Characterization and antibacterial properties of Ag NPs doped nylon 6 tree-like nanofiber membrane prepared by one-step electrospinning

A hierarchically Ag/nylon 6 tree-like nanofiber membrane (Ag/PA6 TLNM) was fabricated by adding tetrabutylammonium chloride (TBAC) and silver nitrate (AgNO3) into spinning solution via one-step electrospinning. TBAC presented in PA6/formic acid (HCOOH) spinning solution was able to cause the formation of a tree-like structure due to its space steric structure and the increasing of solution conductivity. Electrospinning solvent acted as a reducing agent for in situ conversion of AgNO₃ into silver nanoparticles (Ag NPs) during the solution preparation. SEM, TEM, FT-IR XPS and XRD confirmed that Ag NPs were doped in the prepared nanofiber membrane successfully and the mechanical properties, pore size distribution and hydrophilicity of the membranes were investigated. The results showed that the tree-like structure improved the mechanical properties and hydrophilicity of the membrane while ensuring high specific surface area and small pore size. And the Ag/PA6 TLNM showed superior antibacterial properties against both E. coli and S. aureus compared with common Ag/PA6 nanofiber membranes (Ag/PA6 NMs). All of the results show that the Ag/PA6 TLNM would have potential applications in water purification.