| 硝基漆模耐温变性的初步研究 |
| |
| 引用本文： | 张广仁,王瑞杰,胡云. 硝基漆模耐温变性的初步研究[J]. 木材工业, 1992, 0(4) |
| |
| 作者姓名： | 张广仁 王瑞杰 胡云 |
| |
| 作者单位： | 东北林业大学(张广仁，王瑞杰)，东北林业大学(胡云) |
| |
| 摘 要： | 涂饰硝基漆的木制品表面漆膜容易开裂,本文探讨了涂料组成与配方、基材树种与切面、涂层厚度以及有无底漆等情况对漆膜耐温变性的影响。结果表明,醇酸树脂与顺酥树脂以4∶1的配比时,漆膜耐温变性好;椴木比松木、径切面比弦切面表面漆膜有较好的耐温变性。
|
| 关 键 词： | 硝基漆 耐温变性 漆膜厚度 |
A preliminary study on the resistance to temperature fluctuation of lacquer |
| |
| Zhang Guangren Wang Ruijie Hu Yun. A preliminary study on the resistance to temperature fluctuation of lacquer[J]. China Wood Industry, 1992, 0(4) |
| |
| Authors: | Zhang Guangren Wang Ruijie Hu Yun |
| |
| Affiliation: | Northeast Forestry University |
| |
| Abstract: | The lacquer film of wood product surface is easy to crack. The influences on film crack by paint composition, wood species and sections, thickness of film and prime paint when temperature changes were studied in this article. |
| |
| Keywords: | Lacquer Resistance to temperature fluctuations Thickness of lacquer film |