Behavior of Brick Samples in Aggressive Environments

The weathering of different brick samples ina range of aggressive environments has been studied.Brick samples were prepared using two clay types (fromGranada, Spain), different additives, and a range offiring temperatures (850–1100 °C). The brickscompositional and textural characteristics wereevaluated using XRD, SEM, hydric tests and mercuryintrusion porosimetry (MIP). The samples weresubjected to accelerate aging, including wet-dry,freeze-thaw and salt crystallization cycles. The decayof the bricks in polluted atmospheres was simulated ina static chamber containing sulfur dioxide (SO₂)at 25 °C and 50% relative humidity. Samplesfired at 1000 °C proved to be the most durable,with better hydric behavior (fast drying and slowwater absorption) and fewer micropores. However, theywere not suitable for salt-rich environments (badperformance in the salt decay test). Samples fired at850 °C turned out to be more resistant to saltdecay, but they showed a poor hydric behavior (slowdrying and rapid water absorption) and littleresistance to freeze-thaw and wet-dry cycles. Samplesfired at 1100 °C had good hydric behavior, theyperformed well in the salt decay test, but they didnot perform as well as the samples fired at1000 °C in most accelerated aging tests. Gypsumformed on all the brick samples submitted to SO₂atmosphere regardless exposure time (e.g. gypsumappears following just 24 h of exposure),composition, or firing temperature. Samples withdeposited particulate matter collected from vehicleexhausts (diesel, as well as leaded and non-leadedgasoline motor cars) resulted in the fastest gypsumdevelopment and greater abundance. On the other hand,the blank samples, and the samples withpollution-derived dust collected from historicalbuildings showed little gypsum development. Theimplications of these results in historicalbrick-building preservation in a range of aggressiveenvironments, and in polluted atmospheres inparticular, are discussed.