Preparation and characterizations of polypyrrole on liquid ammonia pre-treated wool fabric

Wool fabric was treated with liquid ammonia at -40 °C for 30 and 60 s prior to the application of polypyrrole (PPy). The polymer was deposited on wool fiber using the chemical oxidation method with 0.02 and 0.05 mol/l (Py) monomer concentration and FeCl₃ as a catalyst. Functional groups of wool samples were analyzed using FT-IR, and surface morphology was investigated using SEM micrographs. Properties such as water absorbency, surface resistivity, abrasion resistance, weight add-on, and air permeability of coated specimens were explored. The FT-IR outcomes revealed the liquid ammonia pre-treatment changed the amount of amide I (NH), cystic acid, cystic monoxide, and dioxide content of the fiber. SEM micrographs revealed the descaling of wool surface after pre-treatment and smooth coating of polymer. Pre-treatment of wool in liquid ammonia improved absorbency of wool fabric with respect to the treatment duration. The surface resistivity of wool fabric decreased with the increase of monomer concentration and pre-treatment duration. The results of abrasion resistance confirmed that the pre-treated fabric exhibited lower loss of polymer after 200 cycles of abrasion. The weight of the fabric was increased and air permeability decreased when the monomer concentration and liquid ammonia pre-treatment duration was increased.