| 履带拖拉机摆轴销栓断裂分析 |
| |
| 引用本文： | 杜冈峰,杨永生,刘岩,曹耕原.履带拖拉机摆轴销栓断裂分析[J].拖拉机与农用运输车,2013(1):52-53. |
| |
| 作者姓名： | 杜冈峰 杨永生 刘岩 曹耕原 |
| |
| 作者单位： | 中国一拖集团有限公司工艺材料研究所 |
| |
| 摘 要： | 某履带拖拉机摆轴销栓在试车过程中发生断裂,采用断口观察、金相检验、硬度测试、扫描电镜观察和生产工艺等方法进行综合分析。结果表明:由于摆轴销栓表面存在脱碳,造成表面硬度合格的假象;次表面的马氏体组织导致镀锌氢脆敏感性增加,最终使其断裂。
|
| 关 键 词： | 摆轴销栓 马氏体 脱碳 氢脆 |
Fracture Analysis of Pivot Bolt in Crawler Tractor |
| |
| DU Gang-feng,YANG Yong-sheng,LIU Yan,CAO Geng-yuan.Fracture Analysis of Pivot Bolt in Crawler Tractor[J].Tractor & Farm Transporter,2013(1):52-53. |
| |
| Authors: | DU Gang-feng YANG Yong-sheng LIU Yan CAO Geng-yuan |
| |
| Institution: | (Technology and Material Research Institute,YTO Group Corporation,Luoyang 471004,China) |
| |
| Abstract: | A crawler tractor pivot bolt was broken in the testing process.The reason was analyzed by the way of fracture observation,metallographic examination,hardness testing,scanning electron microscopy,production processes and other methods.The result showed that decarburization on the surface of pivot bolt leaded to the illusion of surface hardness testing.Martensite of subsurface increased the sensitivity of zinc plating hydrogen embrittlement,which resulted in its rupture. |
| |
| Keywords: | Pivot bolt Martensite Decarburization Hydrogen embrittlement |