多层喷射沉积制备耐热铝合金管坯热流分析(Ⅱ) --沉积过程热流分析

通过建立沉积阶段热流分析模型，对多层喷射沉积制备耐热铝合金管坯过程中喷射流沉积后的凝固和冷却进行了分析．喷射流沉积后与基体／沉积坯的传导热交换占热输出率的90％以上，在沉积过程中，沉积面的温度变化呈周期性的升降．计算结果表明，多层喷射沉积采用移动坩埚式扫描方式，延长了喷射流沉积时间间隔，喷射流沉积后可以获得10^3K／s以上的冷却速度。     

冷冲高硬度材料模具失效的原因与对策研究

在日常的应用中,我们发现,制作材料是高合金钢的模具要比硬质合金制作的模具耐用,我们进而研究了其失效的方式以及失效的比例,研究结果显示,硬质合金的失效主要体现在掉渣和崩刃,而高合金钢的失效主要体现在正常的磨损方面。在制作的过程中,高合金钢会由于在加热的不适当而使得碳化物不均匀,或者使得硬度不稳定等原因而没有充分发挥材料的潜在能力,文章对如何提高高合金钢的寿命提出了具体方案。     

发动机缸盖用铸造铝硅合金的成分优化与组织性能研究

采用正交试验对ZL101合金进行了成分优化设计，并分析了合金元素对铝硅合金力学性能的影响.对改良后的合金进行了热处理工艺研究，其最佳热处理工艺条件为：500 ℃×5.5 h+180 ℃×5 h.研究结果表明，改良合金在铸态下的力学性能为：抗拉强度为244.57 MPa，伸长率为5.95%，硬度为75.1 HB；在T6态下的力学性能为：抗拉强度为397.92 MPa，伸长率为4.68%，硬度为141.2 HB.     

Effect of the Silicic Acid Polymerization Degree on the Coagulating Property of Polyalumium Silicate Chloride

Polyaluminum silicate is a new type of inorganic macromolecular flocculants, which is developed as a complex product in recent years on the base of polyalumium flocculant and polysilicic acid flocculant. Sodium silicate is diluted to the concentration of 3.0% SiO 2 with distilled water. The solution was adjusted to pH 4.5 with sulphate acid and kept at quiescency for different time to get polysilicic acid with different polymerization degrees. Using polysilicic acid prepared and aluminium chloride as materials, a series of polyaluminium silicate chlorides(PASC) with different basicities(B), Al/Si molar ratios and polymerization degree of silicic acid are prepared by copolymerization technique. The Al-Ferron timed complex colorimetric method is applied to characterize species distribution of PASC and to study its influence factors. The interaction between hydrolyzed aluminum species and polysilicic acid with different polymerization degrees in PASC is discussed.The flocculant prepared is applied to the treatment of commercial concrete wastewater. The turbidity removal of commercial concrete wastewater is up to 97% when a PASC, prepared with polysilicic acid of 145 min polymerization degree.     

Phase Transformation Diffusion Bonding of Titanium Alloy to Stainless Steel

Jointing of titanium alloy and stainless steel is very often in the fields like aviation, chemical plants etc. The combination of materials has the advantages of both titanium alloy and stainless steel and will reduce the consumption of titanium resource. The phase transformation diffusion bonding of TA17 titanium alloy to 0CriSNigTi stainless steel are carried out on Gleeble - 1500D. The effcet of maximum thermal cycle temperature, the tensile strength, the fracture surface and microstruture of the joints are investigated. The results show that TiFe and TiFe2 intermetallics and some solid solutions are formed along the interface, when maximum thermal cycle temperature increase, the area proportion of intermetallics in the fracture surface increase, which are detrimental to the mechanical properties of the transition joints.     

Artificial Neural Networks Models for Flow Stress during High Temperature Plastic Deformation of Al-Li Alloy

Using gained experimental data to develop the models of stable flow stresses at high temperature plastic deformation by statistical methods for alloy materials, precision of the models is poor and at the same time the processes of modeling are complicated with great workload. On the basis of the data obtained on Gleeble-1500 Thermal Simulator,the predicting models for the relation between stable flow stress during high temperature plastic deformation and deformation strain, strain rate and temperature for 1420 Al-Li alloy have been developed with BP Artificial Neural Network method. The results show that the model on basis of BPNN is practical and it reflects the real feature of the deforming process. It states that the difference between the real value and the output of the model is in order of 5 percent.     

ZrO_2对Al_2O_3基泡沫陶瓷过滤器的性能影响

以Al2O3为主要成分的料浆中加入ZrO2,采用有机泡沫浸渍法,用1560℃烧结制备Al2O3基泡沫陶瓷过滤器,并测定不同ZrO2含量过滤器样品的抗压强度、热震次数并观察其显微结构,实验结果表明:Al2O3基泡沫陶瓷的抗压强度、抗热震性能随ZrO2加入量的增加先增加,而后略有下降。在ZrO2加入量为20%(重量)时制品的抗压强度及抗热震性能最佳,其最高抗压强度达2.31 MPa,1100℃热震循环次数为16次。