalyptus pilularis, Eucalyptus marginata and Eucalyptus obliqua, were characterized using state-of-the-art equipment at AgroParisTech, ENGREF, France. The wood properties were measured for input into microscopic (cellular level) and macroscopic (board level) vacuum-drying models currently under development. Morphological characterization was completed using a combination of environmental scanning electron microscopy and image analysis software. A clear difference in fibre porosity, size, wall thickness and orientation was evident between species. Viscoelastic properties were measured in the tangential and radial directions using dynamic mechanical analysis instrumentation. The glass transition temperature was markedly different for each species owing to anatomical and chemical variations. The radial direction showed higher stiffness, internal friction and glass transition temperature than the tangential direction. A highly sensitive microbalance and laser technology were used to measure loss of moisture content in conjunction with directional shrinkage on microsamples. Collapse shrinkage was clearly evident with this method for E. obliqua, but not with other species, consistent with industrial seasoning experience. To characterize the wood–water relations of E. obliqua, free of collapse, thinner sample sections (in the radial–tangential plane) are recommended.     

含LT型裂纹木梁起裂载荷确定方法的试验研究

木材裂纹萌生的准确判定对木材损伤断裂的评估具有重要的意义,起裂载荷是标定裂纹萌生的关键参数。本试验以杉木为研究对象,利用声发射技术(AE)、数字图像相关法(DIC)和电测法(EM),对含LT型裂纹木梁的损伤断裂特性进行了试验研究。通过研究木梁在加载过程中声发射参数变化规律以及裂尖区域的表面应变信息的演变,分析木梁裂纹萌生规律并确定起裂载荷Pini。结果表明:声发射累计振铃计数、幅度可有效反映木梁内部损伤的产生和演化,利用声发射参数的变化规律能准确确定含LT型裂纹木梁的起裂载荷Pini;数字图像相关法、电测法可以实时监测木梁表面裂缝尖端区域的应变变化,根据应变演变特征可以有效监测木梁表面裂纹的萌生和扩展。声发射技术、数字图像相关法、电测法在确定木梁起裂载荷Pini方面有较好的适用性,所确定的起裂载荷大小为:电测法>数字图像相关法>声发射。试验结果为研究监测含LT型裂纹木材裂纹萌生的试验方法提供了依据,应用时可结合实际工况选择合适的测量方法。     

Fractography of shear failure surface of softwood decayed by brown-rot fungus

In order to investigate shear failure surface of decayed wood, wood pieces of ezomatsu (Picea jezoensis) were exposed to brown-rot fungus (Fomitopsis palustris), and standard shear test in radial plane was conducted. The failure surfaces were examined by scanning electron microscopy and surface roughness measurements were also conducted. Transwall failure that the crack elongated parallel to the tracheid axis was observed in the earlywood region through all phases of decay. Intrawall failure principally occurred in the latewood region on the early phase of decay. When decay progressed considerably, transwall failure that the crack elongated perpendicularly to the tracheid axis occurred. And transwall failure was also dominant failure morphology in the latewood region. Fragments of tracheids which were partly peeled out from S₂ layers were observed in some specimens. Size and appearance frequency of fragments of tracheid were smaller and lower when decay progressed. Arithmetic average roughness, which was the index of fragment size and appearance frequency, had positive correlation to shear strength ratio. Especially, line surface roughness of radial direction, which was measured across the radial files of tracheid, had the highest correlation to the shear strength ratio. The surface roughness would be a good indicator to evaluate the decay degree.     

落叶松木材API胶粘剂弦径面胶接强度的差异

对落叶松木材水性高分子异氰酸酯 (API)胶粘剂弦径面胶接强度进行了研究。结果表明 :落叶松木材API胶粘剂弦径面胶接强度存在着差异 ,落叶松木材API胶粘剂径切板胶合强度试件的常态压缩剪切强度是弦切板的 1 4 1倍 ,而反复煮沸压缩剪切强度径切板的却比弦切板的低。落叶松木材本身弦径面顺纹抗剪强度和剪切强度率的试验结果表明 :造成落叶松胶合强度试件弦径面常态压缩剪切强度存在差异的根本原因在于落叶松木材本身弦径向的强度存在差异 ,木材径向的强度比弦向的大 ,文中对这造成这种差异的原因进行了分析     

Effect of coupling media on velocity and attenuation of ultrasonic waves in Brazilian wood

Coupling media are necessary to ensure that transducers bond to wood specimens to minimize coupling losses and improve the accuracy of ultrasonic measurements. There are several types of coupling media available, and the optimal choice is not known. In this work, we analyzed the results of ultrasonic wave attenuation for 0.1-MHz longitudinal and transverse transducers with six different materials as coupling media in nine species of Brazilian wood with densities in the range 700–1170 kg/m³. Tests were performed using constant pressure on the transducer and with wave propagation in the longitudinal direction. For transverse transducers, the polarization was in the radial and tangential directions. The results were analyzed statistically and showed that, for attenuation in both longitudinal and transverse waves, the material used for coupling had significant effects, whereas the wood species had no effect. For longitudinal waves, the statistical evaluation showed that the coupling material performance was strongly dependent on the species of wood, but it was not possible to observe any tendency of behavior associated with specific anatomical properties.     

Change in fracturing and colouring of solid spruce and ash wood after thermal modification

Effects of different thermal treatments (maximum treatment temperatures of 200, 210 and 220°C for 2.5 hours) on solid spruce (Picea abies L. Karst.) and ash (Fraxinus excelsior L.) were investigated in this study. The fracture behaviour in radial/longitudinal as well as in tangential/longitudinal and the change of the wood colour (CIEL*a*b* colour space) on all principal anatomical surfaces (cross sectional, radial and tangential) were analysed. The specific fracture energy and the maximum breaking load decreased almost significantly after all thermally treated samples in comparison to the untreated (standard dried) sample. The wood colour changed also significantly, in particular the lightness decreased with increasing intensity of thermal treatment on all investigated surfaces. A comparison of the percentage loss of the different fracture and colour values has shown a strong correlation between the maximum breaking load and the lightness after several thermal treatments, in both investigated crack propagation systems, on all measured surfaces and for both analysed species.