正交胶合木（CLT）在木结构建筑中应用越来越广泛,特别是在中高层建筑物中。CLT作为楼盖构件使用时,承受柱或墙体施加的垂直荷载,因此CLT产品的设计及应用需要其横纹承压弹性模量和强度方面的参数;改善CLT横纹承压性能,也可以提高整体结构强度和建筑安全系数。文中主要介绍目前CLT横纹承压性能测试方法,总结CLT横纹承压性能影响因素方面的研究进展,以期为国内CLT研究提供参考。     

正交胶合木抗压承载力试验研究

为获得正交胶合木（CLT）截面的综合抗压性能,对由云杉-松-冷杉（SPF）制成的CLT试件进行抗压试验,并基于复合层板理论计算CLT的抗压强度、泊松比及弹性模量等,旨在为CLT力学性能测试提供参考。制作了9个尺寸相同的CLT试件进行轴心受压试验,分析其极限承载力、纵向应变、横向应变、泊松比等的变化规律;依据《木结构设计标准》预测试件的理论承载力并辅以有限元验证。结果表明：荷载-轴向位移试验曲线呈典型的二折线特征,轴压力下试件分别经历了弹性和弹塑性阶段直至试件破坏;经换算得到的SPF等效弹性模量为10 011.57 MPa,抗压强度为35.16 MPa,泊松比为0.39,理论计算值与试验值较为吻合;弹性段有限元模拟结果与试验值吻合良好。     

胶合木构件胶接性能及耐久性研究

以层板胶合木为研究对象,采用ASTM D1037、BS EN1087-1,CAN/CSA-0188,ASTM D3434四种人工加速老化方法对单组份聚氨酯胶黏剂胶合而成的层板胶合木构件进行处理。老化处理后,试材的胶合剪切强度下降幅度在27.8%~44.9%之间,下降程度明显高于吸水厚度膨胀率、静曲强度和弹性模量,据此建议将胶合剪切强度作为判定层板胶合木构件耐老化性能的指标。BS EN1087-1老化处理后试材的性能变化情况SASTM D1037较为相似,且用时短,认为是研究层板胶合木构件耐久性较优的人工加速老化处理方法。     

落叶松集成材的胶合条件和性能

落叶松集成材不仅克服了落叶松易变形、易开裂的缺点,而且纹理美观、材质均匀、强度高,是建筑木构件、家具和室内装修的理想材料,是弥补优质材供应不足的措施之一,为落叶松利用开辟了新的途径。胶合是集成材制造的主要工序。为了保证集成材质量、提高生产率、降低产品成本,掌握诸因素对集成材胶合性能的影响十分重要。本试验在室内用脲醛树脂胶,室外用间苯二酚树脂胶,分别进行了涂胶量、加压压     

应县木塔部分横纹抗压木构件残损分析

对应县木塔二层明层和五层明层内槽转角柱的普拍枋、华拱和泥道拱等横纹抗压构件进行勘测,测量其尺寸与含水率,使用相机拍照记录其破坏特征,后期利用ImageJ软件分析其裂隙率及破坏状况,探讨两明层横纹抗压构件的开裂程度与分布。结果表明：二层明层内槽转角柱上的普拍枋横纹抗压开裂严重,其裂隙率均值为16.6%,多数端面呈散裂状,甚至枋体有完全压溃和部分脱落的现象,华拱和泥道拱横纹抗压裂隙率均值分别为7.7%和12.0%,且拱身已有部分剥离和折断现象;五层明层各内槽转角柱上的普拍枋、华拱和泥道拱横纹抗压破坏主要为细微开裂,其裂隙率均值分别为2.9%、2.6%和2.1%,较二层明层而言,开裂较为轻微;对于木塔两层横纹抗压构件的开裂分布,二层明层多出现在塔身西南和东北方位,而五层明层横纹抗压构件在开裂方位上不明显。本研究所采用的方法可以有效获取应县木塔内部构件的横纹抗压破坏状况及开裂分布,为今后木塔修复与保护工作提供一定的基础数据。     

空心胶合木柱轴心受压性能研究

【目的】节能环保理念越来越受关注,木材作为绿色环保的可再生建筑材料可应用在工程中,目前国内木建筑中应用的木柱主要局限于原木圆柱,为了提高木材利用率,同时降低成本,改善受力性能,满足工程需要,提出一种新型的空心胶合木柱,并进行试验研究分析。【方法】使用相同尺寸拱形锯材作为骨架,利用环氧树脂胶粘剂进行胶合,制作3根空心胶合木柱试件进行轴心加载受压试验,研究空心胶合木柱的轴压力学性能,在试验过程中通过仪器记录应变、应力和位移等数据,主要分析木柱的竖向与横向应变、竖向与侧向位移、稳定承载力等特性,并利用ABAQUS有限元软件进行建模对比分析,探讨木柱最终破坏特征。【结果】空心胶合木柱破坏形态主要是整体压屈破坏,达到极限荷载80%左右时,承载能力快速下降,侧向位移随荷载增加而迅速增大,加载过程中存在多个增长台阶;与同截面积原木圆柱比较,理论承载力提高了4.3%,计算得承载能力稳定系数为0.9,材料缺陷对轴心承载力有影响;通过有限元建模分析,材料在弹性阶段理论值与试验值吻合程度较好。【结论】空心胶合木柱应用在实际工程中是可行的,能够满足工程使用需求,充分利用小型锯材,提高了木材利用率,降低了成本,相较于原木圆柱受力性能更好。     

正交胶合木胶合性能研究现状及展望

胶合性能是胶合木制品的重要性能之一。在正交胶合木（CLT）中木材特征、胶黏剂性能以及木材与胶黏剂之间界面性能共同决定了正交胶合木的胶合性能。木材作为一种天然各向异性材料,其纹理方向不同,造成组坯方式对于胶合性能影响巨大。在胶合性能测试中,取样尺寸、取样形状对于胶合性能的测试结果都有一定的影响。胶合界面性能表征方面的研究正逐渐兴起,但是针对CLT胶合界面性能表征的相关研究报道并不多。有关CLT胶合的研究多集中在胶黏剂和胶合工艺方面,而针对不同锯材单元的特性对胶合性能尤其是耐久性影响的研究尚少有报道。文中基于现有研究对CLT胶合界面性能影响因素进行总结,梳理对比CLT胶合性能测试方法以及胶合界面性能表征技术,并对今后研究方向提出意见和建议。     

胶合木T梁弯曲承载力试验研究

为了增强结构整体性与耐久性,节省材料,降低造价,提出一种理论上适合工程应用的正交胶合木T梁这一新的构件形式。采用兴安落叶松板材和结构胶,制作了正交T梁、平行T梁(高跨比1/7.6)及矩形梁(高跨比1/9.2)共3组试件,进行静力弯曲承载力试验,对比分析各类构件的应变、挠度及极限承载力。结果表明:1)3类梁受弯时均为中部顺纹剪切破坏,正交T梁的抗弯承载力比矩形梁提高了33%,比平行T梁低30%;2)基于刚度等效原则,提出了将正交T梁等效为平行T梁,然后采用Rammer抗剪强度公式来计算其弯曲剪切强度的策略;3)分析表明所提出的策略合理、可靠,扩展了Rammer公式的适用范围。研究成果可为工程应用提供理论依据。     

正交胶合木胶合耐久性能研究进展

胶合耐久性是正交胶合木(CLT)最基本的性能之一,正交组坯结构和层板间缝隙等构造特征增加了CLT胶合耐久性评估方法的复杂性。同时,胶黏剂种类、胶合工艺参数、试件大小及形状和层板处理等均会影响胶合耐久性能的评价结果。比较分析了不同CLT胶合耐久性测试方法,并对CLT胶合耐久性能主要影响因素相关研究进行总结,为后续CLT胶合耐久性能研究提供参考。     

日本柳杉木构件内嵌钢填板销连接横纹承载性能

【目的】研究日本柳杉木构件内嵌钢填板销连接在横纹荷载作用下的破坏机制和承载性能,为木结构梁、柱构件金属件连接时梁端销连接设计提供依据。【方法】在梁端部开槽钻孔后将单个钢销连接到内嵌钢填板,分别对日本柳杉锯材梁和胶合木梁进行横纹荷载作用下的弯曲剪切加载试验,按照日本通行数据分析方法确定销连接短期承载力标准值,并与5个不同国家标准规定的屈服荷载计算值进行比较。【结果】加载初期,荷载-位移曲线呈线性关系,构件处于线弹性阶段,随着位移增加曲线呈非线性,构件进入弹塑性阶段,当位移增加到一定数值,梁端出现初始脆性开裂,荷载瞬间急速减小,随后荷载又随位移增加再次上升,加载至极限状态时,梁构件产生劈裂破坏丧失承载力;最终的破坏形态为梁构件沿销孔水平剪切面开裂、销连接屈服模式Ⅲ型;通过足尺试验得到断面尺寸120 mm×240 mm锯材梁和胶合木梁的钢填板单个销连接短期承载力标准值取决于屈服荷载,分别为8.6和13.7 k N,初始开裂对应的荷载平均值分别为15.0和21.1 k N,屈服荷载平均值分别为14.50和15.00 k N,最大荷载平均值分别为27.0和30.8 k N。【结论】胶合木梁钢填板销连接的最大荷载和屈服荷载平均值均大于锯材梁,且变异系数明显小于锯材梁,含水率低而变异小,从而导致试验获得胶合木梁销连接的短期承载力标准值明显高于锯材梁,当销连接作为中小断面梁柱构件的主要连接方式时,宜选用强度等级确定、质量合格的胶合木作为木构件,比锯材具有更高的连接承载力。梁端销连接节点承载力与单个销连接承载力和销数量具有良好的相关性,可作为梁柱节点梁端销连接设计依据。销连接部位发生销屈服后木材开裂,初始开裂取决于木材抗剪强度、横纹抗拉强度和销所在的梁高部位以及销孔到梁端的距离,发生初始开裂后钢销仍能起到支撑作用,连接节点延性较好;锯材梁和胶合木梁短期承载力标准值与标准中规定的屈服荷载公式计算值吻合度较好。各国标准中关于脆性破坏计算公式均能较好预测销连接木材的脆性破坏,与试验值比较,日本标准对于劈裂破坏的计算值最为接近,欧洲和加拿大标准的计算结果更趋于保守,我国现行标准在销连接设计中尚未考虑木材的脆性破坏,今后应进一步研究完善销连接计算公式和参数,更好地保证木构件连接安全可靠度。     

Detection of glue deficiency in laminated wood with pulse thermography

 Adhesion problems sometimes occur during the production of laminated wood products. To minimize such quality problems, there is a need for a nondestructive test that can provide continuous control of the process and the product. This study presents results from measurements performed to evaluate the potential of pulse thermography as a method to detect glue deficiency in laminated wood. Defect depth, defect size, and degree of glue deficiency have been varied. The surface layer was made of merbau (Intsia bijuga) and the substrate of Scots pine (Pinus silvestris). The results showed that pulse thermography is a promising tool for detecting glue deficiency underneath the thin laminated wood surface layers, mainly because of the short inspection time. Lack of glue with a minimum thermal defect size of 3 was detectable (thermal defect size is defined as the quotient of defect size and defect depth). The penetration depth was 1.0 mm and the highest contrast, 0.62°C, was achieved for one of the largest defects (24 mm) below the thinnest (0.5 mm) surface layer after 1 second. Starved glue joints showed about half the contrast compared to areas with total lack of glue. Received: April 24, 2002 / Accepted: July 26, 2002 Acknowledgments We gratefully acknowledge the support of this work from the Knowledge Foundation and The Swedish Wood Association.     

Finger joint performance of structural laminated bamboo member

The structural performance of finger-jointed laminated bamboo was investigated for two bamboo species by considering the finger length, profile orientation, lamination direction, culm growth height, and mechanical properties of bamboo materials. Based on the growth height variation and bamboo species, the best finger-jointed laminated bamboo was found for the lamina processed from the middle growth height of a moso bamboo culm with the finger profile shown on the width face of the beam. It was 38.7% higher in bending strength than the lowest group, with the lamina from the lower ma bamboo culm showing the finger profile on the thickness face of the beam. When considering the finger length and lamination orientation, the strongest finger-jointed laminated bamboo joined with an 18-mm finger, showing the finger profile on the width face of a vertically laminated beam was 50.1% higher in bending strength than the lowest group having a 12-mm finger showing the finger profile on the thickness face of a vertically laminated beam. The laminated ma bamboo showed higher finger-joint efficiency, 11.6%, than moso bamboo, and the members showing the finger profile on the width surface was 12.3% better in joint efficiency than that showing on the thickness surface of the beam.     

COMPARATIVE STUDY OF WOOD PROPERTIES BETWEENWHITE WOOD OF DAHURIAN LARCH AND MONGOLIANSCOTCH PINE

DahurianlarchandMongolianscotchpinearetwomajorconunerciaIconilbroustTeesinDaxing'anlingForesnyArea.Itisob-viousthattbcwoodproPertiesandworkability'ofthetWoplantsarecompletelydifferent.Butlnrecert'years,ltlsfoundthattherearetwodiffer':nttypesinparameterofwood'scolour.phy'sicalandmechanicalproPertiesandwork-ability'inDahurianlarch,namelyredwoodandx"hite..od.l']Andthepropertiesofwhite`voodaresligl1tlyyellow-white,medianweightandhardness,goodinworkability'andLard-ness,goodinwodability'anduneas…     

毛白杨速生材压缩密实化工艺初步研究

以河北平原地区普遍种植的速生毛白杨木材为对象,通过压缩密化处理,测定素材和处理材的物理力学等性能,分析各因素对回复率的影响,寻找压缩密化的较优工艺条件。结果表明：饱水试件进行微波软化处理后,热压温度180℃左右、热压时间2．5h、压缩量为50％时所得试件性能较好。     

落叶松人工商品林的培育与经营

落叶松是一个高纬度、高海拔的树种,据报导,全世界共有25种,在我国分布的天然落叶松有10种5个变种,它们主要分布于我国的西北、华北、华中、东北和西南山地与高山地区。兴安落叶松和长白落叶松是我国东北地区主要的用材树种之一。它分布广泛,生长迅速,易于栽培。各地区都营     

常温下落叶松材的渗透性

落叶松林改性处理的关键是研究它的渗透性。本实验是在常温加压条件下通过加压时间的改变来考察浸注深度和湿增重的变化，以探索处理工艺与渗透性的关系。     

ARIMA MODEL ON WOOD PROPERTIES VARIATION PATTERN OF KOREAN LARCH

INTRoDUCTIONItwasfOundthatthegoOdnssoffitwasnotgOodandthecOefficientofcorrelahonwaslowwhileuslngthemethodoflinearregressionanalysistoanalysesthewoodgrOwthnngvanahonpatternofPlantedLanxolgensis.ThewoodpowthringProPenieslnc1udesguwthringdenSty,grOWthringwidthandlatewoodpercentage.AslthewoodPrOpenies'parameters,mentionedasabove,thevariahont6ndencywassindlarwiththeresultsofPreviousresearch,butthedopeeofdjssociahonofadjacenttestpointswasbigrelahvely,andthevanahonten-dencywasinduencedbyran…     

碱处理兴安落叶松材改性的研究

采用１％ＮａＨＣＯ＿３水溶液对兴安落叶松（Ｌａｒｉｘｇｍｅｌｉｎｉ）木材进行了处理，并用红外光谱、扫描电子显微镜和化学分析等方法对处理前后木材的尺寸稳定性、吸湿性、官能团和超微构造的变化进行了比较和分析。从而确定影响兴安落叶松木材尺寸稳定性的主要因素。本究研为兴安落叶松木材的改性和利用提供了理论依据。     

落叶松木材的高强度微波辐照法改性

The larch wood was treated by microwave irradiation under different radiant intensity and treating duration. The microwave-treated wood specimens together with the un-treated for comparison were impregnated by water in pressure vessel and then tested for permeability, mechanical properties and microstructure change by SEM to study the modification performance of microwave treatment on larch wood. The results showed that under suitable conditions of microwave treatment the permeability of larch wood was improved without noticeable decreasing of the modulus of rupture （MOR） and the modulus of elasticity （MOE）. The radial parenchyma and some pit membrane were ruptured, and tiny cracks were formed in the cell walls. The formation of tiny cracks in the cell walls serves as man-made channels of gas and liquid and this contribute to improve the permeability of the wood.     

落叶松单宁胶在中密度纤维板生产中的应用

以粉状落叶松单宁胶与传统的酚醛树脂胶制成的中密度纤维板 (MDF)作对比实验 ,证明了落叶松单宁胶制成的板的主要物理力学性能接近于或优于酚醛树脂胶制成的板 ,落叶松单宁胶可基本替代酚醛树脂胶