一、前言在刨花板中,胶粘剂是以细小的胶滴分布在刨花表面上,刨花表面胶滴的大小和分布的均匀对刨花板的质量至关重要。自1960年以来,胶在刨花表面的分布问题逐渐为人们所重视,并且开展了测定方法的研究。据报道,测定方法大致有几种。各种测定方法是以测定胶的覆盖率或胶量来量度刨花表面胶的分布均匀性。并且受刨花几何形态和刨花大小的限制。本文提出图象法,是将试样或标准件用彩色反转片照相,把试样转变为图象,应用微机图象处理法测定刨花表面胶的覆盖率。对测定覆盖率后的图象进一步使用分光光度计测定图象的光密     

木材含水率测定方法的比较研究

为修订国家标准“CB1931—80木材含水率测定方法”提供依据,本文对含树脂和挥发性物质较多的马尾松等5种木材,采用烘干法、真空干燥法和蒸馏法进行含水率测定的比较。结果表明,烘干法简便实用,但所测得的含水率结果比真空干燥法和蒸馏法为高,如果试样含有较多的挥发性物质,应用烘干法测定含水率误差偏大时,可采用真空干燥法。     

竹木复合刨花板制造工艺研究

从胶水类型、施胶方法以及关键工艺参数等方面探讨了竹木复合刨花板的生产工艺,综合结果表明,竹木复合刨花板批量生产的工艺参数为:低摩尔比环保树脂胶、搅拌气流式喷胶法、竹刨花比例40%～60%、用胶量70 kg(干胶)·m-3、热压压力2.0 MPa、热压温度170℃、热压时间20 s·mm-1、刨花颗粒(芯层)0.5～1.0 mm、板厚8.8 mm。生产的竹木复合刨花板产品质量执行国家标准,质量可以达到国标A类刨花板一等品标准。     

Preparation of Chinese fir wood/MMT nanocomposites and the factors affecting it

The nano intercalation compounding of wood and MMT has important implications for the modification of wood and for the development of new materials. With water-soluble phenol formaldehyde resin as an intermediary, the nanocomposites of Chinese fir (Cunninghamia lanceolata) wood and montmorillonite (MMT) were prepared via three impregnation methods, i.e. normal pres-sure, once and twice vacuum methods. Based on the weight percent gain (WPG) of impregnated wood, the effects of compounding wood and MMT in term...     

基于GC-MS顶空进样法鉴别瘿木降香黄檀与大果紫檀

分别对两个批次含瘿瘤的降香黄檀和大果紫檀木材,采用GC-MS技术顶空进样方式,获取其总离子流图并进行相关系数、系统聚类和特征性化学成分分析。结果表明:两种木材之间总离子流图差别大,无相关性,而同种木材不同批次间相似度高,均含有相同的特征峰,相关系数高(R>0.900);系统聚类分析进一步验证了该试验结果;两种含瘿瘤木材主要特征化学成分种类和含量也完全不同;相关性分析、聚类分析和特征性成分分析均可鉴别区分这两种含瘿瘤木材,解决了含瘿瘤木材传统方法难以鉴别的难题。     

人工林木材的苯酚液化及树脂化研究Ⅱ.液化木基酚醛树脂的制备和性能表征

研究液化产物树脂化合成工艺,表征液化木基酚醛树脂的物化性质,评价树脂的胶合强度和木破率.结果表明,采用一次缩聚的投料方式能简化操作工艺,缩短合成时间.木材液化产物中残渣的过滤与否,对树脂性能有一定程度的影响:残渣含量高时,影响较大;残渣含量低时,影响较小.当甲醛与苯酚的量比为1.5和1.8时,利用含11.0%残渣的杉木液化产物和含16.5%残渣的杨木液化产物,制备了性能优良的酚醛树脂.     

热固性树脂真空加压浸注工艺条件的研究

以西南桦和械木为研究对象，探索不同种类的热固性树脂和不同浸注条件与树脂浸入量和改性材尺寸稳定性的关系。研究结果表明，不同树脂，甚至同一树脂对不同树种的木材具有不同的浸注性，其浸入量随加压浸注时间的延长而增加；木材心边材对树脂的接收能力有所不同；木材性能的改善程度因树种和树脂浸入量而异。     

聚乙烯醇缩甲醛胶对杉木木材的物理与力学性能的影响

对杉木素材与聚乙烯醇缩甲醛浸渍处理材的物理与力学性能进行了对比研究,并利用扫描电子显微镜(SEM)分析了改性剂在木材中的分布情况。结果表明:随着改性剂浓度的提高,改性材的气干密度和抗缩系数均逐渐提高,气干密度最大可达0.4 g/cm3,提高了5.7%,抗缩系数最大提高了18.8%;改性材的吸水率逐渐下降,最多下降了21.1%;当改性剂浓度为30%时,改性材的破坏极限和弹性模量分别提高了6.7%和35.3%;当改性剂浓度为15%时,静曲强度下降了9.9%。SEM结果表明,改性剂填充于部分木射线以及交错纤维间的空隙中。     

木材液体渗透性的改善方法

归纳了影响木材液体渗透性的因素(木材结构、抽提物、微生物、含水率和干燥方法)及其改善方法(化学法、生物法、物理法),着重介绍了压缩法,并提出今后改善液体渗透性的研究方向.     

卫浴用树脂浸渍单板重组材的尺寸稳定性

为满足卫浴装饰装修用木材的需求,以速生桦木为原料,开发出一种树脂浸渍单板重组材。通过分析浸渍三聚氰胺-甲醛(MF)树脂固体含量、浸渍方法、热压压力等因子对板材尺寸稳定性的影响,结果表明:当MF树脂固体含量45%、热压压力1.0MPa,采用辊压浸渍(压榨率50%～70%)时,板材的极限体积膨胀率为6.2%,低于水曲柳、栎木等实木试件,尺寸稳定性大大改善。     

微波等离子处理对脲醛胶性能的影响

脲醛树脂胶粘剂是木材加工领域应用最广泛的胶粘剂,在保障其胶合性能的前提下降低脲醛胶的甲醛释放量是社会关注的焦点和难点。通过试验,研究不同的微波等离子处理方法对脲醛树脂胶粘剂的固化时间、适用期、胶合强度、游离甲醛含量的影响。试验结果表明:等离子处理对脲醛树脂胶粘剂的固化时间和适用期的影响不明显;合适的等离子处理条件可以改善脲醛胶的胶合性能;与未经等离子处理脲醛胶相比,等离子处理后脲醛胶的游离甲醛含量显著降低。     

施胶量和断面结构对沙柳材重组木性能的影响

以沙柳材为原料,在沙柳材重组木施胶量对沙柳材重组木物理力学性能的影响.试验结果表明,实验室条件下的施胶量较佳工艺参数为9%.当木束层平行组坯时,其横纤维方向的干缩率是顺纤维方向的2.27倍;而木束层垂直组坯时干缩率较小、且长宽方向上相近.     

Measurement of urea-formaldehyde resin distribution as a function of MDF fiber size by laser scanning microscopy

A technique has been developed to show the extent of the distribution of the adhesive on the fiber surface. This involves treatment of the resinated fibers with the dye Toluidine blue O, to quench the autofluorescence of the wood materials, to show only the fluorescence of the UF resin in the presence of the dye. The results indicate that this method is a simple and practical way to understand UF resin coverage on wood fibers. With image analysis, the adhesive has been shown to cover a small percentage (3.5%) of the fiber surface, although the percent by weight (based on wood fiber) of resin is much more (13%). The fiber size strongly affects the resin coverage ratio and the chance to collect resin droplets, but it is not significant in the resin-droplets size distribution. Decreasing the proportion of shorter fibers is beneficial in improving resin coverage uniformity. A model for calculating the resin-coverage ratio was developed. The resin coverage is about 4.8% for the resin content of 13% by the model.     

Wood-coating layer studies by X-ray imaging

The penetration depth into wood structure by different wood finishes (solvent-borne, waterborne or powder) was assessed using a non-destructive analysis method, that is, X-ray tomography. The coating thickness was also evaluated. The results obtained from the image analysis by two specific softwares, namely VGStudio MAX^® and ImageJ^®, are compared and discussed by taking into account the chemical properties and anatomy of wood materials and the nature of finishes. The degree of coating penetration is mainly determined by its ability to flow into capillaries, and it was observed that resin type, solid matter content and drying method influence this ability.     

木材产品市场地位图评价方法的研究

本研究确定了市场地位图评价方法的原则，根据这些原则，设计一套较科学的木材产品市场地位图和评价方法，并举两个林业局为例，进行应用，得出合理的评价结果。     

溶胶-凝胶法功能性改良木材研究进展

基于木材天然的双重毛细管系统结构,金属醇盐可在木材"微/纳米容器"内进行溶胶-凝胶反应最终制备木材-无机复合材料。在溶胶-凝胶改良木材过程中,以金属醇盐为主要组分的前驱体溶液可通过涂覆、浸渍/真空加压浸渍、微波/超声波辅助等方式对木材进行改性,且木材密度、基材初始含水率、溶胶反应体系、溶胶粒径、溶胶pH值等对木材溶胶-凝胶改性效果都会有一定的影响。文中主要从制备方法和影响因素2个方面对溶胶-凝胶法功能性改良木材的研究现状进行归纳总结,并提出溶胶-凝胶功能性改良木材的应用前景和发展方向。     

环氧树脂/木质碎料复合材料力学性能

以环氧树脂为胶结材料、不同类型的砂和木质碎料作为集料,利用平板振捣器,采用振实法制备了树脂基木质碎料复合材料.分析环氧树脂用量、木质碎料用量以及砂类型对树脂基木质碎料复合材料的抗折、抗压强度的影响规律.结果表明:试件的最大抗压、抗折强度分别可达5.74和17.16 MPa;在相同胶集比下,试件强度随着木质碎料掺入量的增...     

美国人造板工业发展动向及工艺技术新进展

本文详细论述了美国人造板工业的基本情况、主要产品的开发和研究动向、新工艺和新技术的进展、新型人造板的发展趋势、新胶种的研究和开发、施胶技术的新进展、人工林木材在人造板工业中的开发与利用、人造板的产量和进出口贸易、供需矛盾及解决途径、实现发展目标所采取的措施等。     

竹木复合积成材生产工艺研究

以杉木制材边皮经梳解获得的木束条和刨切薄竹过程中产生的废料为原料,选用酚醛树脂胶黏剂,探讨竹木复合积成材生产工艺及各因素对复合材料性能的影响。结果表明,随着竹片废料用量的增加,竹木复合积成材的各项性能均有不同程度的提高;竹木混杂比、木束条粗细及比例和板密度对积成材静曲强度和弹性模量的影响较大;木束条施胶量对积成材吸水厚度膨胀率和内结合强度的影响较大。     

Quantification of urea formaldehyde resin in wood fibers using X-ray photoelectron spectroscopy and confocal laser scanning microscopy

The potential merits of X-ray photoelectron spectroscopy (XPS) technique for the quantification of nitrogen on the wood fiber surface before and after resination with UF resin was investigated and the resin content was calculated. The bulk nitrogen content of the fibers obtained by XPS after grinding was compared with those obtained by combustion and Kjeldahl methods. Four different fluorescence staining agents were tested by UV spectroscopy. Their λ_max shifted to longer wavelengths when reacted with UF resin. Appropriate analysis conditions were tested for a satisfactory analysis of wood fibers by the confocal laser scanning microscopy (CLSM). The result obtained by CLSM was compared with that obtained by XPS.