Use of Near Infrared Spectroscopy to Measure Mechanical Properties of Solid Wood

The visible and near infrared （NIR） （350-2500 nm） spectra and the MOE of 438 small clear wood samples from Chinese fir, eucalyptus and poplar 72 were measured. Using partial least-square （PLS） modeling, the NIR spectra could be used to predict MOE and MOR of the clear-wood samples from Chinese fir and eucalyptus solid wood. NIR spectra could only be used to Predict MOE but not MOR of poplar clear-wood samples. With the exception of MoR of poplar clear-wood samples, the correlations between NIR and the mechanical properties are very strong, and the calibration and test correlation coefficients are both above 0.80.     

竹片覆面胶合板的初步研究

本文研究了以竹片为外层材料、多层杨木单板为芯层材料的复合胶合板的结构和力学性能，分析了板坯结构形式、纵向纵片厚度、单板层数及板坯压缩率与产品机械强度之间的关系。初步研究结果表明，板坯结构形式对产品的静载荷抗弯曲性能影响显著；在试验范围内，纵向竹片厚度为３．５－５．０ｍｍ、板坯压缩率在２３％左右时，竹片覆盖面杨木胶合板的综合力学性能比较理想。     

低毒防腐剂百菌清及铜制剂对木材尺寸稳定及力学性能的影响

百菌清（CTL）、氨浴季铵铜（ACQ）、氨溶柠檬酸铜（ACC）处理马尾松（Pinus massoniana)、毛白杨（Populus tomentosa)后对木材尺寸稳定性及MOE／MOR的影响本文进行了研究。结果表明，除剂量11．48kg/m^3的百菌清处理的毛白杨外，以上防腐剂处理试材后吸水至饱和时的尺寸稳定性与对照相比有不同程度的增加，幅度为3．9％－28．05；各处理对抗弯弹性模量（MOE）影响幅度不大，其中对于马尾松，MOE差异不明显，对于毛白杨，各处理对MOE稍有增加（百菌清乳剂处理除外），幅度6．3％－8．1之间。各制剂处理马尾松、毛白杨后对抗弯强度（MOR）影响不明显。     

落叶松层板分级质量评价

对落叶松胶合木用层板进行目测分级并测定其弹性模量和静曲强度,研究各等级层板的弹性模量和静曲强度及其相互之间的关系,探讨层板目测分级和机械弹性模量分级的科学性、合理性。结果表明:根据层板缺陷进行目测分级,等级高的层板其弹性模量和静曲强度的平均值和5%分位值高,目测分级能够基本反映其材质性能,具有一定的科学性与合理性;但目测分级层板弹性模量和静曲强度值的离散度很大,目测分级所能达到的准确与可靠程度决定其不能替代机械弹性模量分级。机械弹性模量分级层板的静曲强度与弹性模量呈正相关性,但各等级层板的静曲强度与弹性模量的相关系数大不相同,其静曲强度值的离散度也比较大,说明该分级方法还有改善的余地。更加科学、可靠的胶合木层板分级方法还有待进一步的探索研究。     

圆盘豆木材力学强度对高温热处理条件变化的响应

以过热蒸汽为传热介质和保护性气体,在热处理温度为160℃、180℃、200℃、220℃,热处理时间为2h、4h、6h、8h的条件下对圆盘豆木材进行高温热处理,研究圆盘豆木材在不同热处理条件下的力学性能变化规律。结果表明,随着热处理温度升高和热处理时间延长,圆盘豆热处理材抗弯强度降低;弹性模量在160℃时最高,然后降低;硬度的变化趋势不明显。红外光谱分析表明,热处理使木材中的半纤维素、纤维素、木素发生降解反应,导致木材力学强度降低。     

人工林落羽杉力学性能研究

对江汉平原人工林落羽杉物理力学性能进行了研究,结果表明:落羽杉的气干密度为0.413 g/cm3,气干密度等级为轻;综合强度为74 MPa,强度等级为Ⅰ级;径向横纹抗压强度略大于弦向横纹抗压强度;端面硬度最高,弦面硬度与径面硬度差别不大。落羽杉南北面近树皮处木材的密度、抗弯强度、弹性模量、顺纹抗压强度均大于近髓心处,南北方向对落羽杉的密度、顺纹抗压强度在5%水平上差异均不显著,而对其抗弯强度、弹性模量在1%水平上差异显著。     

竹材复合板的试件尺寸对静曲强度及弹性模量测试值的影响

采用二次正交旋转组合设计试验,研究了竹材复合板静曲试件的宽厚比、跨厚比对静曲强度及弹性模量测试值的影响。结果表明：在试验研究范围内,试件的宽度不影响静曲强度、弹性模量的检测结果;试件长度（或试验跨距）对静曲强度、弹性模量的测试值影响显著;合理的跨厚比为２５左右。为保证试件的代表性及在弯曲过程中的稳定性,建议试件宽度为５０ｍｍ左右。     

Feasibility of using eggplant (Solanum melongena) stalks in the production of experimental particleboard

This study examined possible feasibility of eggplant (Solanum melongena) stalks in the production of particleboard. Three-layer experimental particleboards with density of 0.53, 0.63, 0.73 and 0.78 g/cm³ were manufactured from eggplant stalks using certain ratios of urea formaldehyde (UF) and melamine urea formaldehyde (MUF) adhesives. Modulus of elasticity (MOE), modulus of rupture (MOR), internal bond strength (IB), thickness swelling (TS) properties of the boards were evaluated and a statistical analysis was performed in order to examine possible feasibility of these stalks in commercial particleboard manufacturing. The experimental results have shown that production of general purpose and furniture grade particleboard used in dry conditions using eggplant stalks is technically viable. The results of the study demonstrate that eggplant stalks can be an alternative raw material source for particleboard industry.     

利用近红外光谱技术预测杉木力学性质

利用三点弯曲实验方法测定了155个杉木样品的抗弯弹性模量和抗弯强度,并用近红外光谱仪采集其径切面和横切面的近红外漫反射光谱,以2/3的试样(103个)作为校正集建立抗弯弹性模量和抗弯强度的偏最小二乘法校正模型,以1/3的试样(52个)作为预测集对模型进行验证.结果表明,切面对模型预测效果的影响比较小,且与光谱区域的选择有关.对于可见近红外全波段光谱(350～2 500 nm)利用径切面比利用横切面光谱建立的力学性质模型的预测效果略好,对于短波光谱(780～1 050 nm)利用横切面比利用径切面光谱建立的模型的预测效果略好;降低波谱范围后,利用横切面短波近红外光谱建立的力学性质校正模型的效果与全波谱模型相比差异较小;利用径切面和横切面2个切面可见近红外全波段光谱、利用横切面短波光谱分别建立的杉木力学性质的校正模型,其预测相对分析误差在1.51～1.90之间,表明利用近红外光谱技术预测杉木木材的力学性质的能力属普通,可用之作为初步的检测工具.     

The lamination influence on properties of agro-based particleboard

Abstract

Response surface methodology (RSM) based on a three-level, three-variable central composite rotatable design was applied to evaluate the effects of the parameters such as ratio of rice straw (Oryza sativa)/poplar (Populus deltoids) wood particle bonded with urea-formaldehyde resin in panels, species of wood veneer coating these panels and amount of adhesive in glue line on the modulus of rupture (MOR), internal bonding (IB), and thickness swelling (TS) of panels. Mathematical model equations were derived by computer simulation programming to optimize the properties of the particleboard. These equations that are second-order response functions representing MOR, IB, and TS were expressed as functions of three operating parameters of panel properties. Predicted values were found to be in a good agreement with experimental values (R ² values of 0.96, 0.98 and 0.98 for MOR, IB, and TS, respectively). This study has shown that the RSM could efficiently be applied for modeling panel properties. It was found that the variables affected the properties of panels. Straw usage up to 30% in the mixture did not cause a significant decrease in MOR, IB, and TS. Using beech veneer and 190 g/m² glue line had the highest MOR and lowest TS.