Feasibility of supercritical carbon dioxide as a carrier solvent for preservative treatment of wood-based composites

 Supercritical carbon dioxide (SC-CO₂) was tested for its potential as a carrier solvent for preservative treatment of solid wood and wood-based composites. A preliminary trial showed that the treatability of solid wood varied with its original permeability and that the SC-CO₂ treatment was not promising for refractory timber species such a Larix leptolepis Gordon. In contrast, 3-iodo-2-propynyl butylcarbamate (IPBC)/SC-CO₂ treatment resulted in enhanced decay resistance without any detrimental physical or cosmetic damage in all structural-use wood-based composites tested: medium density fiberboard, hardwood plywood, softwood plywood, particleboard, and oriented strand board (OSB). Further trials under various treatment conditions 25°C/7.85 MPa (80 kgf/cm²), 35°C/7.85 MPa, 45°C/7.85 MPa, 35°C/11.77 MPa (120 kgf/cm²), and 45°C/11.77 MPa] indicated that although small changes in the weight and thickness of the treated materials were noted the strength properties were not adversely affected, except for a few cases of softwood plywood and oriented strand board. The results of this study clearly indicated that the treatment condition allowed SC-CO₂ to transport IPBC into wood-based composites, and the optimum treatment condition seemed to vary with the type of wood-based composite. Received: October 24, 2001 / Accepted: February 15, 2002 Part of this work was presented at the 51st Annual Meeting of the Japan Wood Research Society, Tokyo, April 2001; and the 32nd Annual Meeting of the International Research Group on Wood Preservation, Nara, May 2001 Correspondence to:M. Muin