1三层实木复合地板的特点三层结构实木复合地板是指以实木拼板为面层、实木条为芯层、单板为底层制成的企口地板。该产品采用三层纵横交错结构,相邻层互相抑制,使地板各个方向性能接近,地板不易翘曲变形,能用于地热条件铺装。     

热塑性树脂胶合板板坯热压过程中影响温度变化的主要因素

以聚乙烯薄膜为胶黏剂、桉树单板为原料制作多层热塑性树脂胶合板,并对影响制作过程中板坯温度变化的主要因素进行研究,以便更好地控制产品质量,提高生产效率,减少能源消耗。研究结果表明:板坯含水率对热塑性树脂胶合板热压所需时间有显著影响,降低板坯的含水率,能明显缩短板坯热压至要求温度所需时间;当板坯含水率较高时,通过提高热压温度能明显缩短热塑性树脂胶合板的热压时间,当板坯含水率较低时,对热压时间的缩短则不如板坯含水率较高时明显;所使用的厚度0.08 mm以下的聚乙烯薄膜不会阻碍热量在板坯中的传递,对板坯温度的变化没有明显影响;板坯从热压机推移至冷压机的过程中,板坯与外部环境接触,表面温度会快速下降,如果下降过大会使板材表层的胶合强度明显降低,因此在确定热压温度参数时,应考虑板坯从热压机推移至冷压机过程中可能产生的温度损耗,才能保证板材的强度。     

单板复合强化木地板的研制

试制了"耐磨纸-意杨单板-HDF基材(12 mm厚)-平衡纸"4层结构强化木地板基材,研究了单板厚度(1.2,1.5,2.0 mm)、胶黏剂种类(聚氨酯,脲醛树脂)及涂布量(单面100,110,130,150,160 g/m2)对板材翘曲度、吸水厚度膨胀率、内结合强度及机加工性能的影响。结果表明:实木贴面复合木地板具备工艺技术可行性,产品的翘曲度随单板厚度和施胶量的提高而递增(最高可达约0.6%),采用聚氨酯胶黏剂时产品性能优于脲醛树脂胶合板材,但冷压周期偏长。推荐工艺条件为:单板1.2 mm,PU或UF胶黏剂均可,涂布量控制在100 g/m2左右。     

单板/HDF复合木地板的制造工艺与产品性能研究

单板/高密度纤维板(HDF)复合木地板结合了实木地板和浸渍纸层压木质地板的优点,是地板产业发展的新方向之一。文中以12mm厚HDF为基材、复合意杨单板,试制了"耐磨纸-单板-HDF基材-平衡纸"四层结构地板用复合板材。研究了不同单板厚度、胶黏剂种类(聚氨酯-PU,脲醛树脂-UF)及涂布量对板材翘曲度、吸水厚度膨胀率、内结合强度及机加工性能的影响。结果表明:1)单板与HDF复合制造木地板是可行的;2)复合木地板的翘曲度随单板厚度和施胶量的提高而递增,最高可达约0.6%;3)贴面采用聚氨酯胶黏剂,产品性能优于脲醛树脂胶合板材,但冷压周期偏长。推荐工艺条件为:单板1.2mm,PU或UF胶黏剂均可,涂布量控制在100g/m~2左右。     

轻质稻秸保温材料高频热压板坯内部温度的研究

研究了高频电场中板坯厚度方向温度分布规律以及制板工艺因素(包括原料含水率、板材厚度和板材密度)对轻质稻秸保温材料板坯内部温度的影响,试验采用荧光光纤温度测定仪自动准确测定高频热压时板坯内部温度。结果表明:板坯升温过程分为快速升温、水分排出、慢速升温三个阶段,板坯内部温度在厚度上存在差异.温度分布总体表现为芯层高表层低。与常规热压相比,高频热压大大缩短了热压时间,且板坯厚度方向温度均匀性大大优于常规热压。在快速升温阶段,在一定范围内提高含水率能加快板坯的升温速度;在水分排出阶段,通过减小原料含水率能缩短水分汽化时间;原料含水率对慢速升温阶段基本没有影响。在整个升温阶段,板材密度越低,其升温速度越快;在水分排出阶段。板材密度越低,水分汽化时间越短。板材厚度的影响作用与板材密度类似。     

竹木层积塑化板的研制

以竹席、杨木单板、底层纸和水溶性酚醛树脂胶为原料,将竹席先行水煮、然后进行干燥、浸胶并再干燥,杨木单板进行两次双面涂胶,底层纸则通过浸胶、干燥成胶膜纸,然后组合成以竹帘为芯层,杨木单板为内层,胶膜纸为表层的板坯,采用“冷-热-冷”胶合工艺,压制成强度高,吸水厚度膨胀率小的竹木层积塑化板。     

薄型单板层积材结构改进的研究

薄型单板层积材(LVL)可替代锯材,应用于木质门窗构件等轻载结构领域.由于单板全部顺纹组坯,导致产品存在横向翘曲变形的技术问题.为此,尝试采用"部分单板横纹组坯"和"纤维板与单板复合"两种方法进行改进,制造了15 mm厚LVL,包含1～2层单板横纹组坯或1～2层3 mm纤维板.测试结果表明:单板横纹组坯.显著降低了LVL的抗弯性能,但LVL的弹性模量仍能达到单板层积材国家标准中70E级别的要求,而静曲强度甚至超过180E级别优等品的限值;与此同时,改进结构的LVL吸水翘曲变形显著降低.横纹单板越靠近LvL表层,板子抗弯性能降低越显著,而翘曲变形改善越明显.采用纤维板与单板复合制造LVL,纤维板的内结合强度衰减明显,易受破坏.     

C型木质薄壁结构材的轴压性能

【目的】利用杨木单板制备C型木质薄壁结构材,研究其轴压性能及屈曲变形模式,为新型木质结构材在建筑工程领域的应用提供理论基础。【方法】借鉴冷弯薄壁型钢的截面形式,探讨组坯结构、玻璃纤维布(GFC)、卷边和厚度等因子对C型木质薄壁结构材短柱轴压性能的影响。【结果】顺纹单板组坯结构、表层横纹芯层顺纹单板组坯结构和顺纹横纹交错单板组坯结构的平均极限载荷分别为12.5、14.6和12.97 kN。GFC-杨木单板复合C型木质薄壁结构材试件截面的有效性整体较大,在46.46%~50.21%之间;表层GFC芯层顺纹单板组坯结构与表层横纹芯层顺纹单板组坯结构试件相比,用GFC代替横纹弯曲单板,平均截面面积减少26.90%,质量减少5.17%,而极限载荷提高8.63%。外转角表面贴GFC芯层顺纹单板组坯结构与表层GFC芯层顺纹单板组坯结构相比,极限载荷降低34.17%,且局部屈曲半波发生在翼缘和腹板的中间位置。表层GFC芯层顺纹单板组坯结构、表层GFC芯层顺纹单板组坯卷边宽度25 mm结构和表层GFC芯层顺纹单板组坯卷边宽度50 mm结构,对应实际极限承载力分别为15.86、16.76和18.98 kN。表层GFC芯层顺纹单板组坯卷边宽度50 mm结构与表层GFC芯层加厚顺纹单板组坯卷边宽度50 mm结构相比,芯层杨木单板组坯厚度增加从而截面面积增大52.96%,平均每米质量增加33.33%,极限载荷提高90.31%。【结论】 C型木质薄壁结构材相同层数组坯时,表层横纹芯层顺纹单板组坯结构较顺纹单板组坯结构和顺纹横纹交错单板组坯结构合理,轴向承载性能好;用GFC代替横纹弯曲单板,可增强C型木质薄壁结构材轴向承载性能,表现出塑性破坏模式;仅对C型木质薄壁结构材外转角处表层局部粘贴GFC,不能提高无卷边的C型木质薄壁结构材的轴向承载性能。卷边对C型木质薄壁结构材轴向承载性能有强化作用,在0~50 mm卷边宽度范围内,试件轴向承载性能随卷边尺寸增大而增大。C型木质薄壁结构材芯层顺纹单板总厚度增加,C型材试件轴向承载能力也随着提高。     

单板在结构刨花板中的应用

本研究的目的是,探讨是否可以用单板做芯层,以提高结构刨花板的尺寸稳定性。作者意图验证三层结构刨花板中,单板芯层垂直于定向排列的刨花面层,是否能有效地提高板子的尺寸稳定性以及是否能限制定向刨花表层的横向膨胀。     

基材和压贴工艺对浸渍胶膜纸饰面细木工板柜门翘曲度的影响北大核心

针对浸渍胶膜纸饰面细木工板制作的定制衣柜柜门变形率高的问题,探究细木工板基材结构、压贴工艺和厚度对浸渍胶膜纸饰面细木工板定制衣柜柜门翘曲度的影响。结果表明:炭化和异型结构细木工板基材能够有效降低定制衣柜柜门的翘曲度;相较于覆贴和直贴重组装饰单板,覆贴1.0 mm高密度纤维板(HDF)的压贴工艺更有利于降低柜门的翘曲度;定制衣柜柜门厚度的增加同样也可以降低柜门的翘曲度。     

Productive test of a newly drying technology of veneer： intermittent-contact drying of veneer with flexible screen belt

A newly drying technology, intermittent-contact drying of veneer with flexible screen belt (ICD-fbs), was invented and used in poplar veneer drying. Productive test was carried out for validating the practical use of this drying method. The test result shows that to dispose flexible screen belts on the two sides of hot board could help steam discharge remarkably. The veneer dried using ICD-fsb method had smooth and level surface, less deformation and warping, even moisture content, and high utilization rate. The time for opening hot board to discharge steam,which, early or late, is a key to obtain good drying result, was determined at the time when the core‘s temperature of veneer reaches 100℃ (vaporization). Using ICD-fsb method, the shrinking rates in tangent of veneer were from 1.90% to 2.26% for veneer of 0.4 mm in thickness,2.49% to 4.50% for veneer of 1 mm in thickness and 1.34% to 3.30% for veneer of 1.7 mm in thickness, which are much lower than the results obtained by other drying methods. The method of ICD-fsb offers a reliable technological guarantee for solving the deformation problem of veneer drying, especially the deformation of wood from quick-growing plantation.     

杨木单板的湿热处理对单板层积材性能的影响

杨木单板的湿热处理规律以及对杨木单板层积材性能影响的研究结果表明,单板湿热处理后产生了塑化,形成了一部分不可恢复的变形,密度平均增加了38.7%;对抗拉强度的影响不显著;对单板压缩率和膨胀率有着特别显著的影响,单板平均压缩了27.8%,经24h水浸泡,单板恢复膨胀仅18.7%.单板湿热处理后经过低压压制,可以得到与高压压制相同密度的板材,且板材的断面密度差异小,水平剪切强度提高了27.1%,静曲强度增加了17.8%,弹性模量没有显著变化,吸水厚度膨胀率降低了约10个百分点.     

辊压连续式单板干燥机的设计

单板干燥机是单板及胶合板生产过程中的主要设备之一,单板干燥质量直接影响贴面板、胶合板产品质量。辊压连续式单板干燥机的设计,主要是利用国际上最新的加压接触式单板干燥技术,其主要工作原理是:单板在上下两条钢带的夹持下经过预热管的预热使钢带和单板温度趋于一致,而后进入干燥滚筒之间进行快速干燥。由于钢带与滚筒之间具有一定的压力,使单板在被夹持的状态下进行连续干燥,因此可以使干燥后的单板平整、含水率均匀,干燥质量和干燥效率得到很大提高;并且具有高温滚筒与湿单板直接接触传热,热效率高,热损失小,大大减少热能损耗的特点。     

Gas permeability of fiberboard mats as a function of density and fiber size

ABSTRACT

Gas permeability and structure of fiberboard mats are essential properties because of their impact on mat internal gas pressure, moisture content and temperature evolution during the hot-pressing process. The objectives of this work were to determine the effect of fiber size and mat density on the intrinsic gas permeability of the mat. For the study of these mat properties, panels with a homogeneous density profile through the thickness were manufactured at five density levels (200, 400, 600, 800 and 1000?kg m^?3) for three different fiber sizes. Fiber refining was performed in a disk refiner at three plate spacings. Gas permeability was measured with an in-house built apparatus. The results showed that the fiber sizes studied had no significant effect on the intrinsic permeability. This was likely due to a more significant impact of the internal porous structure of the mat compared to fiber size. Besides, the intrinsic permeability decreased significantly when the panel density increased from 198 to 810?kg m^?3. This suggests that the decrease of the intrinsic gas permeability during the last seconds of press closure plays an essential role in the bulk moisture mass transfer through the fiberboard mat.     

刨切薄竹贴面中密度纤维板工艺研究

对刨切薄竹贴面中密度纤维板(MDF)的工艺进行了研究,结果表明:在MDF的上下表面直接粘贴刨切薄竹的工艺可行,并根据试验结果确定了较优的贴面工艺参数.测试结果还显示,刨切薄竹背衬无纺布后再与MDF胶合,其表面胶合强度比刨切薄竹直接贴面MDF时低.     

三层实木复合地板背板含水率对其变形的影响

采用单因素试验法，探讨了三层结构实木复合地板背板的含水率对地板长度方向变形的影响。结果表明：背板含水率对地板的变形有明显影响，含水率过低或过高时复合地板的变形都较大；背板含水率可依据背板密度的大小而调整，但一般不得高于12％；背板一般使用针叶树材．允许使用软阉叶树材，但含水率的控制相对需严格。含水率控制适当是解决复合地板变形的重要方法之一。     

纳米TiO2改性薄竹的工艺试验

研究了纳米TiO2改性薄竹机理与工艺,分析薄竹切面、薄竹厚度、浸渍压力与浸渍时间等工艺因素对薄竹附载TiO2效果的影响,并运用X射线光电子能谱与环境扫描电镜技术手段,分析了薄竹改性处理前后的表面元素组成、元素变化、TiO2分布效果。试验结果表明:浸渍时间90 min、浸渍压力0.10 MPa、薄竹厚度0.3 mm、径切面纹理的薄竹、纳米TiO2溶液浓度0.5 g/L、浴比1∶10～20、常温浸渍纳米TiO2溶液改性薄竹工艺是可行的,TiO2附载率约为1.3%。     

旋切过程中单板厚度变化的理论研究

从理论上探讨了旋切过程中单板厚度的变化规律。结果表明：单板厚度总是小于或等于单板名义厚度，其变化与装刀高度，名义厚度及木段瞬时半径有关。