Modeling of Liquidus Temperature for Al-Si Cast Alloys with Adaptive Neuro-fuzzy Inference System

During the melting and processing practices, an accurate knowledge of liquidus temperature is necessary in the determination of process parameters relating to a given alloy. Adaptive neuro-fuzzy inference system (ANFIS) modeling method has been used to improve accuracy of prediction for liquidus temperature based on the compositions of Al-Si series cast alloys. The developed fuzzy inference system could extract Takagi-Sugeno type fuzzy rules from data directly, and has a feed-forward network structure with supervised learning capability. In order to adapt the parameters of the model, the proposed fuzzy inference system is trained over a wide range of compositions from the published data of industrial alloys. The result shows that, the developed ANFIS model can capture non-linear relationships between compositions and liquidus temperature, and then provides better prediction than the reported multiple statistic analysis. The developed model can be used to predict the liquidus temperature needed in computer modeling and thermodynamic calculation, which are needed in the aluminium alloys casting industry and research.     

压铸铝合金制件的质量控制

简述铝合金压铸件从原材料供给、压铸模具的设计与制造、压铸生产过程中各工艺参数的控制及其对压铸件质量的影响,提出在这一过程中的控制措施.     

镁合金消失模铸造充型过程中模样-金属界面行为的研究

通过直接观察充型过程和金属充型速度的标准方差分析技术研究了抽真空条件下镁合金消失模铸造充型过程中模样-金属界面行为。结果表明：在镁合金的浇注温度下，泡沫模样主要熔解为液态产物。在不抽真空时充型过程主要受模样-金属问热解产物的排除控制，金属前沿充型平稳并呈微凸形，充型速度很小并持续降低。然而，在抽真空条件下金属充型更多地受模样-金属界面处模样分解控制，金属前沿极不平稳并呈不规则的凹形，在充型过程中金属的充型速度变化很大并且无明显的规律可循。金属的充型速度随真空度提高而迅速增大，真空度与浇注温度对充型速度的影响具有很强的交互作用；进一步提高真空度，浇注温度成为影响充型过程最重要的因素，而真空度以及真空度与浇注温度的交换作用对充型速度的影响大为减弱。基于以上研究，提出了负压条件下镁合金消失模铸造充型过程中模样-金属界面处模样的热解和热解产物的排除行为模型。     

温度对桦木单板表面化学镀Ni—Cu—P三元合金的影响

利用化学镀方法在桦木单板表面沉积Ni—Cu—P三元合金,考查施镀温度对镀后单板表面电阻率和电磁屏蔽效能的影响,采用扫描电镜(SEM)观察镀后单板的表面形貌,利用EDS和XPS分析镀层成分,利用X射线衍射(XRD)分析镀层的组织结构,采用直拉法测定镀层与木材表面的结合强度。结果表明:当温度从80℃升高到90℃时,镀层平均表面电阻率从0.451Ω/cm2降低至0.301Ω/cm2;继续升高温度,表面电阻率小幅升高;在90℃时,施镀单板的电磁屏蔽效能在9 k Hz~1.5 GHz频段达到55~60 d B。SEM观察发现镀层连续、致密且具有金属光泽;EDS分析可知镀层中存在Ni、Cu和P元素,XPS分析可知镀层组成为Ni、Cu、P,其质量分数分别为79.84%、11.82%和8.34%;XRD分析表明镀层为微晶态结构;镀层与木材表面结合牢固。     

Cyclic Creep Constitutive Model of Magnesium Alloy at High Temperature

With high strength-to-weight ratio and excellent technological properties, Magnesium Alloy plays a more and more important role in automotive industry. But the inferior high temperature creep resistance limited its application to power components such as engine and transmission cases. In order to investigate the cyclic creep behavior of Magnesium Alloy at high temperature, creep tests of plate specimens AM50 were conducted. Through the analysis about the microstructure and defects of AM50, an isotropic and scalar damage parameter was introduced into an existing creep constitutive model. Furthermore, a Fortran code based on numerical algorithm was developed to simulate plasticity, cyclic creep, and recovery phenomenon observed. Comparisons between calculated results and experimental data show good agreement.     

化学镀非晶Ni-Mo-P与Ni-P镀层性能的对比

通过在镀液中加入Na2MoO4的化学沉积法对酸性Ni-Mo-P镀层的形成进行了实验研究，运用正交设计法确定了此多元合金镀的最佳工艺。运用能谱法和X射线衍射实验对镀层的成分，结构及其性能进行了分析并与Ni-P镀层进行了对比研究，结果证明Ni-Mo-P镀层比Ni-P镀层的热稳定性高，耐腐蚀性好。     

铝合金纳米粉末中相生成规律的初步研究

采用蒸发凝聚法制备了Al-M(M=Cu,Fe,Cr,Mn)合金纳米粉末,研究了粉末中的相生成规律.实验结果表明,纳米粉末的相组成及其相对含量主要是由母合金的成分决定的.在Al-Cu合金纳米粉末中生成的合金相有-θCuAl2,γ2-Al4Cu9,-βAlCu3,Cu在Al中的最大固溶度明显高于Al-Cu平衡相图上的值.在Al-Fe合金纳米粉末中生成了Al13Fe4和FeAl2相.在Al-Mn和Al-Cr合金纳米粉末中则分别生成了-βMnAl6,η2-Al8Mn5相和Al13Cr2,Cr9Al17相.纳米颗粒的组织和形貌与纯金属纳米粒子的差异很大.讨论了合金纳米粒子的形成机理.     

二元合金超微粉末中化合物相生成规律的研究

采用感应加热式的气相蒸发法制备了 Mg- Sb,Bi- Mg,Pb- Mg,Mg- Zn和 Sb- Zn五种合金的超微粉末 ,研究了超微粉末中的相生成规律及粉末粒子的形貌和组织特征 .在 5种合金的超微粉末中均未出现在其合金相图上不存在的化合物相或固溶体相 .在 Mg- Sb合金超微粉末中生成了β-Mg3Sb2 高温相 ,在 Bi- Mg合金超微粉末中生成了 γ- Mg3Bi相 ,在 Mg- Zn合金超微粉末中生成了ε- Mg Zn2相 ,在 Sb- Zn合金超微粉末中生成了 Sb Zn,Sb3Zn4 和 Zn3Sb2 化合物相 ;对于在相图上同时存在固溶体相和化合物相的 Pb- Mg合金 ,超微粉末中只生成了β- Mg2 Pb相 ,未发现固溶体相 .各种合金超微粉末粒子的形貌与相应的纯金属超微粉末的形貌不同 ,形状不规则 ,表面粗糙 ,含有化合物相的粒子衬度不均匀 ,为复相混合组织     

搅拌参数对ZA27合金半固态组织与性能的影响

在连续冷却条件下以不同的参数对 ZA2 7合金熔体进行了电磁搅拌处理 ,并分析了搅拌参数对组织形貌及力学性能的影响。结果表明 ,最佳搅拌时间可选定在 5～ 15 m in之间 ,在连续缓冷条件下 ,半固态 ZA2 7的初生相随搅拌强度提高而细化。