Hard Surface-adhesive Properties of TiO2 Nanoparticles-encapsulated Microparticles Prepared by Spray Drying and Surface Coating Method

The aim of this study is to compare hard surface-adhesive properties of TiO₂ nanoparticles (TNPs)-encapsulated microparticles prepared by spray drying and surface coating method. Thus, TNPs were encapsulated with chitosan by spray drying and poly(L-lysine) by surface coating method, which were selected as positively charged materials. And then, the TNPs-encapsulated microparticles were investigated by particle surface properties and adhesion properties on hydroxyapatite (HAP) surface as model for hard surface-adhesion. The characteristics of TNPs-encapsulated Chitosan microcapsules (CM) and TiO₂ nanoparticles coated with cationic poly(L-lysine) polymer (TNPs-PLL) were determined with scanning electron microscope (SEM) image and zeta-potentials. The hard surface-adhesive properties on HAP surface were confirmed with SEM and whitening test. The zeta-potentials of TNPs and HAP were negative, -13 mV and -18 mV respectively, while TNPsencapsulated CM, and TNPs-PLL of positively charged polymers were positive, 13 mV and 57 mV respectively. Whitening test was carried out on model surface when shaking the samples. TNPs-PLL were adhered to HAP surface very much more than those of TNPs-encapsulated CM. Also, the change value of whiteness of the HAP surface treated with TNPs-PLL is large evidently, compared with TNPs-encapsulated CM.