Fabrication of electropsun PLGA and small intestine submucosa-blended nanofibrous membranes and their biocompatibility for wound healing

In recent decades, tremendous research has focused on the production of nanoscale fibers using synthetic polymers, with the goal of fabricating nanofibrous scaffolds for wound healing. However, the hydrophobicity of such polymers typically hinders attachment and proliferation of the cells. In this study, we combined poly-d,l-lactide-co-glycolide (PLGA) and small intestine submucosa (SIS) to fabricate blended nanofibers for wound healing by electrospinning. PLGA and SIS were dissolved in 1,1,1,3,3,3-hexafluoro isopropanol to produce different weight ratios of PLGA/SIS-blended nanofibrous membranes (NFM). Physicochemical characterization of the electrospun NFM was performed by scanning electron microscopy (SEM), Fourier transform infrared spectroscopy, water contact angle analysis, degradation test and tensile testing. The PLGA/SIS-blended NFM showed improved hydrophilicity and tensile strength. Better infiltration, attachment and proliferation of rat granulation fibroblasts of PLGA/SIS-blended NFMs compared to PLGA NFMs were identified by morphological differences determined by SEM and a water-soluble tetrazolium salt assay kit. Based on our results, the PLGA/SIS blended NFMs were found to be suitable for use as a potential material for wound dressing.     

A novel method based on loop shape for simulating knitted fabric using mass spring model

Fabric simulation is result of combining various methods that have been dramatically evolved during the decade. However, there still exist some limitations. One of the limitations in fabric simulation is lack of using fabric properties such as material, weave structure, density and so on in mass spring modeling. In knitted fabrics, this issue is more important due to their different fabric structures. In this paper, a new mesh based on loop shape for simulating 1×1 rib fabric is proposed which is called Loop mesh. By using the Loop and common meshes, 3D model of drape behavior in 18 types of knitted fabric are simulated. Results of simulation are compared with 3D shape of actual drape behavior in fabric samples which are achieved by depth camera. Results show that the Loop mesh is able to predict the drape behavior of knitted fabric with error value of 5 percent as compared with the real result. It can be found that the Loop mesh produced a closest drape shape to the actual fabric drape than other mesh models.     

Degradation and kinetic modeling of polyvinyl alcohol in aqueous solutions by a H<Subscript>2</Subscript>O<Subscript>2</Subscript>/Mn(II) system

This paper is about the degradation of polyvinyl alcohol (PVA) in aqueous solutions using a H2O2/Mn(II) system. Fourier transform infrared spectroscopy (FTIR) and gel permeation chromatography (GPC) were applied to analyze the degradation products of PVA, and the results revealed that the backbone chain of PVA could be effectively broken and oxidized. Several unsaturated degradation products, including carboxylic acids, ketones, aldehydes, olefins, and alkynes were also detected and identified by gas chromatography-mass spectrometry (GC-MS), which indicated that higher treatment temperatures would considerably promote the generation of lower molecular weight degradation products. According to the work presented in this paper, the degradation efficiency of PVA increased from 55 % at 60 oC to 99 % at 90 oC after treatment when the initial PVA concentration was 5 %, at pH=3 with a H2O2 and Mn(II) dose of 100 ml/l and 0.6 mol/l, respectively. In addition, kinetic modeling indicated that the experimental results were best fitted by the Page-modified model with an activation energy of 48.78 kJ/mol.     

Dyeing performance of the azo dyes containing trifluoromethyl group for polyester fabrics and its single crystal structure

The structures of disperse dyes and their intermolecular interactions have important impacts on dyeing and printing performances for polyester fabrics. The fluorine dyes show some unique molecular stability and photochemical properties. The dyeing property of the azo dye containing trifluoromethyl group for polyester fabrics, 4'-(N-acetoxyethyl-Nethyl)- amino-2-bromine-4-nitro-6-trifluoromethylazo- benzene (D1), was investigated and compared with the similar structure disperse dye. The results show that the high color yield and good exhaustion of the dyed PET fabrics could be obtained. The polyester fabrics dyed with D1 had excellent light fastness. Its single crystal was prepared and the supramolecular interactions were solved by X-ray diffraction. Dye D1 formed triclinic crystals in a trimeric packing mode. The C-F bond distances of CF3 are 1.2730 Å, 1.2240 Å and 1.2900 Å, respectively. The two benzene rings linked azo unit (-N=N-) are obviously twist. The dihedral angle of the two benzene rings is 50.23 o. There are six weak hydrogen bonds around trifluoromethyl group in the intramolecule and intermolecule. The excellent light stability of the dye should be attributed to its unique supramolecular structure.     

Structural and optical properties of cellulose nanocrystals isolated from the fruit shell of <Emphasis Type="Italic">Camellia oleifera</Emphasis> Abel

Cellulose nanocrystals (CNC) with high aspect ratio of 80 have been readily prepared from the inexpensive fruit shell of Camellia oleifera Abel (SCOA) for the first time. In this study, SOCA was consecutively subjected to alkali extraction, hydrogen peroxide bleaching and acid hydrolysis to remove non-cellulosic components and release CNC. The derived CNC possesses a needle-shaped structure that in average diameter and length of 6±2 nm and 500±100 nm, respectively. The crystallinity index of CNC increased to 72 % and the initial decomposition temperature raised to 230 oC. The obtained CNC was formed to nanopaper by vacuum filtration showing high visible light transmittance over 90 %. Thus SOCA derived CNC is of great practical potential to apply in the field of biomedicine, energy, packing, etc. Overall, this study is anticipated to offer new possibility for the CNC production from the inexpensive but abundant agricultural wastes.     

Fabrication of hydrophobic/oleophilic cotton fabric by mussel-inspired chemistry for oil/water separation

A straightforward approach was proposed to modify cotton fabric for oil/water separation based on musselinspired reaction. The poly(DMA-Octadecyl acrylate) was designed to contain key chemical constituents present in mussel adhesive proteins by free radical polymerization of dopamine hydrochloride and octadecyl acrylate, which strongly adsorbed to fabric substrates, providing a special surface for fabric. The chemical structure, surface topography, and surface wettability of the fabric were characterized. The results showed that as-prepared cotton fabric displayed a high CA of >150° when dripped water droplets were on the modified fabric surface, and the oil contact angle (OCA) was close to 0°, it had excellent potential to be used in practical applications and has created a new method of fabric modification for oil/water separation.     

Multifunctional colored polyester fabric treated with dopamine hydrochloride at room temperature: higher tensile,hydrophilicity and anti-bacterial properties along with aminolysis

In this work, dopamine hydrochloride, an environmental friendly compound, was applied on polyester fabric through conventional simple impregnation method in alkaline solution (pH=8.5) at room temperature. In situ spontaneous oxidative polymerization of dopamine form polydopamine (PDA) along with aminolysis of polyester fabric surface. Also, a range of colored polyester fabric were successfully achieved by formation of polydopamine adhesive coating layer at different concentration of dopamine hydrochloride (0.001-4 g/l). Fourier transform infrared spectroscopy and field emission scanning electron microscopy showed deposition of polydopmaine on the polyester fabric surface. The modified colored polyester fabric showed reasonable durability against washing, rubbing and light. The treated polyester fabric with 2 g/l dopamine hydrochloride as optimum concentration indicated not only lower spreading time for water droplet and electrical resistance with higher tensile strength but also very good bactericidal activity against Staphylococcus aureus and Escherichia coli.     

Enzymatic treatment on cotton fibers: degradation kinetics of pectin and influence of shape change on adsorption

Alkaline pectinase was one of the most effective enzymes to treat cotton as alternative agent to replace the conventional alkaline method. Removal of pectin and cutin was considered the explanation for improvement of wettability as well as water adsorption on cotton fiber. However, degradation kinetics of pectin is unclear, and the influence of fiber shape on property changes after enzymatic treatment was ignored. The main objective of this work was to reveal interactions between pectinase and cotton fiber for mechanism study. A heterogeneous catalysis kinetic equation, which is associated with Langmuir adsorption model and enzyme deactivation, was used to describe the heterogeneous catalysis. The enzymatic process conditions were optimized. Raw cotton fibers, pectinase-treated and alkali-treated fibers were characterized by impurities content determination, Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and scanning electron microscope (SEM). Mechanism of water adsorption enhancement on treated fibers was discussed. In addition to elimination of the outer impurities, flat fibers with less twist and shape changes of lumen were also obtained to ensure better accessibility and water adsorption after enzymatic treatment.     

Conductive 3D structure nanofibrous scaffolds for spinal cord regeneration

The complex nature of spinal cord injuries has provided much inspiration for the design of novel biomaterials and scaffolds which are capable of stimulating neural tissue repair strategies. Recently, conductive polymers have gained much attention for improving the nerve regeneration. In our previous study, a three-dimensional (3D) structure with reliable performance was achieved for electrospun scaffolds. The main purpose in the current study is formation of electrical excitable 3D scaffolds by appending polyaniline (PANI) to biocompatible polymers. In this paper, an attempt was made to develop conductive nanofibrous scaffolds, which can simultaneously present both electrical and topographical cues to cells. By using a proper 3D structure, two kinds of conductive scaffolds are compared with a non-conductive scaffold. The 3D nanofibrous core-sheath scaffolds, which are conductive, were prepared with nanorough sheath and aligned core. Two different sheath polymers, including poly(lactic-co-glycolic acid) PLGA and PLGA/PANI, with identical PCL/PANI cores were fabricated. Nanofibers of PCL and PLGA blends with PANI have fiber diameters of 234±60.8 nm and 770±166.6 nm, and conductivity of 3.17×10^-5 S/cm and 4.29×10^-5 S/cm, respectively. The cell proliferation evaluation of nerve cells on these two conductive scaffolds and previous non-conductive scaffolds (PLGA) indicate that the first conductive scaffold (PCL/ PANI-PLGA) could be more effective for nerve tissue regeneration. Locomotor scores of grafted animals by developed scaffolds showed significant performance of non-conductive 3D scaffolds. Moreover, the animal studies indicated the ability of two new types of conductive scaffolds as spinal cord regeneration candidates.     

High water content silk protein-based hydrogels with tunable elasticity fabricated via a Ru(II) mediated photochemical cross-linking method

Silk is very promising in the field of biomaterials as a natural biomacromolecule. Silk protein can be made into various forms of materials, including hydrogels. However, silk protein-based hydrogels have not attracted much attention due to its weak mechanical properties. Here, we report high water content silk protein-based hydrogels with tunable elasticity which were fabricated through Ru(II) mediated photochemically cross-linking tyrosine residues in regenerated silk protein. The regenerated silk protein was characterized by Fourier transform infrared spectroscopy (FTIR). The gelation kinetics of the silk protein was studied by rheology measurements. The compressive mechanical properties of the silk protein-based hydrogels was investigated using compressive tests and dynamic mechanical analysis (DMA). Compressive modulus of the hydrogels reached 349±64 MPa at 15 % strain. The fabricated silk protein-based hydrogels were also characterized by Scanning electron microscopy (SEM), revealing an interconnected porous network structure, typical of hydrogels, with an average pore size of approximately 130 μm. Finally, biocompatibility of the silk protein-based hydrogels was demonstrated through cell culture studies using a human fibroblast cell line, HFL1. The reported silk protein-based hydrogels represent a promising candidate for biomaterial applications.