木粉-HDPE复合材料的单板贴面效果研究

本研究在单板与木塑复合材料中间添加含有马来酸酐接枝聚乙烯（MAPE ）的薄膜，采用热压成型工艺制备单板贴面木塑复合材料，研究不同木粉含量木塑复合材料的贴面效果。结果表明，黏结层中加入MAPE后，单板与木塑复合材料之间的黏结性能明显提高，耐热、耐水性能优良；当木塑复合材料中HDPE含量为30％、黏结层中MAPE含量为HDPE含量的2％时，贴面木塑复合材料的表面胶合强度最大，为1.68 MPa，单板没有出现浸渍剥离现象。

Study on Veneer Overlaid of Wood-Flour/HDPE Composites

In this article,a layer containing maleic anhydride grafted polyethylene（MAPE）film was added in the middle of the veneers and wood-plastic composites,and then prepared the veneered wood-plastic Composites by hot-pressing molding process.The effect of wood flour content contained in wood-plastic composite on bonding strength was evaluated.The results showed that,after added MAPE,the adhesion between the veneers and wood-plastic composites was obviously increased,and head-resistance,and hydrolytic resistance was improved.when HDPE content was 30%in the wood-plastic composites and MAPE content in the adhesive layer accounting for 2%based on HDPE in the wood-plastic composites,the surface bonding strength of the composite increased to 1.68 Mpa,and there was no stripping phenomenon after dip stripping test.