MA-SEBS对木纤维/聚丙烯复合材料冲击断裂行为的影响(英文)

马来酸酐接枝苯乙烯-乙烯-丁烯-苯乙烯(MA-SEBS)用作聚丙烯/木纤维复合体系的界面相容剂及冲击改性剂,来提高其界面粘接及冲击强度。研究了MA-SEBS含量对PP/WF复合材料冲击断裂行为的影响,当MA-SEBS含量达到8%时,冲击性能达到了最大值,进一步增加到10%并未提高其断裂韧性,但动态热机械分析(DMA)表明复合材料刚性的提高,这归因于PP/WF界面的改善,当MA-SEBS超过8%,聚丙烯与木纤维分子间的相互作用增强。扫描电子显微镜(SEM)分析了样品的断裂表面,表明木纤维与聚丙烯表面强烈的界面粘结。图5表1参11。

Effect of maleic anhydride grafted styrene-ethylene-butylene-styrene (MA-SEBS) on impact fracture behavior of polypropylene/wood fiber composites

MA-SEBS as compatibilizer and impact modifier was incorporated into Polypropylene/Wood Fiber (PP/WF) to enhance interface adhesion and impact strength of the composite. The effect of MA-SEBS content on the impact fracture behavior of PP/WF composites was studied. The impact properties of composites with 8% MA-SEBS reached the maximum value. And further increasing of MA-SEBS content to 10% did not improve the fracture toughness,but improved the stiffness of composites by DMA analysis. This was attributed to the im-proved PP/WF adhesion. As the MA-SEBS content is more than 8%,the molecule interaction of PP and WF was expected to much stronger than lower MA-SEBS. Scanning electron microscopy (SEM) was performed to analyze the impact fracture surface and showed a stronger affinity for the wood surfaces.