排序方式: 共有66条查询结果,搜索用时 312 毫秒
1.
采用微波辅助光催化降解和直接光解实验方法,研究了苯噻草胺在光催化和直接光解两种体系下的降解情况,并考察了初始pH值、腐植酸浓度以及阿特拉津对其光催化降解和直接光解的影响。结果表明,在光照4min内,苯噻草胺直接光解效率为93.3%,较光催化降解效率高出28.9%;初始pH值从1.88增加至10.28时,苯噻草胺光催化和光解速率常数分别提高了250%和58.6%;添加腐植酸对苯噻草胺的直接光解和光催化均具有抑制效应,并且抑制效应随着腐植酸浓度的增加而增加,当腐植酸浓度增加至40mg·L^-1时,直接光解和光催化降解速率分别降低了51.8%和47.5%;10mg·L^-1的阿特拉津抑制了苯噻草胺的前期降解,整体直接光解速率降低了46.3%,但整体光催化降解速率没有减小。此外,采用GC—MS对苯噻草胺两种降解体系下的主要中间产物进行鉴定,并提出了主要的光降解途径。 相似文献
2.
Pt and Cr co doped Nano TiO2 film was prepared by the sol gel method. The film was characterized by AFM, XRD and UV Vis. The experiment showed that when the average TiO2 film diameter is 32 nm and the film thickness is 290 nm, the rate of photodegradation is 95% in 2.5 hours. Additionally, when the optimal co doping ratio for Pt Cr is n(Pt): n(TiO2) equals 0.03% and n(Cr):n(TiO2) equals 0.4%, the photodegradation of methylene blue for Nano TiO2 film can be enhanced. The photocatalytic properties of Pt and Cr co doped Nano TiO2 film is better than that of pure TiO2 and Pt, Cr separately doped TiO2 film. 相似文献
3.
4.
刘祥英 《湖南农业大学学报(自然科学版)》2011,37(5):551-553
以高压汞灯为光源,研究纳米二氧化钛(TiO2)降解毒死蜱的反应动力学,考察纳米TiO2用量、毒死蜱起始质量浓度及溶液pH值对毒死蜱光催化降解速率的影响.结果表明,纳米TiO2最佳用量为50~100 mg/L,毒死蜱初始质量浓度在5~80 mg/L时,其降解反应符合一级反应动力学规律,表现为毒死蜱质量浓度越大,降解速率常... 相似文献
5.
6.
光催化降解汽车尾气路面喷洒机的研究 总被引:1,自引:0,他引:1
根据光催化降解汽车尾气材料的喷洒要求及喷洒时所需的工作特点,结合我国实际的道路状况,研究设计光催化降解汽车尾气路面喷洒机。介绍喷洒机的结构组成及工作原理,对喷洒机的主要结构进行设计。该喷洒系统可利用牵引设备的动力或自载蓄电池来驱动直流电机液泵,取代传统的小型汽油机或柴油机,使该机工作时具备环保、低噪声和低振动等诸多优点。对喷洒机的试验方法进行研究,确定试验时的施工工艺,通过试验验证喷洒机的工作效果良好。 相似文献
7.
Five-membered nitrogen heterocycles (pyrrole, imidazole and 1,2,4-triazole) have been degraded using titanium dioxide and simulated solar radiation at pH = 8. The degradations followed a simple Langmuir-Hinshelwood mechanism. Accordingly, the adsorption equilibrium constants K of the heterocycles on the titanium dioxide surface and the rate constants k of degradation of the heterocycle-catalyst adduct have been obtained experimentally. While the K values decrease with heterocycle pKa, the k values increase with increasing pKa. Therefore, apparently, the rate constant depends on the availability of the electron pair on nitrogen, but at the same time the electron pair repulsion induced by the negatively charged titanium dioxide surface at pH = 8 causes a reverse effect in the adsorption equilibrium constant. Only in the case of imidazole, where the adsorption equilibrium constant is low enough (K = 0.013 M(-1)), can the rate constant be approximated to a pseudo-first-order rate expression: k(obs) = Kk. In all other cases, k(obs) = Kk/(1 + K(heterocycle)). 相似文献
8.
9.
Two kinds of Fe3+/TiO2 catalysts are prepared by Sol-gel method and hydrolysis method. XRD, UV-Vis, BET, curves of N 2 adsorption-desorption and 3D fluorescence are used to analyze the structures and properties of the catalysts, and their photocatalytic activities are investigated through degradation of DBP. The results show that two kinds of catalysts are anatase TiO 2. The band gap of the Fe3+/TiO 2 catalysts prepared by Sol-gel and hydrolysis method are 2.6 eV and 3.2 eV respectively, and the former with an absorption edge at 477 nm, while the latter with no redshift. The curves of N 2 adsorption-desorption of the Fe3+/TiO 2 catalysts prepared by Sol-gel and hydrolysis method are type Ⅳ and Ⅴ, their BET specific surface areas are 57.03 m2/g and 10.94 m2/g, and the hysteresis loop of the latter shifts to the high relative pressure region with a smaller pore volume and a bigger average pore diameter. Two kinds of catalysts can reduce photoluminescence properties of TiO 2 at various degrees, and the catalyst prepared by Sol-gel method shows a weaker photoluminescence property. The results of degradation experiment show the degradation rate of DBP by catalyst prepared by Sol-gel method and hydrolysis method are 60.53% and 31.83% respectively after 2 h. 相似文献
10.
H3PW12O40Ti(OH)4 hydrogel was prepared by the sol-gel method, and then H3PW12O40TiO2/bentonite was prepared through the intercalation of H3PW12O40Ti(OH)4 into interlayer space. The characterization of XRD, SEM and EDS showed that H3PW12O40TiO2 species were successfully immobilized on bentonite, and the layer strucure of bentonite was changed. The discrete anatase TiO2 existed on the bentonite. H3PW12O40TiO2/bentonite was a composite material with the different particle size and th loose structure. The photocatalytic degradation of methyl orange showed that the photocatalytic activity of catalyst had been better by doping H3PW12O40, and the H3PW12O40/TiO2/bentonite had a wide applicable range of pH value. Moreover, H3PW12O40TiO2/bentonite had a good catalytic stability. Based on the results of characterization analysis and catalytic performance, the schematic procedure for the action mechanism of H3PW12O40TiO2/Bentonite in photocatalysis was presented. 相似文献