花生蛋白在碱减量腈纶表面上的接枝及接枝腈纶服用性能研究

研究了在碱减量腈纶表面用聚乙烯醇缩水甘油醚100%(PVAGE100%)交联荆接枝花生蛋白工艺,以及碱减量腈纶接枝交联花生蛋白后碱减量晴纶服用性能的变化.用红外光谱对接枝蛋白后的腈纶进行了表征.采用单因素法研究了碱减量腈纶交联接枝花生蛋白的最佳工艺参数,结果表明:碱减量腈纶用PVAGE100%接枝花生蛋白的最佳工艺条件为PVAGE100%最佳浓度31.08 g/L,最佳接枝温度120℃,最佳接枝时间40 min,花生蛋白最佳浓度31.5 g/L.碱减量接枝花生蛋白后.随着接枝率的升高,白度基本没有变化;回潮平有较大幅度增加;抗静电性能也大幅度提高;抗褶皱弹性略有下降.

Abstract：

Polyacrylonitrile was hydrolyzed by NaOH and then modified with arachin by poly vinylalcohol glycidyl ether 100%(PVAGE100%).It was characterized by FT-IR spectroscopy, and its wearability was studied.The best grafting technology was studied with signal factor method and the best technological pa-rameters were obtained: PVAGE100% concentration 31.08g/L, temperature 120℃, reaction time 40 min and arachin concentration 31.5 g/L.With the increase in the rate of grafting arachin on hydrolyzed polyac-rylonitrile, the whiteness of the polyacrylonitrile fabric showed little change, while its hygroscopic proper-ty and antistatic property increased greatly and its elasticity decreased slightly.     

紫外光接枝改性木塑复合材料的表面抑菌性1）

以二苯甲酮为光敏剂,通过紫外光辐照引发,将N,N－二甲基十四烷基对乙烯基苄基氯化铵（ C9 H9 Cl－14DMA）单体接枝在含有乙烯基的木塑复合材料（ WPC）表面,赋予WPC表面抗菌功能。利用XPS光电子能谱和扫描电子显微镜（SEM）对WPC的表面化学组成和形貌结构进行表征,采用抑菌圈法对大肠杆菌进行抑菌活性研究。探讨了单体质量浓度、光敏剂质量浓度、光照时间对接枝率的影响。结果表明,最优的接枝条件为：光敏剂质量浓度0．150 g/mL、单体质量浓度0．800 g/mL、光照时间3 min,接枝率为62．5μg/mm2,接枝后的WPC表面具有良好的抑菌性能。     

影响共聚焦荧光法检测单细胞中蛋白表达的因素探讨

采用免疫荧光技术联合共聚焦技术研究不同培养细胞中蛋白的表达及定位.结果发现:①同样以丙酮固定293细胞,不用0.5%Triton X-100处理,着丝粒蛋白E亚型(CENP-E)在分裂期细胞核周浓聚,核内未见;而用0.5%TritonX-100处理后,CENP-E呈散点状分布于分裂期细胞的核内.②分别以甲醇、95%乙醇和4%多聚甲醛固定并以1%TritonX-100处理k562细胞,不同固定剂处理组间结果无明显差异,信号转导与转录激活因子(STAT3)均定位于胞浆.共聚焦系统PMT=511时,显示胞核染色适中,核仁染色明显,而PMT=593时,整个核呈饱和染色状,微细结构不清楚.③以2%甲醛联合0.5%TritonX-100处理平滑肌细胞,固醇调节元件结合蛋白裂解激活蛋白(SCAP)在整个细胞中呈弥散性分布,核内含量较高,高尔基体上SCAP无特异性高表达.结论:是否使用TritonX-100处理对293细胞中核蛋白CENP-E的定位具有较大影响;k562细胞对醛类固定剂及醇类固定剂无特殊选择性,图片采集时共聚焦参数PMT对蛋白定位结果也有影响;醛类固定剂和Triton联用可准确定位SCAP在平滑肌细胞中的表达.

Abstract：

The expression and location of proteins in single cells cultured under different conditions were studied with a laser scanning confocal microscope. CENP-E appeared mainly around the nucleus in HEK293 cells by fixing with acetone without 0.5% Triton X-100 treatment, but localized mainly in the nucleus when the cells were fixed with acetone plus further 0.5 %Triton X-100-PBS solution and scattered in the nucleus with condensed points. Plus l% Triton treatment, K562 cells fixed with 4% paraformaldehyde, methanol or 95 % ethanol all showed that STAT3 protein mainly distributed in cytoplasm at the edge of the cell body, the nucleus occupied a greater part of the cell body with PI staining, nucleolus staining seemed stronger under PMT= 511, but seemed the same as the other part of the nucleus under PMT=593. SCAP (SREBP cleavage-activating protein) could be detected in cytoplasm and was more accumulated in nucleus in smooth muscle cells fixed with 2 % formaldehyde and 0.5 % Triton penetrating, and Golgi apparatus were found to scatter around the nucleus. In conclusion, it is important to locate CENP-E protein in HEK293 cells with TritonX-100 by immunofluorescence microscopy. SCAP in smooth muscle cells and STAT3 expression in K562 cell can be exactly located with the combination of formaldehyde and Triton penetrating. STAT3 expression in k562 cells fixed with formaldehyde or spirits fixative has no difference.The confocal system itself, such as PMT gain, can also affect the location of proteins in single cells.     

胡柚皮中类黄酮素提取及残渣综合利用工艺研究

采用单因素法对比乙醇浸提、微波提取、超声波提取以及组合工艺提取类黄酮素的效果,优化其工艺参数。然后,再将提取残渣分别进行碱化、醇化预处理,进行柠檬酸和季铵盐接枝改性,以Cu~(2+)和F~-作为模型离子,进行静态吸附和动力学试验。结果表明,三元组合工艺类黄酮素提取率在同等其他条件下比二元法提高了13.9%。优化后的提取条件如下:70%(V/V)乙醇溶液(浸提比1∶10)浸泡下,依次于40 kHz 200 W超声振荡9 min、400 W微波加热8 min、80℃加热回流3 h,可获得3.17mg/g提取率。25℃柠檬酸残渣改性吸附剂对Cu~(2+)的吸附等温线符合Langmuir模型G=G_0c/(A+c),G_0=0.99 mg/g,A=5.95mg/g。季铵盐残渣改性吸附剂对F~-的吸附等温线符合Freundlich模型G=ac~b,a=0.006 6,b=3.55。吸附动力学研究表明,阳离子的吸附饱和时间为10 min,阴离子的吸附饱和时间为5 min。这表明从胡柚皮中提取类黄酮素后,其残渣经化学改性后成为离子吸附剂在技术上具有可行性。     

淀粉-衣康酸接枝共聚物的合成及表征

以可溶性淀粉和衣康酸为原料,以过硫酸钾-亚硫酸氢钠氧化还原体系为引发剂,合成淀粉-衣康酸接枝共聚物,采用红外光谱对其共聚产物进行结构表征,并分析了引发剂用量、淀粉与衣康酸质量比、反应温度等因素对聚合反应的影响.结果表明:当淀粉与衣康酸质量比为1:5、引发剂用量为淀粉质量的3％、反应温度为50℃时,制备得到的接枝共聚物接枝率最高.     

疏水缔合阳离子淀粉的合成研究

本研究以环己烷为连续相,Span 80/Tween 80为分散剂,采用氧化还原引发体系,通过反相悬浮聚合技术,合成疏水缔合阳离子淀粉接枝共聚物。研究了反应温度,引发剂用量,反应时间对接枝性能的影响及溶解性能。并用IR、X衍射对共聚物进行了表征。结果表明:采用氧化还原引发剂可使聚合反应低温快速进行,在m(St)∶m(AM)∶m(DMDACC)∶m(OA)为4∶7.4∶1.5∶0.6时,引发剂用量3.1 mmol/L,30℃反应3 h,单体转化率92.6%,接枝率53.8%,粘均相对分子质量(MV)3.26×106。     

魔芋葡甘聚糖接枝共聚物的合成及其抗菌活性

考察了一种实验室自制的魔芋葡甘聚糖季铵盐衍生物(KGM-g-DMAE-BC)的合成以及抗菌性能。正交试验优选出的最佳合成条件为:反应温度70℃,单体质量比(mKGM∶mDMAE-BC)1∶5,引发剂用量0.7 mmol/L,反应时间3 h。悬菌定量实验结果表明:KGM-g-DMAE-BC(接枝率为38.5%)对大肠杆菌、金黄色葡萄球菌及白色念珠菌有较强的杀菌作用,在振荡作用15 m in后,平均灭杀率分别为99.99%、94.26%和99.99%。     

淀粉接枝型保水剂施用方式对玉米出苗率及产量的影响

<正>1试验材料与方法1.1试验材料试验设在黑龙江省五大连池市二龙山农场农业科技园区。供试玉米品种:德美亚1号。供试保水剂品种:普通淀粉接枝型保水剂。1.2试验方法本试验分为盆栽试验与小区试验。盆栽试验,试验用盆上口直径22cm,下口直径19.5cm,盆高21cm。共12个处理,主要分为3种方式:不施保水剂(对照)、干施保水剂后浇水(干施)、保水剂与水混合后施用(湿施),每种方式均控制盆内土壤在四个含水量水平上:A(含水量占田间持水量     

木材表面非极性化原理的研究 Ⅱ.木材与苯乙烯接枝共聚过程中化学官能团和表面极性的变化

通过对杉木、杨木木材及其主要成分在与苯乙烯接枝共聚反应过程中化学官能团及临界表面张力变化的研究,探讨了木材各化学组成在接枝共聚过程中的反应性能和对木材表面极性的影响。研究表明:木材可与苯乙烯发生接枝共聚反应,反应只在木素和苯乙烯之间进行。木材与苯乙烯接枝共聚可降低木材临界表面张力,即降低木材表面自由能,从而有效地改善木材的极性。     

剑麻纤维接枝丙烯酸吸水树脂的研究

以剑麻纤维为骨架,以一定中和度的丙烯酸和少量丙烯酰胺为单体,采用硫代硫酸钠(Na2S2O3)和过硫酸盐为引发体系,通过接枝反应制备纤维素基吸水树脂.考察引发体系及条件对制备吸水树脂的影响,探索单体配比、交联剂浓度对吸水树脂的吸水能力、吸水速率、保水性能和反复吸水性能的影响.结果表明:在硫代硫酸钠和过硫酸盐组成氧化还原引发体系中,采用过硫酸钾和过硫酸铵两种氧化剂组成的引发体系,在引发剑麻纤维接枝丙烯酸单体的反应中起到协同效应;有效地将过硫酸盐引发接枝反应的温度由常用的55～80℃降至30～50℃,同时,达到较高的接枝率和单体转化率.交联剂的用量、丙烯酰胺(AM)的用量和丙烯酸(AA)的用量对吸水倍率和吸盐水倍率有显著的影响.吸水树脂的最大吸水倍率为530 g/g,最大吸盐水倍率为58 g/g,吸水速率为8 g(g·min),树脂具有良好的保水性和热稳定性.FTIR分析结果表明,吸水树脂是纤维素和丙烯酸的接枝共聚物.TGA分析结果表明,吸水树脂比剑麻纤维热稳定性好.