Effects of mat moisture content and press closing speed on the formation of density profile and properties of particleboard

Isocyanate resin-bonded 0.5 and 0.7 g/cm³ lauan (Shorea sp.) particleboards were produced from mats with uniform and distributed moisture content (MC) distributions, using three hot press closing speeds. The effects of these processing variables on the formation of density profile in particleboard and board properties were analyzed statistically. A definition of the density profile was introduced, and the correlations among the various defining factors were established. The results are summarized as follows. (1) The peak density (PD) of particleboard could be increased, with a slight reduction in the core density (CD), using mats with different MC distributions. (2) In a conventional density profile, CD and PD are highly dependent on the board mean density (MD); and the gradient factor (GF), peak distance from the faces (Pdi), and peak base (Pb) are significantly correlated to each other, at the 99% significance level. (3) Greater press closing speed reduces Pdi and Pb, with an increase in GF. (4) Greater press closing speed could increase the PD in board of low MD, with minimal effect on CD. (5) The modulus of elasticity (MOE) of particleboards from mats with high MC near the faces were consistently higher than those from mats with uniform MC, irrespective of the press closing speed, whereas their modulus of rupture (MOR) became indifferent at higher MD under slow and fast closing speeds. (6) Sanding does not improve the MOR and MOE of particleboard significantly.     

Formation of the density profile and its effects on the properties of fiberboard

Two main types of fiberboards were produced using lauan (Shorea spp.) fibers with an isocyanate resin as the binder; fiberboard with a flat, homogeneous (homoprofile), and typical U-shaped (conventional) density profile along the board thickness. The processing parameters included manipulation of mat moisture content distribution, press closing speed, and hot pressing method. The results are summarized as follows: (1) A larger variation was observed in the peak density (PD) and core density (CD) of fiberboards at 0.5g/cm³ mean density (MD) level than in those at 0.7 g/cm³. Generally, PD showed a greater variation than CD, irrespective of MD level. (2) Boards produced using two-step hot pressing recorded substantially higher PD with reduced CD. (3) Multiple regression analysis showed that CD and PD could be calculated based on the other profile defining factors, and a rough estimation for peak distance and gradient factor was possible. (4) Based on static bending, conventional fiberboard had a higher modulus of rupture (MOR) than the homo-profile board but a similar modulus of elasticity (MOE). (5) At 0.5 g/cm³ the MOR and dynamic MOE of fiberboard increased by up to 67% and 62%, respectively, when the PD increased from 0.5 to 1.07 g/cm³. Similarly, an increase of PD from 0.7 to 1.1 g/cm³ resulted in corresponding increases of 55% and 34% in the MOR and dynamic MOE of 0.7 g/cm³ boards. (6) The internal bond strength and screw withdrawal resistance were almost entirely dependent on the CD and MD, respectively. (7) Homo-profile fiberboards registered higher thickness swelling and water absorption than conventional fiberboards throughout the dry/wet conditioning cycle.     

Durability characteristics of cement-bonded particleboards manufactured from maize stalk residue

Cement-bonded particleboards of 6 mm in thickness were manufactured using maize stalk (Zea mays) particles of uniform sizes at three levels of board density and additive concentrations respectively. The bending strength and dimensional properties were assessed. Increase in board density and additive concentration caused increase in Modulus of rupture (MOR), Modulus of elasticity (MOE), and decrease in Thickness swelling (TS) and Water absorption (WA). The MOR, MOE and TS of the boards were significantly affected by board density except for WA, but additive concentration affected all the boards’ properties examined at p ≥ 0.05. Strong and dimensional stable cement-bonded boards could be manufactured from maize stalk particles with Portland cement as the binder after hot water treatment. Although the dimensional stability and mechanical strength properties of the boards were affected by the board density and additive concentration, the study revealed that cement-bonded particleboards could be manufactured from maize stalk (Zea mays) particles. However, the increase in board density and additive concentration could cause the increase in MOR and MOE, and cause the decrease in TS and WA of boards.     

Characterization of bagasse binderless particleboard manufactured in high-temperature range

This paper describes the features of binderless particleboard manufactured from sugarcane bagasse, under a high pressing temperature of 200–280 °C. Mechanical properties [i.e., modulus of rupture (MOR) and elasticity (MOE) in dry and wet conditions, internal bonding strength (IB)] and dimensional stability [i.e., thickness swelling (TS)] of the board were evaluated to investigate the effect of high pressing temperature. Recycled chip binderless particleboards were manufactured under the same conditions for comparison, and particleboards bonded with polymeric methylene diphenyl diisocyanate (PMDI) resin were manufactured as reference material. The target density was 0.8 g/cm³ for all of the boards. The results showed that the mechanical properties and dimensional stability of both types of binderless boards were improved by increasing the pressing temperature. Bagasse showed better performance than that of recycled chip as a raw material in all evaluations. Bagasse binderless particleboard manufactured at 260 °C had an MOE value of 3.5 GPa, which was equivalent to the PMDI particleboard, and a lower TS value of 3.7 % than that of PMDI particleboard. The MOR retention ratio under the dry and wet conditions was 87.0 %, while the ratio for the PMDI particleboard was only 54.6 %. The obtained results showed the possibility of manufacturing high-durability binderless particleboard, with good dimensional stability and water resistance, which previously were points of weakness for binderless boards. Manufacturing binderless boards under high temperature was effective even when using particles with poor contact area, and it was possible to express acceptable properties to allow the manufacture of particleboards. Further chemical analysis indicated a contribution of a saccharide in the bagasse to the improvement of the board properties.     

Bond durability of kenaf core binderless boards II: outdoor exposure test

An outdoor exposure test was conducted on kenaf core binderless boards (pressing temperatures 200°, 180°, and 160°C; pressing pressure 3.0 MPa, time 10 min, target board thickness 5 mm, target board density 0.8 g/cm³) to estimate their bond durability. Modulus of rupture (MOR), modulus of elasticity (MOE), internal bonding strength (IB), thickness change, weight loss, Fourier transform infrared (FTIR) spectra, and color difference (ΔE*) by the CIE L^*a^*b^* system were measured at various outdoor exposure periods up to 19 months. These values were then compared with those of a commercial medium-density fiberboard (MDF; melamine-urea-formaldehyde resin; thickness 9.0 mm, density 0.75 g/cm³). Generally, dimensional stability and the retention ratios of MOR, MOE, and IB after the outdoor exposure test increased with increased pressing temperature of binderless boards. The MOR retention ratio of the kenaf core binderless boards with a pressing temperature of 200°C was 59.5% after 12 months of outdoor exposure, which was slightly lower than that of the MDF (75.6% after 11 months of outdoor exposure). Despite this, the bond durability of the kenaf core binderless boards should be viewed as favorable, especially when considering the fact that the retention ratio of 59.5% was achieved without binder and without obvious element loss. Part of this report was presented at the International Symposium on Wood Science and Technology, IAWPS2005, November 27-30, 2005, Yokohama, Japan     

Water resistance properties of kenaf core binderless boards

Abstract Binderless boards were prepared from kenaf core under various manufacturing conditions and their water resistance properties were evaluated. The board properties evaluated were retention ratios of modulus of rupture (MOR) and modulus of elasticity (MOE), internal bonding strength after water treatment (IB), thickness swelling (TS), water absorption (WA), and linear expansion (LE). These values were then compared with those of boards bonded with urea-formaldehyde (UF), urea melamine formaldehyde (UMF), and phenol-formaldehyde (PF) resins, and their water resistance properties were assessed. We found that pressing temperature was one of the most important conditions for the improvement of water resistance properties. The retention ratios of MOR, MOE, and IB of kenaf core chip binderless boards (pressing temperature 200°C, target density 0.8g/cm³, and the three-step pressing of 6MPa for 10min, then 4MPa for 3min, and 2MPa for 3min) were 37.1%, 49.9%, and 55.7%, respectively, compared with values for UMF-bonded boards of 22.5%, 27.1%, and 40.7%, and values for PF-bonded boards of 42.8%, 41.8%, and 54.1%, respectively. The results showed that the water resistance properties of binderless boards were higher than those of UMF-bonded boards and almost as high as those of PF-bonded boards. Part of this article was presented at the 53rd Annual Meeting of the Japan Wood Research Society, Fukuoka, March 2003     

Manufacture of oriented board using mild steam treatment of plant fiber bundles

This study investigated the effects of mild steam treatment (0.1 MPa for 2 h) of natural bio-based fibers and orientation (0° and 90°) of those fibers in various fiberboards. Ramie bast, pineapple leaf, and sansevieria fiber bundles were used as materials. The composite fiberboards were prepared using phenol-formaldehyde (PF) resin. To investigate the effect of mild steam treatment on wettability, contact angles of PF resin to the fiber were measured. The mechanical properties of the boards were examined as well as their dimensional stability. The contact angle data showed that mild steam treatment was effective in improving the wettability of fibers. Unioriented steam-treated boards showed better performance of internal bond (IB), moduli of rupture (MOR) and elasticity (MOE), thickness swelling (TS), and water absorption (WA) than other boards. Unioriented steam-treated sansevieria board with longitudinal fiber direction showed higher average values of MOR (403 MPa), MOE (39.2 GPa), and IB (1.33 MPa) and lower values of TS (5.15%) and WA (8.68%) than other boards. The differences in the mechanical properties and dimensional stability of boards were found mainly due to the differences in the ratios of fiber fraction of the boards to the density of the fiber bundles.     

广宁县竹香骨下脚料制备竹碎料刨花板及其复合改性研究

采用竹香骨下脚料为原料,以脲醛树脂和三聚氰胺改性脲醛树脂胶粘剂制备竹碎料刨花板,并与木纤维复合改性,检测并分析了内结合强度、静曲强度、弹性模量和吸水性。结果表明,在热压温度为160℃时,竹碎料板和竹木复合碎料板的物理力学性能均满足国标规定在干燥状态下使用的普通用板要求。当木纤维与竹碎料复合后,复合板材的静曲强度和弹性模量有一定程度提高,但内结合强度降低。     

Development of binderless particleboard from kenaf core using steam-injection pressing

Binderless particleboards were successfully developed from kenaf core using the steam-injection press. The effects of board density, steam pressure, and treatment time on the properties of the board were evaluated. The target board densities were relatively low, ranging from 0.40 to 0.70g/cm³. The properties [i.e., moduli of rupture (MOR) and elasticity (MOE) in both dry and wet conditions, internal bonding strength (IB), and water absorption (WA)] of the boards increased linearly with increasing board density. Steam pressure and treatment time also affected the board properties. The bending strength and IB were improved with increased steam pressure. A long steam treatment time contributed to low thickness swelling (TS) values and thus better dimensional stability. The appropriate steam pressure was 1.0MPa, and the treatment time was 10–15min. The properties for 0.55g/cm³ density boards under optimum conditions were MOR 12.6MPa, MOE 2.5GPa, IB 0.49MPa, TS 7.5%, and wet MOR 2.4MPa. Compared with the requirement of JIS 5908, 1994 for particleboard, kenaf binderless boards showed excellent IB strength but relatively poor durability.Part of this report was presented at the 19th Annual Meeting of the Japan Wood Technological Association, Tokyo, October 2001     

蔗髓含量对蔗渣碎料板性能的影响研究

研究了蔗髓含量（质量分数）分别在10%、20%、30%、40%4种不同情况下蔗渣碎料板的密度、静曲强度、弹性模量、内结合强度、吸水厚度膨胀率和板面握钉力等物理力学性能的变化规律.结果发现，随蔗髓含量的增加，板材的密度增加，弹性模量和板面握钉力下降；在蔗髓含量低于20%以下时，蔗髓的存在对板材的静曲强度无明显影响，而随蔗髓含量增加，吸水厚度膨胀率影响显著上升；在蔗髓含量高于20%以上时，蔗髓的含量增加使板材静曲强度明显下降，而对吸水厚度膨胀率无影响；蔗髓的含量对板材的内结合强度影响不明显.     

毛竹无胶粘剂蒸爆板的制造和特性研究

研究了22、26、33 kg/cm2爆破压力,5 min蒸煮时间对毛竹无胶粘剂蒸爆板的制造和特性的影响,结果表明,无胶板的静曲强度、弹性模量和内结合强度与板材密度普遍呈紧密的线性正相关。爆破压力26 kg/m2、蒸煮时间5 min的蒸爆条件有利于产生高强度的弹性和内结合力。无胶板密度超过1.1 g/cm3时,24 h浸泡处理水分吸收率不超过30%,几乎所有压制成的无胶板的24 h浸泡处理厚度膨胀率不超过10%。     

Effect of flake geometry on properties of cement-bonded particleboard from mixed tropical hardwoods

Summary Laboratory scale cement-bonded particleboards were made from mixed particles of three tropical hardwoods. Boards were three-layered comprising of 2 mm thick sawdust face and 4 mm thick core layers made from flakes of three lengths-12.5 mm, 25.0 mm and 37.5 mm and two thicknesses of 0.25 mm and 0.50 mm. The panels were fabricated at three density levels of 1,050 kg/m³, 1,125 kg/m³ and 1,200 kg/m³. From the statistical factorial analysis carried out, flake length, flake thickness and board density had significant effects at 1% level of propability on the properties of the tested panels. Mean MOR ranged from 5.22 to 11.15 N/mm²; MOE-2,420 to 4,820 N/mm²; water absorption and thickness swelling following 144 hours soak in water, 32.95 to 46.00% and 0.35 to 5.47% respectively. The longer and thinner the flakes, the stronger, stiffer and more dimensionally stable the experimental cement-bonded particleboards. Similarly, the higher density panels generally exhibited higher strength values in terms of MOR and MOE and were more dimensionally stable. MOR, MOE, water absorption and thickness swelling were found to be highly correlated with flake length, flake thickness and panel density. Correlation coefficients (R) for these relationships were 0.888 to 0.986 for the combined variables; and 0.574 to 0.992 for the individual factors. In all the cases tested, the regression relationships were linear.     

Preparation of composite board using foil-laminated and plastic-laminated liquid packaging paperboard as raw materials

We investigated the properties of composite board formed using base sheets of aluminum foil-laminated and polyethylene (PE) plastic-laminated liquid packaging paperboard (LP) as an alternative to recycling these items in wastepaper stream. Boards of different specific gravities ranging from 0.55 to 0.75 were made by pressing shredded LP blended with urea resin having resin content of 6%–10% at 180°C. Subsequently, we also prepared mixed particleboard [wood (WD) particles and LP mixed], three-layered particleboard (LP as the middle layer, WD in the upper and lower layers), and wood particleboard all having resin content of 10% and various specific gravities. Static bending and internal bonding strengths and thickness swelling of the specimens were determined to examine their properties. At the same specific gravity, the properties of LP particleboards were affected by their resin content. The modulus of rupture (MOR), modulus of elasticity (MOE), and internal bond strength of the LP particleboards increased with increasing specific gravity of the boards at the same resin content, but thickness swelling of the LP particleboards showed the reverse trend. The average MOR of the LP particleboards approximated that of the mixed particleboards and was greater than those of the three-layered particleboards and wood particleboards. Internal bond strength and thickness swelling of the LP particleboards were smaller than those of the other particleboards. Based on the above observations, we deemed that LP can be made into composite boards with adequate properties either alone or mixed with wood particles.     

利用杨树人工林剩余物生产刨花板可行性研究

The composite board industry in Iran is obliged to use residues from forest operation as well as wood industry for competing with paper industry because of shortage of wood. In the present study we investigated the residues from poplar plantation used for particleboard production. Three kinds of wood materials, poplar branches, small diameter poplar wood (3–8 cm) and beech wood, were used in the experiment of particleboard production. The results demonstrated that the characteristic of particleboard made from poplar branches and small diameter wood is comparable to that made from mature beech wood. To avoid too much residual acid in the final board, the properties of boards produced with 1.5% hardener at 175°C press temperature are acceptable, although the properties of particleboard produced with 2% hardener were higher than were higher than that of the board produced with lower hardener (1% or 1.5%).. The MOR, MOE and IB of particleboard made from branches were measured as 14.57, 2015, and 1.32 MPa, respectively, while The MOR, MOE and IB of particleboard produced from small diameter poplar wood were 19.90, 2199, and 1.86 MPa, respectively. The thickness swelling of boards made from branches after 2 and 24 h immersion in water was 20.14% and 31.26%. The utilization of branches and very small diameter wood of poplar is recommended for the survival and developments of particleboard industry in Iran.     

锯屑掺入量对快速固化水泥刨花板性能的影响

就不同的细料(锯屑)掺入量对快速固化水泥刨花板的性能的影响作了探讨,结果表明:锯屑的掺入对水泥刨花板的密度、静曲强度、内结合强度和厚度膨胀率均有一定的影响,当锯屑的掺入量占木质原料总量的20% ～ 30%时,既可以改善板的性能,又可以提高木质原料的利用率.     

半干法石膏纤维板工艺研究：Ⅰ.原料配比,密度等对板材性能的影响

本研究是建立在我国资源和工业技术基础之上,探讨利用木纤维以半干法制造石膏纤维板（ＧＦＢ）的生产工艺;提出了半干法石膏纤维板的工艺方案,并建立了密度、木膏比、水膏比与板材性能的数学模型。结果表明：密度（Ｄ）增加,板材力学性能显著提高,木膏比（Ｗ／Ｇ）、水膏比（Ｈ／Ｇ）有效强的交互影响。木膏比增大,板材反弹率和吸水厚度膨胀率（ＴＳ）增加,纤维形态,蒸煮工艺对板材静曲性能无显著影响,纤维形态对内结合强度     

Properties of particleboard produced using a sealed press

In this study, different properties of experimental particleboard produced using a sealed press were determined and were compared with those for particleboard produced using a conventional press. Three types of binder, namely urea formaldehyde (UF), melamine formaldehyde (MUF), and polymethylene diphenyl diisocyanate (PMDI), were used for board production. For the UF-bonded boards produced using the sealed press, the modulus of rupture and the internal bond strength (IB) decreased due to the high temperature and steam pressure used in comparison to the conditions in a conventional press. However, MUF- and PMDI-bonded boards had improved IB and thickness swelling (TS). For the PMDI-bonded boards, especially, the TS was further improved and IB was increased by using a sealed press. PMDI is known to possess superior properties and was confirmed to achieve good properties when used as a binder for particleboards produced using a sealed press.     

Properties of kenaf core binderless particleboard reinforced with kenaf bast fiber-woven sheets

Kenaf composite panels were developed using kenaf bast fiber-woven sheets as top and bottom surfaces, and kenaf core particles as core material. During board manufacture, no binder was added to the core particles, while methylene diphenyldiisocyanate resin was sprayed to the kenaf bast fiber-woven sheet at 50 g/m² on a solids basis. The kenaf composite panels were made using a one-step steam-injection pressing method and a two-step pressing method (the particleboard is steam pressed first, followed by overlaying). Apart from the slightly higher thickness swelling (TS) values for the two-step panels when compared with the one-step panels, there was little difference in board properties between the two composite panel types. However, the two-step pressing operation is recommended when making high-density composite panels (>0.45 g/cm³) to avoid delamination. Compared with single-layer binderless particleboard, the bending strengths in dry and wet conditions, and the dimensional stability in the plane direction of composite panels were improved, especially at low densities. The kenaf composite panel recorded an internal bond strength (IB) value that was slightly low because of the decrease of core region density. The kenaf composite panel with a density of 0.45 g/cm³ (one-step) gave the mechanical properties of: dry modulus of rupture (MOR) 14.5 MPa, dry modulus of elasticity (MOE) 2.1 GPa, wet MOR 2.8 MPa, IB 0.27 MPa, TS 13.9%, and linear expansion 0.23%.     

喷蒸热压法棉秆无胶碎料板的研制

以棉秆为原料,采用喷蒸热压法研制无胶碎料板,探讨板的密度、蒸汽压力及喷蒸时间对棉秆无胶碎料板的物理力学性能的影响.结果表明:在试验范围内,随着板密度增大,无胶碎料板的静曲强度、弹性模量与内结合强度明显提高;提高蒸汽压力及延长喷蒸时间,能明显降低无胶碎料板的吸水厚度膨胀率.     

半干法石膏纤维板工艺研究：Ⅱ.搅拌和铺装均匀性因素分析

石膏和纤维的搅拌和铺装的均匀性对石膏纤维板质量影响很大。试验表明，所采用的搅拌机和铺装机性能良好，搅拌和铺装质量较好，铺装机料仓中料高影响板坯密度的均匀性，料高与板坯密度呈很强的一元线性关系；板密度与ＭＯＲ、ＭＯＥ有较好的一元线性关系，但与ＩＢ线性关系相对较差，板密度增加，ＭＯＲ、ＭＯＥ和ＩＢ也增加。