摘    要:将天然毛竹材视为纤维与基体两种组分材料的构成的复合材料,以一个维管束及周围所辖薄壁组织细胞为分析单元进行微观力力性能分析,得出以组分材料性能与含量表示的宏观性抗弹性模量和极限抗强度计算式,实验结果表明,毛竹材组分含量沿壁厚及秆高变异显著,组分(即纤维与基体)的抗拉弹性模量分别为27.60GPa和6.06GPa,抗拉强度分别为547.68MPa和74.60MPa,毛竹材的宏观抗拉弹性模量及强度同组分

关 键 词:毛竹 竹材 抗张强度 弹性模量

.Phyllostachys pubescens Wood:Tensile Elastic,modulus and Tensile Strength
Yang Yunfang. .Phyllostachys pubescens Wood:Tensile Elastic,modulus and Tensile Strength[J]. Journal of Zhejiang Forestry College, 1996, 13(1): 21-27
Authors:Yang Yunfang
Abstract:Natural bamboo is considered as a compound material formed byfiber and base, Micromechanics property is analysed to a vascular bundleand thin- walled tissue involved as a unit.The formula of macro elasticreactance modulus and tensile maximum strength are expressed by compo-nent material property,Analyses show that there is big variation of compo-nent material along the bamboo strunk and wall thickness,Component material(fiber and base)elastic reactance modulus are 27.60 and 6.06 GPa,tensilestrength are 547.68 and 74.60 MPa.There is a closed relationship betweenbamboo macro elastic reactance modulus and number and distribution density of component material.
Keywords:Phylloslachys pubescens  bamboo wood  ensile strength  odulus of elasticity
本文献已被 CNKI 维普 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号