玉米秸秆液化树脂化研究

[目的]研究玉米秸秆液化及树脂化的工艺条件,进而提高玉米秸秆资源的利用价值及开辟玉米秸秆利用的新途径.[方法]以苯酚为液化剂、磷酸为催化剂对玉米秸秆进行液化,通过单因素试验和正交试验确定玉米秸秆液化的最优工艺;然后对液化产物进行树脂化,利用单因素试验确定树脂化工艺.[结果]玉米秸秆液化的最优工艺条件：液化温度150℃、液化时间165 min、固液比3∶13、磷酸用量10％,该液化工艺条件下,玉米秸秆液化残渣率为l2.1％;树脂化工艺条件：甲醛与液化产物摩尔比1.8、NaOH与液化产物摩尔比0.35、树脂化合成温度85℃、保温时间40 min、水与液化产物摩尔比8.0,该工艺条件下可生产获得综合性能较好的玉米秸秆液化物树脂,用其压制的胶合板干状强度1.788 MPa、湿状强度0.812 MPa,胶合强度符合国家标准（GB/T 17657-1999）对Ⅰ类胶合板的要求（≥0.700MPa）.[结论]以玉米秸秆液化产物制备的酚醛树脂胶黏剂可用于木材加工.     

木薯秆磷酸液化及其液化物树脂性能研究

[目的]研究木薯秆磷酸液化最佳工艺条件及其液化物树脂性能,为木薯秆的开发利用提供参考.[方法]以苯酚为液化剂、磷酸为催化剂,通过单因素试验和正交试验考察液固比、催化剂添加量、液化温度、液化时间等因素对木薯秆液化反应的影响,并测定木薯秆液化物树脂的胶合性能.[结果]木薯秆磷酸液化的最佳工艺条件为：液固比5∶1,催化剂添加量13％,液化温度165℃,液化时间130 min;在最佳工艺条件下,木薯秆液化率为90.54％.以木薯秆液化物树脂压制3层胶合板,其平均胶合强度为0.7392 MPa,符合国家标准GB/T 9846-2004对Ⅰ类胶合板的要求（≥0.7000MPa）.[结论]以木薯秆磷酸液化产物合成树脂制备酚醛树脂胶是可行性的.     

杉木粉液化与液化产物树脂化的研究

以硫酸为催化剂、苯酚为液化剂采用溶剂热法对杉木粉进行液化,用杉木粉液化产物制备出酚醛树脂;考察了反应温度、反应时间、液比(苯酚-木粉的质量比)和催化剂用量对杉木粉液化效率的影响,并初步探讨了液化产物残渣率对所制酚醛树脂性能的影响。实验结果表明,杉木粉液化的最佳工艺条件是:反应温度160℃,液化时间12 h,液比值3,催化剂用量3%,在此条件下残渣率约为10%。液化产物残渣率的测定表明,升高反应温度、延长反应时间、增加液比和催化剂用量可以降低残渣率,提高液化效率;液比值为0.5~1.5时残渣率随液比增加而显著降低,催化剂用量为0.5%~2%时液化效率的变化明显。红外光谱结果表明,由液化产物所合成的酚醛树脂中羟甲基含量较高。液化产物残渣率低时制备的酚醛树脂残碳率较高。     

人工林木材的苯酚液化及树脂化研究Ⅱ.液化木基酚醛树脂的制备和性能表征

研究液化产物树脂化合成工艺,表征液化木基酚醛树脂的物化性质,评价树脂的胶合强度和木破率.结果表明,采用一次缩聚的投料方式能简化操作工艺,缩短合成时间.木材液化产物中残渣的过滤与否,对树脂性能有一定程度的影响:残渣含量高时,影响较大;残渣含量低时,影响较小.当甲醛与苯酚的量比为1.5和1.8时,利用含11.0%残渣的杉木液化产物和含16.5%残渣的杨木液化产物,制备了性能优良的酚醛树脂.     

Factors affecting the resinification of liquefied phenolated wood

Wood of Chinese fir and poplar were liquefied in phenol at 150℃ and atmospheric pressure. The liquefied wood were reacted with formaldehyde to synthesize the liquefied wood-based resin. The factors affecting the resinification and the properties of new resin were investigated. The results show that the formaldehyde/liquefied wood molar ratio, reaction temperature, reaction time and sodium hydroxide/liquefied wood molar ratio have important influence on the resin characteristics. With the increase of formaldehyde/liquefied wood molar ratio, the yield of resin increases, and the flee phenol content of resins decreases, showing that the resinification of liquefied wood is more complete at higher formaldehyde/liquefied wood molar ratios. The reaction temperature on the viscosity of the liquefied resin has considerable effect; the viscosity of resin increased with increasing reaction temperature, and the amount of liquefied poplar resin increased more quickly than that of liquefied Chinese fir resin. The resinification time also has obvious influence on the viscosity of resin; the viscosity of liquefied poplar resin is more sensitive to resinification time compared with that of liquefied Chinese fir. The amount of sodium hydroxide can improve the water miscibility of liquefied wood resin. The optimum sodium hydroxide/liquefied wood molar ratio for preparation of liquefied wood-based resins exceeds 0.4.     

核桃壳苯酚液化及其产物树脂化制备木材胶黏剂的研究

采用硫酸催化剂,考察了苯酚与核桃壳质量比等条件对核桃壳液化的影响。结果表明相同液化条件下,随着苯酚与核桃壳质量比从2∶1升至5∶1,残渣率从26.49%降至6.60%;随着浓硫酸加入量从2%增至4%、反应时间从5 min延至120 min、反应温度从100℃增至150℃,残渣率则分别从20.79%降至10.48%、48.84%降至15.62%、28.86%降至9.39%,游离酚含量分别从17.32%降至12.67%、41.71%降至10.25%、21.94%降至14.33%。同时,液化产物重均相对分子质量(MW)可降至706~1 030、分散度可降至1.04~1.25;液化产物中高相对分子质量部分随着苯酚与核桃壳质量比的增加有所降低,但随着浓硫酸加入量、液化反应时间和温度的增加而有所增加;核桃壳液化产物/苯酚/甲醛共缩聚树脂胶黏剂(WPF)与传统酚醛树脂胶黏剂(PF)的对比表明,WPF的胶接强度可达1.33 MPa,可作为胶合板用胶黏剂。     

竹材加工剩余物液化及液化产物制备发泡树脂的工艺研究

采用苯酚和聚乙二醇-400复合液化试剂,对竹材加工剩余物进行液化和液化产物的树脂化试验。采用单因素法,探讨主要工艺因素对液化效果及对树脂性能的影响,得到竹材酚醇复合液化工艺及树脂化工艺的优化参数。利用液化产物制备的树脂,可用于制造建筑用发泡材料,提高竹材加工剩余物的附加值。     

桉树树皮液化及液化物的树脂化

在质量浓度为36%（360 g.L-1）的硫酸催化作用下用苯酚对桉树Eucalyptus spp.树皮进行液化,考察催化剂用量、液固比、液化温度和液化时间对液化反应效率的影响;通过正交实验得到桉树树皮液化的较佳方案,并对桉树树皮液化物树脂化的影响因素进行研究。结果表明：①液固比对桉树树皮液化效果的影响最大,其次依次为液化温度、液化时间。②通过单因素分析法和正交试验法相结合,得出桉树树皮较理想的液化工艺条件：液固比为10∶3,液化温度为150℃,液化时间为80 min,质量浓度36%硫酸用量为液化物总量的6%。③以树皮液化物为基准,选择甲醛摩尔比为1.6,氢氧化钠摩尔比为0.3,水摩尔比为8.0,缩聚温度95℃的树脂化工艺制备树脂胶黏剂用于压板。样板经过广西壮族自治区产品质量监督检验院的检测：产品的含水率为10%,在技术要求范围内;胶合强度的平均值为0.835 8 MPa,在Ⅰ类胶合板的技术要求内;甲醛释放量为1.5 mg.L-1,属于E2级别。图1表2参13