大豆胶制备竹刨花板的工艺参数探究

以大豆胶竹刨花板的静曲强度、弹性模量、内结合强度、2 h吸水厚度膨胀率作为考察指标,探究了刨花板密度、热压温度、热压时间、表层施胶量、防水剂用量等工艺参数对板材性能的影响。结果表明:大豆胶竹刨花板的力学强度随着刨花板密度的增大而增大,最佳密度为740 kg/m3;随着表层施胶量的增大,刨花板的力学强度也随之增大,表层施胶量应12%;随着热压温度的升高和热压时间的延长,刨花板的力学性能也得到了加强,最佳热压温度和时间为210℃和5 min。防水剂的加入能够显著降低刨花板的2 h吸水厚度膨胀率,加入量以0.4%为最佳。     

纯稻壳板制造工艺与性能研究

为充分利用稻壳资源,以纯稻壳为原料,改性酚醛树脂为胶黏剂,研究了热压温度、热压时间、单位压力以及施胶量对稻壳板性能的影响,结果表明:稻壳板的内结合强度、静曲强度与弹性模量随热压温度、热压时间、单位压力的增加而增加,24 h吸水厚度膨胀率、甲醛释放量相应减低;随着施胶量的增加,内结合强度、静曲强度与弹性模量、甲醛释放量随之增加,24 h吸水厚度膨胀率相应降低。当热压温度采用150℃、热压时间72 s/mm、单位压力1.2 MPa、施胶量为绝干稻壳质量的20%,设计密度0.85 g/cm~3时,10 mm厚稻壳板的物理力学性能指标达到P6型刨花板要求,甲醛释放量满足GB18580—2017标准要求。     

烟秆/木材刨花板的初步研究烟秆

初步探讨了实验室条件下烟秆/木材刨花板的生产工艺,研究了热压时间、施胶量、密度、木刨花加入量等因素对板材的静曲强度、内结合强度、吸水厚度膨胀率的影响.实验结果表明,烟秆/木材刨花板的静曲强度和吸水厚度膨胀率较纯烟秆刨花板有所提高,内结合强度相差不大.     

枝桠材制备木质刨花板成板工艺及性能研究

采用柳树枝桠材制得的片状刨花制备木质刨花板;通过正交试验设计,研究施胶量、预设密度以及石蜡添加量对板材物理力学性能的影响。结果表明,预设密度对静曲强度和静曲弹性模量均有显著的正相关线性影响,对内结合强度有显著影响;施胶量对静曲弹性模量和内结合强度有一定的正相关影响;所有试验因素对2 h吸水厚度膨胀率均有一定影响。从板材性能和成本角度考虑,确定柳树枝桠材制备木质刨花板的最佳工艺为:施胶量7%,预设密度0.7 g/cm~3,石蜡添加量4%。     

杨木薄长刨花高密度板生产工艺的初步研究

研究热压温度、板材密度和施胶量3个生产工艺参数对薄长刨花板静曲强度、弹性模量、内结合强度及吸水厚度膨胀率的影响,得出最佳生产工艺条件。经过对实验数据进行分析,得出热压温度、板材密度和施胶量对刨花板各项物理力学性能均有一定的影响,其中板材密度和热压温度对板材各项物理力学性能影响最大。高密度刨花板最佳工艺条件为：热压温度155℃,板材密度0.88g／cm^3,施胶量12％     

均质结构的泡桐刨花板物理力学性能探讨

利用正交试验法,探讨了密度、施胶量及热压压力对板材物理性能的影响,提出较佳的工艺参数。研究表明:在试验范围内,密度增大,力学强度和吸水厚度膨胀率随之增大;施胶量增大,力学强度和甲醛的释放量增加,吸水厚度膨胀率减小;热压压力增加,内结合强度降低,静曲强度、弹性模量以及吸水厚度膨胀率几乎不变,热压压力由1.5 MPa增加到2.25 MPa时,内结合强度约降低了3%,热压压力由2.25 MPa增加到3 MPa时,内结合强度约降低了6%。     

UF/PDMI组合胶黏剂在刨花板生产中的应用

采用脲醛树脂(UF)/聚合异氰酸酯(PDMI)组合胶黏剂,以不同的组合配比在较低热压温度(160℃)条件下用高含水率(9.0%)杂木刨花制备刨花板,检测其静曲强度、内结合强度以及2h和24h吸水厚度膨胀率。结果表明:聚合异氰酸酯(PDMI)的引入,可以显著提高刨花板的物理力学性能和耐水性能;将刨花终含水率提高至9.0%可节约刨花干燥能耗达13.0%以上;与脲醛树脂胶黏剂(UF)相比,使用PDMI/UF配比为1∶9的(10.0wt%PDMI)组合胶黏剂可以提高刨花板静曲强度80%,提高内结合强度150%;在不添加防水剂的条件下,可以将板材的2h吸水厚度膨胀率由31.0%提高至21.0%。该研究可为刨花板节能环保生产提供新思路。     

制板工艺因子对硅酸钠/酚醛树脂玉米秸秆刨花板性能的影响

采用硅酸钠/酚醛树脂胶制备玉米秸秆刨花板,考察工艺因子对试板物理力学性能的影响。结果表明:随着施胶量增加、热压温度升高、热压时间延长,试板吸水厚度率逐渐减小,静曲强度、弹性模量和内结合强度呈先增大后减小的趋势。按照优化工艺:施胶量17%、热压温度180℃,热压时间20s/mm,制备试板的吸水厚度膨胀率和力学性能均满足GB/T4897-2015《刨花板》中干燥状态下使用的家具型刨花板的(P2型)的要求。     

制板工艺因子对硅酸钠/酚醛树脂玉米秸秆刨花板性能的影响

采用硅酸钠/酚醛树脂胶制备玉米秸秆刨花板,考察工艺因子对试板物理力学性能的影响。结果表明:随着施胶量增加、热压温度升高、热压时间延长,试板吸水厚度率逐渐减小,静曲强度、弹性模量和内结合强度呈先增大后减小的趋势。按照优化工艺:施胶量17%、热压温度180℃,热压时间20 s/mm,制备试板的吸水厚度膨胀率和力学性能均满足GB/T 4897-2015《刨花板》中干燥状态下使用的家具型刨花板的(P2型)的要求。     

竹丝模压刨花板的工艺优化研究

采用正交试验法对竹丝模压刨花板制造工艺与产品质量进行优化试验,探讨施胶量、热压温度、热压时间、板坯含水率工艺因素对竹丝模压刨花板物理力学性能的影响,并得到了较优的工艺参数.试验结果表明利用纤维状竹丝可以压制出高质量的竹丝模压刨花板.产品的主要物理力学性能为:密度0.8 g/cm3,弹性模量6 745.7 MPa,静曲强度54.39 MPa,内结合强度0.53 MPa,吸水厚度膨胀率11.3%.     

Blackening of sugi (Cryptomeria japonica D. Don) heartwood in relation to metal content and moisture content

Blackening in heartwood was investigated in relation to the metal contents and the moisture content in xylem of about 50-year-old seedling sugi (Cryptomeria japonica D. Don) planted in a steeply sloped stand in Okutama district (Itsukaichi Tokyo), where blackened heartwood is frequently found. The potassium, calcium, iron, and manganese contents were examined in the variously blackened heartwood and normal heartwood by an atomic absorption method. It was recognized that potassium increased relative to the degree of the blackening of heartwood, resulting in a significant correlation between them. This finding implies that an increase in potassium has an important role in the blackening of heartwood. Moisture content has a tendency to increase in the blackened heartwood, so it seems that the large accumulation of potassium is associated with the high moisture content in heartwood.This work was presented at the 43rd Annual Meeting of the Japan Wood Research Society at Morioka, August 1993     

不同方法对爬山虎中总黄酮含量测定的影响

采用索氏提取法和回流提取法对爬山虎中总黄酮含量进行了提取 ,并用分光光度法进行了测定。结果表明 :爬山虎茎、叶、果中均有黄酮类化合物的存在 ,其中叶总黄酮含量最高 ,果最低 ;同时发现 ,用回流提取法提取所得爬山虎中总黄酮含量较索氏提取法要高。     

利用微波法测量植物叶片含水量

根据植物自身特点,对几种检测植物含水量的方法进行比较。确定采用微波法检测植物叶片的含水量,并对其检测的基本理论和工作原理进行了论述,总结出测量叶片含水量的计算公式。该检测方法具有快速、分辨率高、无污染和操作安全简便等优点。     

陕西土壤有机质与全氮量的关系

分析表明,陕西省9类主要农林土壤有机质与全氮量呈极显著正相关,两者间的回归方程及换算系数均可用于由有机质含量来较准确地估测全氮量。     

干旱处理对侧柏和油松幼苗相对含水量和叶绿素含量变化的影响

以1年生的侧柏和油松幼苗为研究对象,采用盆栽的方式,利用干旱胁迫方式对幼苗的叶片相对含水量和叶绿素含量进行测定。结果表明,随着干旱程度的加剧,侧柏和油松幼苗的叶片相对含水量和叶绿素含量都呈下降趋势,两种树苗两个指标的测定结果都是以油松幼苗的下降最低,抗旱性最好。     

沙柳刨花板及低毒脲醛树脂胶研究

研究了沙柳材的地造，胶接特性和适用于沙柳刨花板的低毒脲醛树脂。通过试验分析了脲醛树脂胶中尿素与甲醛的摩尔比与树脂性能的关系；浓缩处理与树脂中游离甲醛含量的关系。最后研究了抄柳刨花扳的制板工艺、特点和技术改进措施、分析了施胶量与板材性能的关系。     

三个不同因子对滑菇产量的影响

研究了滑菇培养基中含水率、麦麸含量、石膏含量等3个因素对滑菇产量的影响。结果表明:当麦麸含量为17%,石膏含量为1%时,滑菇产量较高,这2个因素不同水平的平均产量差异显著,基质含水率各水平之间的差异不显著。当含水率在63%时,平均产量高于其它2个水平。通过正交试验得出的最佳麦麸含量为17%,石膏含量为1%,培养基中最佳含水率为63%。     

刚竹毒蛾危害对毛竹叶片糖和蛋白质含量的影响

在宜宾市长宁县毛竹林中有代表性的地段设置样地,抽取样株,按刚竹毒蛾危害程度的不同在东、西、东、北方向分别取样全部叶片,带回室内测定竹叶中糖及蛋白质含量。结果表明,不同受害程度毛竹叶片可溶性糖、总糖与蛋白质含量均有显著差异,未受害叶含量最高,重度受害叶含量最低。     

氮磷胁迫下云南松与旱冬瓜混栽幼苗的光合生理指标反应及变化

以盆栽试验为基础,按不同的比例混交栽植云南松与旱冬瓜,用氮、磷浓度不同的平衡营养液对幼苗进行处理并测定分析其叶片的叶绿素、可溶性蛋白、可溶性糖含量的变化。结果表明:对于旱冬瓜而言,与云南松幼苗混栽时,磷缺乏会降低幼苗叶绿素的含量,而缺氮则影响较小,并且混栽一定比例的云南松对其幼苗叶绿素含量影响不大;对云南松而言,混栽旱冬瓜则影响明显。苗期营养供应全面时,混栽云南松对旱冬瓜幼苗可溶性蛋白含量影响不大,而当氮磷缺乏或胁迫时将导致其可溶性蛋白含量增加;氮磷缺乏或胁迫和混栽旱冬瓜对云南松幼苗可溶性蛋白含量均具有明显的影响,同时二者还具有明显的交互影响。混栽云南松和氮磷缺乏对旱冬瓜苗期的可溶性糖的积累和运转影响不大;氮磷胁迫和混栽旱冬瓜对云南松幼苗叶片可溶性糖含量均影响较小,但二者的交互影响明显。