Wood defects during industrial-scale production of thermally modified Norway spruce and Scots pine

This research investigates wood defects, particularly the formation of surface cracks, during the production of thermally modified wood and its exposure to cyclic moisture changes. Boards of Norway spruce and Scots pine originating from different steps within the production of ThermoWood® were collected and wood defects were investigated at macroscopic and microscopic scale. Subsequently, the wood was exposed to capillary wetting cycles to record its sensitivity towards cracking. After the modification process, typical anatomical defects of conventional kiln-drying became more frequent and severe, with the magnitude being to some extent depending on the presence of defects in the raw material. At microscopic scale, damages to ray parenchyma and epithelial cells as well as longitudinal cracks within the cell walls of earlywood tracheids were evident in thermally modified wood. Despite a lower water uptake and higher dimensional stability, thermally modified wood was more sensitive to surface cracking during wetting cycles than unmodified wood, i.e. at the outside face of outer boards (near bark). For limiting surface cracking of thermally modified wood during service life, the use of high-quality raw material, the exposure of the inside face of the boards (near pith) and the application of a surface coating are considered beneficial.     

Modification of three hardwoods with an N-methylol melamine compound and a metal-complex dye

This study evaluated the combined modification and staining of ash, beech and maple wood with a low molecular weight N-methylol melamine compound (NMM) and a metal-complex dye. Wood samples were treated with aqueous solutions of 10, 20 and 30 wt% NMM and 5 wt% of the dye. The treatment caused the fixation of the water-soluble dye by the NMM resin. Vacuum pressure impregnation of unsealed wood blocks did not result in different solution uptake and weight percent gain after curing among the three species, but sealing of the surfaces of the wood blocks to allow penetration only into one direction revealed easiest penetrability of beech followed by maple and ash. UV micro-spectrophotometry and light microscopy indicated that NMM was partly deposited in the cell wall and partly in the lumens. Penetration of the metal-complex dye was shown by means of X-ray micro-analysis (SEM–EDX). The study shows that a combined resin modification and staining of the three wood species tested is possible and that NMM causes fixation of the water-soluble dye.