Mechanical properties of wood in an unstable state due to temperature changes,and analysis of the relevant mechanism IV: effect of chemical components on destabilization of wood

In order to investigate the effects of chemical components and matrix structure on the destabilization of quenched wood, we examined the physical and mechanical properties of steam-treated wood, hemicellulose-extracted wood, and delignified wood, which were treated at different levels. For steam-treated and hemicellulose-extracted wood,the relative relaxation modulus of the quenched sample was lower than that of the respective control sample. For delignified wood, the relative relaxation modulus fell with weight loss and reached a minimum value at a certain weight loss, and subsequently increased significantly. The hygroscopicity of all treated samples changed slightly by steaming, whereas increased with removing the component. More-over, the average volumetric swelling per 1% MC at 100% relative humidity (RH) was less than at 75% RH and 93% RH for component-removed wood. It was clear that a void structure existed. As a result, the destabilization evaluated by the fluidity (1 - E _t/E ₀) of steam-treated wood was influenced by the amount of adsorbed water. For component-removed wood, destabilization increased temporarily at lower weight loss because of nonuniform cohesive structure. At high weight loss, destabilization will decreased because capillary-condensed water gathered in the voids and obstructed the motion of adsorbed water. However, the destabilization of all treated wood changed less than that of chemically modified wood.