简要分析了有限元法和边界元法在梁类零件振动仿真分析中的优点和缺点．梁是常用的机械结构件,在工程机械中的应用非常广泛．应用边界元法对矩形梁弯曲振动进行了仿真分析,当梁的弹性常数不变而横截面的高宽比改变时．其固有振动频率会相应地改变,为通过改变结构参数来改善梁结构的动力学性能进行理论探索．     

木塑构件强度特性的研究

在包装、家具框架中L型构件是一种比较常见的结构形式.本文通过分析跨距对木塑L型构件结构强度和连接结构强度的影响,得出以下结论:跨距对木塑L型构件结构强度的影响非常显著,跨距越短,结构强度越大;跨距对连接结构强度影响也很大,跨距在190mm左右时,连接性能最好.     

地下防水工程渗漏水的修堵

作者结合实践,分析了地下工程渗漏水的原因往往是由于设计不合理及施工不规范而造成的,并提出了相应的防治措施。     

Growth and water potential of j-rooted loblolly and eastern white pine seedlings over three growing seasons

The effects of j-rooting on water stress and growth of loblolly (Pious taeda L.) and eastern white pine (Pious strobus L.) were examined over three growing seasons in the field. Seedlings were planted in an area with severe herbaceous competition with either their roots planted straight or bent into a j shape. All seedlings were planted with their root collars placed at the soil surface. During the first year j-rooted seedlings consistently had lower water potentials but never statistically significant. Since both treatments were planted with the root collar at the soil surface, this trend was likely due to an initial shallower root system in j-rooted seedlings. In year three no differences in water potential were significant and no trends were evident. Growth did not differ significantly by treatment at any time but, by year three, j-rooted plants were consistently larger for both species.     

Current Research and Development on Deformation and Fixation of Bended Wood and Wood-based Composites

There are many advantages of bended wood,such as good-looking shape,simple process and low cost.The product,however,is easy to get recovery,which is urgent to be dealt with.This paper concludes the features of deformation and recovery of bended wood and wood-based composites and summarizes four treating methods to keep dimensional stability.Compared to bended solid wood,some elementary perspectives on the research of bended wood-based composites are presented.The purpose of this paper is to suggest:1)to investigate the optimum heating time and temperature that bended wood and wood-based composites need from the formation of deformation to the recovery and to the permanent fixation,according to its changes of dimensional stability such as curvature radius;2)to measure the composites comprised of wood and adhesives on the changes of stress relaxation,dynamic viscoelasticity and crystal1ization field;3)to quantitatively analyze changes of the major components in wood cell wall polymers as well as the composites under heat/steam treatment and untreated conditions.It will be helpful for subsequent research to clarify on the mechanisms of permanent fixation of bended wood and also contribute to that of wood-based composites.     

Compressive deformation of wood impregnated with low molecular weight phenol formaldehyde (PF) resin II: effects of processing parameters

To obtain high-strength phenol formaldehyde (PF) resin-impregnated compressed wood at low pressing pressure, the effects of resin content, preheating temperature, pressing temperature, and pressing speed on the compressive deformation of oven-dried low molecular weight PF resin-impregnated wood was investigated. With an increase of PF resin content, the Youngs modulus of the cell wall perpendicular to the fiber direction decreases, and collapse-initiating pressure decreases linearly with the Youngs modulus. This indicates that the occurrence of cell wall collapse is strain-dependent. By increasing preheating temperatures, the collapse-initiating pressure increases due to the increment of the Youngs modulus of the cell wall. An increase in pressing temperature results in the thermal softening of the cell wall and causes collapse at a lower pressure. The wood is compressed effectively despite accelerated resin curing. The pressing speed significantly affects the viscoelastic deformation of the cell wall and the wood is well deformed with decreasing pressing speed, although the differences in density and mechanical properties are relatively small after a pressure-holding period of 30min. In all the parameters examined in this study, the Youngs modulus and bending strength increase with increasing density.     

三层实木复合地板弯曲变形原因及控制措施

阐述了三层实木复合地板的结构特点,对其产生弯曲变形的原因进行分析,并结合生产实际提出了三层实木复合地板的质量控制措施。     

基于C语言的结构用集成材木梁抗弯刚度模型研究

基于平行轴定理,采用变换截面法建立结构用集成材木梁的抗弯刚度C语言可执行程序模型,并通过足尺木梁的抗弯力学性能试验验证模型的有效性。本试验根据木材抗弯弹性模量测定方法国家标准（GB/T 1936.2—2009）中的相关要求,测定层板木材的抗弯弹性模量并将其导入C语言程序模型,得到梁体抗弯刚度的模型理论值。依据结构用集成材国家标准（GB/T 26899—2011）对木梁进行四点抗弯测试并实时采集梁体跨中挠度、荷载数据,得到梁体抗弯刚度的实测值。对比梁体抗弯刚度的模型理论值与实测值,得出其平均相对误差率为3.89%。结构用集成材木梁抗弯刚度模型的建立应充分考虑梁体自身的构造缺陷,以综合层板的力学性能变异性及尺寸效应等影响因素,合理引入修正系数,提高模型的准确度与适用性。     

高温冻土融化固结的水热力耦合模型构建

依据比奥(Biot)固结理论,应用总拉格朗日(Total Lagrangian)方法建立考虑大变形的应力场控制方程;引入应力-温度耦合损伤模型作为冻结状态下的高温冻土本构模型,以未冻水含量为耦合节点建立水热力耦合模型;通过冻结粉质黏土的升温三轴压缩试验验证模型的有效性,分析水热力耦合模型与应用小应变假设的模型的差异。结果表明:水热力耦合模型经过引入高温冻土应力-温度耦合损伤本构模型,冻结状态初始融化阶段预测结果与试验曲线较吻合。在变形加速至缓慢变形过渡阶段(1.5~2.5 h),模拟结果与试验曲线存在一定差异,但整体可有效预测高温冻结粉质黏土的融化固结过程。考虑大应变状态的水热力耦合模型,对融化变形的预测精度优于应用小应变假设的模型。根据模拟结果,分析水热力三场的相互作用关系、冻土融化固结过程,高温冻土外部升温状态下,边缘融化部分形成排水通道,加速上部土体水分排出。     

ACM焊点类型对有限元结构刚度的影响分析

针对在白车身等复杂的焊接结构进行有限元分析过程中,不同焊点的模拟方法对结构的弯曲刚度和扭转刚度影响较大的问题,本文通过对ACM焊点进行研究,得出其对有限元分析过程中弯曲刚度和扭转刚度的影响。