Condensation reactions of phenolic resins V: cure-acceleration effects of propylene carbonate

Propylene carbonate (PC) is known as one of the cure accelerators for alkaline phenol–formaldehyde resins. To elucidate the cure-acceleration mechanisms, the effects of PC on the condensation reactions of monomeric hydroxymethylphenols (HMPs) were investigated and compared with those of PC hydrolysate, sodium bicarbonate (NaHCO₃) and ethyl formate. Immediately after the reaction started, PC, decomposing itself simultaneously, accelerated the formation of the ortho-para methylene-bonded dimer of 2,4,6-trihydroxymethylphenol. This effect of PC was very similar to that of ethyl formate. To the contrary, PC hydrolysate accelerated the formation of the para-para methylene-bonded dimer throughout the course of the reaction. This effect of PC hydrolysate was identical to that of NaHCO₃. These results indicate that PC increases the reactivity of the ortho-hydroxymethyl group, presumably through transesterification. On the other hand, NaHCO₃ is formed by the hydrolysis of PC or decomposition of the transesterified HMPs and it increases the reactivity of the para-hydroxymethyl group.     

重组竹材用酚醛树脂渗透性能研究

对四种重组竹材用酚醛树脂在不同胶液固体含量、浸胶温度和浸胶时间等条件下进行竹材浸胶试验。结果表明：胶液固体含量增加时,竹材浸胶量先增大后减小,固体含量25%时浸胶量最大,达到22.6%;浸胶温度升高浸胶量增加,浸胶温度55℃为宜;浸胶时间对浸胶量影响不呈现规律性,浸胶时间需要在60 min以上;树脂分子量大小对渗透性有一定影响,分子量偏小、分布相对较窄且均匀时,渗透性较好。     

EMDI-UF混合胶刨花板制造工艺条件的研究

介绍了东北林业大学人造板研究所在降低人造板游离甲醛释放量的研究成果,利用可乳化异氰酸酯(EMDI)与脲醛树脂(UF)混合胶制造刨花板,使产品达到E1级标准要求。研究结果表明:混合胶的施胶量为7％,采用6％的UF和1％的EMDI是比较适合的比例。将它们混合到一起,不加酸性固化剂,搅拌均匀后喷洒到刨花上,比较适宜的板坯含水率不应超过14％,在175℃下热压4.5min,所粘结的刨花板各项性能都符合GB4897—92—等品和E1级板标准的要求。与UF胶刨花板相比,混合胶刨花板的耐水性得到明显改善,甲醛释放量可降低到7.88mg/100g板。     

改性松香脂环基环氧树脂的机械性能及其影响因素分析

通过测定改性松香脂环基环氧树脂固化物的冲击强度、弯曲强度,研究了环氧树脂的结构、组成及固化时间、促进剂、填料硅微粉的粒径、活性、绝缘等级与用量等因素对环氧树脂机械性能的影响。研究表明,环氧树脂的化学结构与组成是影响材料力学性能的主要因素,以DCT-1为促进剂、120℃固化6～8h、填料硅微粉添加量为环氧树脂质量的2．5倍时,环氧树脂材料的力学性能最佳。     

生物基高吸水性树脂及其在农林生产中的应用

为提高高吸水树脂在农林方面的应用水平,通过查阅大量的文献资料,总结概括了生物基高吸水树脂按原料来源的分类(如淀粉类、纤维素类、海藻酸类、甲壳素&壳聚糖类、其他类等),以及国内外生物基高吸水树脂在农业园林等领域的应用研究进展,并结合当前高吸水树脂相关研究与应用中存在的问题,提出了今后的研究方向。     

大孔吸附树脂纯化油茶壳中多酚类化合物的研究

以油茶壳为原料,采用大孔吸附树脂对油茶壳中多酚的分离纯化工艺条件进行了研究。考察了6种大孔吸附树脂对油茶壳中多酚类化合物的吸附分离性能,确定大孔树脂分离油茶壳中多酚类化合物的工艺条件。结果表明,AB-8树脂对油茶壳中多酚具有良好的吸附分离性能,其工艺条件为:质量浓度为3.78mg/mL,pH值3.7,油茶壳原料液以3BV/h的流速上柱吸附,再用6倍树脂体积的80%乙醇以3 BV/h的流速解吸,产品中多酚含量达61.3%,回收率为77.64%,样品得率为2.95%。     

苯基含氢硅树脂的制备及固化性能研究

以苯基三甲氧基硅烷(Phenyltrimethoxysilane,PTMS)、1,1,3,3-四甲基二硅氧烷(1,1,3,3-Tetramethyldisiloxane,HTMS)和六甲基二硅氧烷(Hexamethyldisiloxane,HMDSO)为主要原料,酸性阳离子交换树脂为催化剂,采用水解缩聚的方法制备了苯基含氢硅树脂(Hydrogen containing phenyl silicone resin,PHMT树脂),采用傅里叶转换红外线光谱(Fourier Transform Infrared Spectroscopy,FTIS)和核磁共振氢谱(1H Nuclear Magnetic Resonance Spectroscopy,1HNMR)对其结构进行了表征,并对其制备工艺、固化性能进行了研究.结果表明,甲氧基的水解程度达99.9%,但羟基缩聚不完全,其残留量约为质量分数0.57%.采用含氢量为体积分数0.37%,黏度为722 mPa·s的苯基含氢硅树脂为交联剂,其固化物机械性能较好.     

不同固含量低分子酚醛树脂浸渍改性杉木板材性能的研究

为改善杉木的物理力学性能,采用真空-加压浸渍工艺,对速生杉木进行低分子酚醛树脂增强改性处理,分析不同树脂增重率对改性杉木性能的影响,以及树脂在木材长度和厚度方向上的分布特点。结果表明,杉木经过固含量为10％、20％、30％的酚醛树脂浸渍处理后,其尺寸稳定性随树脂固含量的增加逐渐提高,静曲强度由64.5 MPa提高至75.0 MPa,弹性模量和表面硬度分别提高了6.1％、27.5％、48.2％和29.8％、63.1％、73.8％,但冲击韧性随着树脂增重率的增加而逐渐降低;树脂在木材长度方向上分布均匀,在厚度方向上木材表面多于其内部。     

一种EGCG单体纯化新工艺

以粗酯型儿茶素为原料,研究采用大孔吸附树脂和结晶纯化儿茶素单体EGCG的制备工艺。通过比较4种大孔吸附树脂对EGCG的吸附和解吸能力,筛选出最优树脂AB-8,并考察乙醇梯度洗脱等特性,再经过结晶析出EGCG晶体。结果表明:AB-8大孔吸附树脂对EGCG具有较好的吸附选择性,通过10%乙醇洗脱,EGCG产品纯度从54.41%提高到了92.65%,得率达93.38%,结晶后得纯度达98%以上的EGCG单体。     

脲醛树脂及三聚氰胺改性脲醛树脂对桉木热解液组分的影响

为了有效利用热解技术处理废弃人造板,采用气质联用技术对比分析桉木、添加质量分数10% 脲醛(UF)树 脂的桉木、添加质量分数10%三聚氰胺改性脲醛(MUF)树脂的桉木、UF 树脂、MUF 树脂的热解液组分。结果表 明:桉木热解液成分复杂,其中2,5-二甲基呋喃的相对含量达到27.56%,3-甲基-2-羟基-2-环戊烯-1-酮和4-(2-氧 代)-2-环己烯-1-酮的相对含量分别为7.04%和7.02%,2,6-二甲氧基苯酚的相对含量为9.48%。添加UF 树脂的 桉木热解液检测到含氮物质的相对含量比桉木热解液增加22.93%,该热解液有望用于肥料生产和土壤改良;添加 MUF 树脂的桉木热解液出现了木糖、丁内酯等桉木热解液中未检测到的产物。