Dynamic Mechanical Properties of Wood Powder /Polypropylene Composites

The dynamic mechanical properties of wood powder/polypropylene composites with different wood content treated and untreated with the compatibilizer have been studied. It has been found that addition of wood powders and the compatibilizer can both improve the viscoelasticity of composites. Glass transition temperature (Tg) of appropriate wood powder-filled composites decreased. The value for the storage modulus (G') increased gradually with increasing wood powder content. The addition of the compatibilizer made glass transition temperature shift to a higher temperature. DSC (Differential Scanning Calorimetry) results showed that, for pure PP, the addition of the compatibilizer decreased its melting point, and increased its Calorie of Melt at the same time. For the composite with 50 % wood powder treated with the compatibilizer, the melting point was almost unchanged, but its Calorie of Melt decreased.     

MAPP改性木粉/聚丙烯复合材料的物理力学性能

木塑复合材料的界面相容性是决定其性能的关键因素,通过添加偶联剂的方法能够改善其界面相容性,从而提高其性能。通过测定毛白杨木粉/聚丙烯复合材料的物理力学性能来研究木粉含量和偶联剂添加量对木塑复合材料物理力学性能的影响,为进一步研究木塑复合材料的界面相容性提供理论依据。研究结果表明:随着木粉含量的增加,复合材料的物理力学性能下降,并且在高木粉含量阶段影响显著;高木粉含量复合材料的性能较差,添加MAPP能显著改善其物理力学性能。     

木粉加入量对木／塑复合材料性能影响的研究

研究了聚丙烯与木粉以不同比率复合而成的材料的物理力学性能和复合形态特征。结果表明：不同混合比率的聚丙烯与木粉进行复合后所得的复合材料，除冲击强度有所降低外，其它力学性能均比纯聚丙烯的有较大幅度的提高。木粉表面的酯化处理可以改善木塑界面之间的相容性和复合材料的均匀性。在木塑复合过程中木塑之间发生镶嵌现象使木塑之间产生物理结合。     

EPDM-MA对木粉/聚丙烯复合材料性能的影响

采用特定设计的双螺杆和单螺杆串联挤出机组,以挤出的方式制备木粉/聚丙烯复合材料。主要采用静态力学试验、动态力学热分析(DMTA)和扫描电子显微镜(SEM)观察等方法,研究了马来酸酐改性的三元乙丙橡胶(EPDM_MA)对木粉/聚丙烯复合材料的静态力学性能、动态力学性能和吸水性能的影响。静态力学性能试验结果表明:添加适量的EPDM_MA有利于提高木粉/聚丙烯复合材料的拉伸和弯曲强度,冲击强度的提高最为显著,但EPDM_MA的添加对复合材料的模量有不利影响。动态力学性能分析结果表明:复合材料的储能模量(E′)和损耗因子(tanδ)的峰值均随EPDM_MA加入量的增加而降低,后者说明EPDM_MA改善了木粉与聚丙烯的界面结合;EPDM_MA的加入,使得复合材料的主转变温度略向高温方向移动,并且在-50℃左右的低温区出现了次级转变峰,表明EPDM_MA对复合材料的热性能产生影响,尤其有利于改善其耐低温冲击性能。SEM研究结果表明:EPDM_MA的添加不仅提高了木粉和聚丙烯的界面结合,并且以直径约为0·1~1μm的球状粒子形态分散于聚丙烯中,能够通过自身的塑性变形而提高复合材料的抗冲击性能。EPDM_MA的添加,有效降低了复合材料的吸水性。     

聚丙烯比例对木塑复合材料性能的影响

通过正交试验,以木材纤维和废旧聚丙烯塑料为原料,异氰酸酯或马来酸酐作偶联剂,压制木材纤维/聚丙烯复合材料,研究聚丙烯(简称PP)用量对木塑复合材料性能的影响。结果表明,聚丙烯比例对复合材料的内结合强度、吸水厚度膨胀率、静曲强度和弹性模量有不同的影响。在热压时间、热压温度、复合材料密度相同的条件下,用异氰酸酯(简称MDI)作偶联剂,聚丙烯用量40%时复合材料的性能最佳;而用马来酸酐(简称MA)作偶联剂,聚丙烯用量50%时复合材料的性能最佳。     

HDPE含量对木塑复合材料力学性能的影响

通过改变高密度聚乙烯(HDPE)和聚苯乙烯(PS)的混合比例,设计了7种制作木塑复合材料的方案,HDPE∶PS分别为0∶10、1∶9、2∶8、3∶7、4∶6、5∶5、10∶0。按照不同设计方案,选用相应的挤出工艺参数制作木塑复合材料型材,按照塑料检测标准对其进行力学性能检测以及扫描电镜观察,找出最优的配方工艺。     

木/麻/PP纤维含量对复合材料性能的影响

采用无纺织气流成型织坯再热压的工艺,研究汽车内饰用木/麻/PP纤维三元复合材料中,3种纤维含量对复合材料性能的影响.研究结果表明,增加PP纤维含量,可以提高复合材料的静曲强度和耐水性;麻纤维含量增加对提高材料的强度影响显著,但耐水性略有下降.当PP纤维含量为40%、麻纤维为30%、木纤维30%时,复合材料的性能较佳.     

乙酰化木粉基复合材料的疏水与流变性能研究

通过双螺杆挤出、注塑方法制备了木粉(WF)、乙酰化木粉(AWF)与低密度聚乙烯(LDPE)、聚乳酸(PLA)的共混材料。采用吸水率测定、接触角测量、旋转流变仪、拉伸测试和扫描电镜(SEM)分别表征了共混材料的疏水、流变性能、力学性能和微观形貌结构。结果表明:由AWF制备的共混材料相比同质量比例的由WF制备的共混材料具有更好的疏水性能,吸水率发生了大幅度降低。随着材料中AWF含量的减少,共混材料的吸水率逐渐降低,接触角逐渐增大。流变测试表明AWF/LDPE共混材料在黏度和储能模量方面都低于WF/LDPE共混材料,AWF/LDPE共混材料的黏度和储能模量也随着AWF含量的减小而减小。力学性能测试显示由AWF制备得到的复合材料相比于由WF制备的复合材料的拉伸强度有所下降,断裂伸长率却有较大幅度的提升。SEM分析表明AWF与塑料基体的相容性得到了改善,两相之间共混分散结合更加紧密。     

捏合温度和木纤维水分对木纤维-聚乳酸复合材料中聚乳酸的影响

采用捏合法制备木纤维-聚乳酸(WF-PLA)复合材料。通过凝胶色谱法(GPC)和差示扫描量热法(DSC)研究捏合温度和木纤维水分对WF-PLA生物质复合材料中聚乳酸分子质量及热性能的影响。结果表明:捏合温度对WF-PLA生物质复合材料中PLA性能影响显著。随着捏合温度由180℃升高到200℃,WF-PLA复合材料中PLA的重均分子质量(M珚w)明显下降,数均分子质量(M珚n)在200℃时也明显下降,在190℃时,PLA分子多分散系数最小。不同捏合温度的WF-PLA复合材料中,PLA熔融温度略有不同,熔融温度变化与PLA分子质量相关。木纤维水分对捏合法制备的WF-PLA复合材料中PLA的分子质量和热性能的影响不显著。     

蔗渣纤维增强聚丙烯复合材料的力学性能研究

利用甘蔗渣纤维作为增强剂,回收的聚丙烯塑料作为基体,并添加MAPP为偶联剂,通过熔融混合、注射成型法制成蔗渣纤维/PP 复合材料,研究蔗渣纤维和偶联剂对复合材料静态及动态力学性能的影响。结果表明：与PP相比,添加了蔗渣纤维和MAPP后,除抗拉强度外,复合材料的静态力学强度有所提高;复合材料的储能模量和损耗模量增加,而损耗因子降低;蔗渣纤维/PP复合材料的玻璃化转变温度Tg为61.8℃。     

二氧化硅/木材复合材料的动态黏弹性

为弄清二氧化硅/木材复合材料的动态黏弹性,通过动态热机械分析仪研究不同增重率的二氧化硅/木材复合材料松弛过程的转变温度及力学损耗角正切的变化.结果表明:二氧化硅/木材复合材料的松弛过程数量减少,直接溶胶-凝胶法制备的二氧化硅/木材复合材料,α松弛过程的转变温度随着增重率的增加而向高温方向移动.增重率为0,5.10%和28.00%的α松弛过程的转变温度分别为75.2,76.8和93.6℃;α松弛峰的峰值减小,增重率为0,5.10%,12.63%和28.00%的α松弛过程的损耗角正切值分别为0.043,0.041,0.033和0.03.加硅烷偶联剂法制备的二氧化硅/木材复合材料,随着增重率的增加,α松弛过程的起始温度向低温方向移动,增重率为6.61%,8.08%和10.58%的α松弛过程的起始温度分别为44.9,41.0和32.2℃.     

硅烷偶联剂对木粉/HDPE复合材料力学与吸水性能的影响

采用乙烯基三甲氧基硅烷(A-171)、乙烯基三乙氧基硅烷(A-151)、γ-氨丙基三乙氧基硅烷(DB-550)、γ-缩水甘油醚氧基丙基三甲氧基硅烷(DB-560)、γ-甲基丙烯酰氧基丙基三甲氧基硅烷(DB-570)和γ-巯丙基三乙氧基硅烷(DB-580)6种含有不同取代基的硅烷偶联剂对木粉(WF)进行表面处理,然后与高密度聚乙烯(HDPE)混合挤出制备处理木粉/HDPE复合材料。对复合材料的拉伸、弯曲和无缺口冲击强度及吸水率进行测试,采用扫描电子显微镜(SEM)观察其断面微观形态,并对硅烷处理前后的木粉进行红外光谱(FTIR)分析,从而筛选出较适宜的硅烷偶联剂。结果表明:经这6种偶联剂对木粉处理后,复合材料的力学性能、耐水性和界面相容性都有所改善,其中A-171的处理效果最好,处理后复合材料的弯曲、拉伸和无缺口冲击强度分别提高了31.59%,31.26%和49.29%,冷水和沸水吸水率分别降低了59.71%和48.29%。通过对复合材料SEM观察和FTIR分析可知:A-171成功与木粉发生缩聚反应,最有效地改善了复合材料的界面相容性。这应归因于乙烯基三甲氧基硅烷兼有适宜地与木粉发生缩聚接枝反应及可能与HDPE...     

三种塑料与木纤维复合性能的研究

选用线性低密度聚乙烯(LLDPE)、聚丙烯(PP)、聚苯乙烯(PS)为原料,以2种比率与木纤维复合,用热压法制备了3种木塑复合材料,分析了塑料种类对复合材料的物理力学性能的影响.结果表明,LLDPE与木纤维的复合性能最好,其复合材料的抗冲击性好,但弯曲强度和弹性模量最低;PS与木纤维的复合性最差,其复合材料抗冲击性很差,但弯曲强度和弯曲弹性模量高;木纤维与PP复合材料的综合性能最佳.由此提出用LLDPE与PS共混改性制造木/塑复合材料的设想.     

Effect of Wood Particle Size on the Properties of Wood/Polypropylene Composites Ⅰ:Mechanical Properties

The mechanical properties of wood powder/polypropy!ene composites with different wood particle sizes and wood species have been studied. All of the wood particie sizes increased the E-modulus of the composites. Tensile tests showed that wood partide sizes had a negative effect on the elongation at break and the tensile strength of the composites has been improved when wood particle sizes were be(ow 150 μm (below 100 mesh). For the impact tests, the wood partide sizes had a negative effect, but the MDF fiber can increase the Izod impac     

马来松香对木粉/HDPE复合材料流变性质的影响

用马来松香对木粉进行流动性能改善处理,与高密度聚乙烯(HDPE)熔融复合,挤出成型制备木粉/HDPE复合材料(WF-HDPE).利用傅里叶变换红外光谱(FTIR)和X-射线光电子能谱(XPS)技术,分析经马来松香改性前后木粉表面官能团的变化和元素的变化,采用旋转流变仪研究.WF-HDPE的流变行为.FrIR与XPS分析表明,马来松香分子中的酸酐基团与木粉表面的羟基发生了酯化反应,并且马来松香是以单酯的形式接枝到木粉表面,同时产生一游离羧基.WF-HDPE流变学研究表明:复合材料的复合黏度(η*)、储能模量(G′)和损耗模量(G″)随马来松香用量的增加先减小后增大最后减小,但体系的黏度和模量总体呈下降趋势,木粉经马来松香改性后复合熔体的流变性能显著改善,这不仅有利于提高复合材料的成型加工效率,而且适当的马来松香处理也能够提高复合材料的拉伸强度和弯曲强度,后者被静态力学试验结果所证实.     

密度对稻壳-木材复合材料性能的影响

研究测试在0．75～0．85g／cm^3的变化范围内，密度对稻壳—木材复合材料物理力学性能的影响。试验结果表明，在该密度变化范围内，密度对板的静曲强度、内结合强度及吸水厚度膨胀率等影响显著。     

温度对两种木塑复合材料的影响

在众多环境因素中,温度是对木塑复合材料性能影响最显著的因素之一.在一定温度范围内,木塑复合材料的抗弯性能随温度的升高而降低.     

竹/木复合材料的研究现状与发展趋势

简要介绍了国内外竹/木复合材料研究和发展现状,对竹/木复合材料发展中存在的问题进行了探讨,简要分析了发展竹/木复合材料的经济效益和生态效益,提出竹/木复合材料今后的发展方向.     

白蜡树杆材的剖面密度及与动态力学性能的关系

以6年生白蜡树（Fraxinus chinensis）杆材为试材,利用剖面密度仪测试其不同高度的剖面密度,并分析白蜡树杆材不同高度剖面密度与动态力学性能的关系。结果表明：白蜡树杆材近树皮的木材密度最低、由树皮到近髓心部位的木材密度逐渐升高、髓心处的木材密度又较低;下部的密度平均值为409.0 kg/m3、中部的密度平均值为313.3 kg/m3、上部的密度平均值为304.1 kg/m3;下部心材密度值较集中,而中部和上部心材密度值波动性较大;除白蜡树杆材上部剖面密度与储能模量不显著相关外,白蜡树杆材其他部位的剖面密度与储能模量、损耗模量和损耗因子等动态力学性能极显著相关。     

人工林米老排木材的物理力学性质

对23年生人工林米老排木材物理力学性质进行了测定和分析.结果表明:木材气干密度、全干密度和基本密度分别为0.577 g/cm3,0.554 g/cm3,0.463 g/cm3,属中等级别.木材全干差异干缩和气干差异干缩分别为1.963和2.442,弦向和径向干缩湿胀差异较大;木材端面、弦面和径面的硬度分别为5 717.0 N,3 963.7 N和3 822.8 N,弦面和径面的抗劈力分别为16和14 N/mm,弦面和径面的顺纹抗剪强度分别为11.6 MPa和11.3 MPa,抗弯强度和抗弯弹性模量分别为132.3 MPa和13 092 MPa,冲击韧性为62.5 kJ/m2,顺纹抗压强度为48.7 MPa;木材综合品质系数为3 909×105Pa,品质系数非常高,属高等级材.