水曲柳落叶松纯林与混交林的枯叶分解动态

在２９年生的水曲柳落叶松纯林和混交林中,用网袋法研究了枯叶的分解动态。通过１ａ的分解。水曲柳纯林枯叶质量损失率为６６．０％;混交林为４１．５％;落叶松纯林为２５．７％。阶段质量损失率三种林分均是５月５月－７月５日最大。７月６日－９月５日次之。１１月６日－第２年５月８日最低。经模拟研究表明,水曲柳纯林枯叶９５％分解需２．８ａ;混交林需５．３ａ;落叶松纯林需１０．０ａ。通过对枯叶养分含量的测定表明;在     

水曲柳薄木贴面装饰板的表面化学处理

采用过氧化氢为主剂的木材表面处理剂, 对水曲柳薄木贴面装饰板进行辊涂法工业性连续试验。结果表明： 按国家装饰板标准大部分水曲柳薄木贴面装饰板外观质量明显上一档次; 处理对水曲柳薄木贴面装饰板力学性能无影响; 油漆安全性试验符合要求, 处理成本只有０１０ ～０３０ 元·张－ １ , 具有生产应用价值。图１ 表５参４     

带约束拉杆钢管/竹胶板组合空芯短柱的偏心抗压性能

采用冷弯薄壁方型钢管和胶合竹板通过横向约束拉杆和结构胶黏剂复合成顺纹抗压的组合空芯短柱(thin-walled steel tube/bamboo-plywood composite hollow short column with binding bars,SBCCB),采用9个试件研究SBCCB试件的偏心抗压破坏模式、抗压承载力和影响规律。结果表明,SBCCB试件受压破坏形态主要为柱端开胶破坏、横向约束拉杆之间基体胶合界面开胶剥离破坏和胶合竹板局部压屈破坏;SBCCB抗压极限荷载随胶合竹净横截面积增大而提高,随着长细比和荷载偏心率的增大而降低,随空心率增大而增大;约束拉杆可有效延迟SBCCB的开胶剥离破坏,改变屈曲破坏模式,有助于试件抗压承载力的提高;相对于不带约束拉杆试件,SBCCB抗压极限应力提高约17.64%;局部翘曲随约束拉杆间距减小而减小,相对拉杆间距比3.0以下能确保较小的局部翘曲变形。薄壁钢管和胶合竹板能形成较好的复合抗压结构单元,该批试件平均值抗压强度达到18.54 MPa,展现了优异的抗压性能。SBCCB可作为绿色建筑材料广泛应用于现代装配式工程结构,同时拓展竹材的应用途径,实现"以竹代木,以竹代钢",具有很好的工程价值和应用前景。     

丙烯酰胺-降解玉米蛋白复合胶黏剂的研究

研究了丙烯酰胺改性降解玉米蛋白、制备Ⅱ类胶合板用无醛胶黏剂。通过正交试验表明,当降解玉米蛋白500g、丙烯酰胺40g、顺丁烯二酸酐10g时,用所制得的改性玉米蛋白胶黏剂压制的胶合板的胶合强度达到0.97MPa,符合Ⅱ类胶合板国家标准要求。     

魔芋葡苷聚糖/壳聚糖共混胶黏剂应用于胶合板的研究

以胶合强度为考察指标,进行魔芋葡苷聚糖/壳聚糖共混配比胶黏剂工艺的制备研究.试验结果表明,胶黏剂中各组分用量的较佳参数为:壳聚糖1%,魔芋葡苷聚糖1.5%,NaOH为1%.此配比制备的胶黏剂压制的胶合板,干状胶合强度最大;在壳聚糖1%,魔芋葡苷聚糖1.5%,NaOH为2%的配比时,胶合板的湿状胶合强度最大.     

Tree-ring-width chronology of Larix gmelinii as an indicator of changes in early summer temperature in east-central Kamchatka

We developed a 378-year tree-ring-width chronology based on 110 core samples from 55 individual trees of Larix gmelinii (Rupr.) Rupr. growing in a wide open forest close to the tree line in the Kronotsky National Park. Reflecting strong climatic control over tree growth not only within the study area but also more extensively over central Kamchatka, our chronology was well correlated with those from other larch sites. Response analysis with 10-day mean temperature revealed that the ring width was primarily controlled by the temperature of early summer, i.e., of late May through late June (40 days). While the regression models for a formal reconstruction failed to pass stringent verification tests commonly used in dendroclimatology, the relationship between tree growth and climate was statistically significant and credible. We therefore used our chronology as a proxy of early summer temperature. The chronology shows a cool period from the 1660s until the 1680s, followed by gradual warming until ca. 1800, then by a slight cooling trend extending to ca. 1910, and a warming trend continuing up to the present, with decadal fluctuations throughout the chronology. The warming trend found in our chronology over the twentieth century is generally consistent with the ones commonly appearing in higher latitudes.     

落叶松木材的热解特性

采用热重分析仪研究了在不同升温速率、粒径下,落叶松树皮和实木的热解特性.结果表明:升温速率升高使热重(TG)和微商热重(DTG)曲线向高温侧移动,热解主要阶段变宽;粒径增大,DTG曲线温度增加,GDT绝对值减少;落叶松树皮GDT最大值为-0.0048,落叶松实木GDT最大值为-0.01,落叶松实木的热解转化率大于落叶松树皮的热解转化率.     

热重法研究落叶松热解动力学特性

采用热重分析仪,研究了氮气气氛下升温速率分别为20、30、40、50℃/min时落叶松木材的热解过程,并使用不同动力学分析方法对落叶松主要热解阶段进行了动力学研究,探讨了各方法之间的相似性.落叶松的热解过程可以分为预热、前热解、热解和后热解4个阶段.Freeman-Carroll法线性拟合结果表明,落叶松主要热解阶段可...     

薄壁C型钢—竹胶板组合箱型柱抗震性能试验

提出了一种新型的组合柱—以两块薄壁C型钢为基本骨架口对口拼接,在型钢腹板及翼缘处用结构胶黏剂黏结4块竹帘胶合板,形成截面形式为箱型的薄壁C型钢—竹胶板组合柱.以钢板厚度、长细比、轴压比等为基本参数,对5根组合柱进行了拟静力加载试验,观察组合柱在不同参数设置下的钢板、竹胶板的应变变化和荷载—位移滞回曲线,得到了组合柱的承...     

落叶松杂种与亲本ISSR鉴别技术

以兴安落叶松（Larix gmelini）、长白落叶松（Larix olgensis）和日本落叶松（Larix Kaempferi）及其杂种子代当年生嫩叶为研究材料,采用ISSR分子标记技术对落叶松亲本与杂种进行了鉴别.结果表明:用ISSR16和ISSR19号引物扩增的特异条带能够分别鉴别兴安落叶松×长白落叶松杂交种和...