阳离子型松香施胶剂的制备

以非离子型聚合物改性得到阳离子化剂,通过转型法成功制得了阳离子型分散松香施胶剂(CDRS),并对其性质进行了表征。CDRS为白色均一乳液,其Zeta电位为 26mV,体积平均粒径为0.271μm,一致性为0.404,粒径分布较好。在pH值6.0、Al2(SO4)3用量1%的条件下,CDRS对再生纸浆的施胶度为40s,施胶效果接近对照样品,耐老化性能则优于对照样品Hi-phase35。浊度实验和扫描电子显微镜观察表明,由于游离松香的皂化作用,CDRS的施胶效果随着pH值的升高而迅速下降。由于成本低,制备方法简单,在近中性条件下施胶效果较好。     

叔胺型与季铵型阳离子分散松香施胶剂的性能比较

用苯乙烯、丙烯酸酯与甲基丙烯酸二甲胺乙酯或二甲基二烯丙基氯化铵的共聚物作乳化剂分别制备了叔胺型阳离子分散松香施胶剂(SYM-1)和季铵型阳离子分散松香施胶剂(JYM-1),并比较了它们的施胶性能。实验结果表明,叔胺型高分子表面活性剂(SYS-1)的电荷密度和SYM-1的施胶性能受pH值影响较大,SYM-1的施胶度在相同施胶条件下比JYM-1大10 s以上,但在含碳酸钙抄纸体系中失去其施胶性。季铵型高分子表面活性剂(JYS-1)的电荷密度不受pH值的影响,用硫酸铝和聚乙烯胺复合物作定着剂时JYM-1在含碳酸钙抄纸体系中的施胶度大于5 s。     

Preparation and sizing mechanisms of neutral rosin size II: functions of rosin derivatives on sizing efficiency

Four rosin derivatives, including rosin esters and rosinamides, were synthesized and used to prepare neutral rosin sizes. Their effects during sizing are discussed in detail. Compared to natural rosin, the rosin derivatives had nearly no effect on sizing even at high retention levels in paper. However, the rosin derivatives in the rosin sizes improved the stability of the emulsion size particles, and there was good correlation between the sizing effect and the stability of the emulsion sizes under neutral to alkaline conditions. On the other hand, the structure of the rosin derivatives significantly influenced the stability and sizing effect of the neutral rosin sizes. In particular, for glycerin rosin ester-rosin sizes, the emulsion stability and sizing effect increased with an increasing proportion of dirosinate, among the glycerin rosin esters. Consequently, it was suggested that the rosin derivatives hardly contribute to the sizing performance of paper but predominantly function to stabilize the neutral rosin size particles, thereby improving the efficiency of the size under neutral to alkaline sizing conditions. Also it was supposed that glycerol dirosinate in the neutral rosin size would probably enable formation of a more stable particle structure to prevent the destructive action of the OH^– ion.This research was presented in part at the 48th annual meeting of the Japan Wood Research Society, Shizuoka, April 1998     

阳离子聚合物施胶增效剂的制备与应用

以丙烯酸甲酯、苯乙烯和阳离子单体为主要原料,采用无皂聚合法制备了阳离子聚丙烯酸酯乳液(CPEE),优化的制备工艺为：阳离子单体用量为总单体量的5％,引发剂用量为总单体量的1％。CPEE、阳离子聚酰胺多胺环氧氯丙烷(PAE)和阳离子淀粉(CS)作为施胶增效剂,用于阳离子石油树脂胶在草浆中的施胶,能够实现中性施胶并取得较好的施胶效果。CPEE和PAE配合使用可明显提高纸页的施胶度和裂断长,效果优于普通的助留剂。     

Mechanism of size retention on handsheets prepared in rosin soap size-alum systems

The mechanism of rosin size retention in rosin soap size-alum systems was studied on the basis of sizing behavior and the rosin size and aluminum contents of handsheets prepared under normal and particular conditions. Rosin size, aluminum, and calcium contents of handsheets prepared with various stirring times of pulp suspensions after pH adjustment suggested that rosin size components adsorbed on pulp fibers predominantly have the structure of free rosin acid rather than rosin aluminum or calcium salt. When a carboxyl group-blocked pulp was used, the rosin size content clearly decreased. This result shows that pulp carboxyl groups play a significant role in rosin size retention. Electrostatic interactions between dissociated carboxyl groups of pulps and anionic rosin size components through cationic aluminum compounds must be present in pulp suspensions. On the other hand, nonionic interactions in pulp suspensions, which occur particularly around pH 6.2–6.5, may also contribute to rosin size retention and appearance of sizing features. When the carboxyl group blocked pulp was used, some rosin size components were retained in the handsheets in largely coagulated form, resulting in no or quite low sizing levels, when the handsheets were dried at 20°C.This research was presented in part at the 64th pulp and paper research conference of Japan TAPPI, Tokyo, June 1997     

Application of cationic polymer prepared from sulfuric acid lignin as a retention aid for usual rosin sizes to neutral papermaking

Cationic polymers that acted as the retention aids for usual rosin sizes in neutral papermaking were prepared from sulfuric acid lignin (SAL), one type of acid lignin. To convert SAL to the cationic polymer (MP-SAL), SAL was phenolated and then treated by the Mannich reaction to introduce the amino groups. In the MP-SAL single system, MP-SAL exhibited high sizing effectiveness in neutral papermaking with the rosin emulsion size. However, MP-SAL showed no sizing effectiveness when soap rosin size was used. MP-SAL showed increased sizing effectiveness as the pK _a of the introduced amino group increased. From this and comparison of the sizing degrees of MP-SAL and polyethylenimine, which possesses a linear structure, it was suggested that the sizing effectiveness was not only affected by the charge density and molecular weight, but also by the basicity of the introduced amino groups and the molecular structure of the retention aid. In the alum–MP-SAL dual system, alum and MP-SAL synergistically enhanced the sizing effectiveness in the rosin emulsion sizing at neutral pH. In turn, this allowed a decrease in the MP-SAL dosage and resulted in a small decrease in brightness.Part of this report was presented at the 48th Lignin Symposium, October 2003, Fukui     

塔尔油制强化造纸施胶剂的研究

以塔尔油为主要原料，研究制造纸用施胶剂的配方及生产工艺条件，该施胶剂可代替松香用于造纸浆内施胶，并对施胶工艺条件进行了探讨。     

松香酸封端的二聚脂肪酸/聚乙二醇聚酯的合成及性能表征

以妥尔油脂肪酸二聚酸为原料,先与聚乙二醇(PEG 400)缩聚后得到聚酯,然后再用松香对聚酯封端,制备了松香基聚酯醚型非离子高分子表面活性剂,并对其性能进行了研究。聚酯适宜的制备工艺条件:减压条件下,反应物二聚酸与聚乙二醇的摩尔比为1∶1.20,催化剂SnC l2用量为二聚酸质量的0.30%,反应温度200℃,反应时间6 h,酯化率达到98.11%。产物的数均相对分子质量(Mn)6 135,重均相对分子质量(Mw)7 438,相对分子质量分布系数(Mw/Mn)为1.212且呈好的窄分布状态。正交试验优化后的松香封端反应的条件为:再补加聚酯质量0.20%的催化剂SnC l2,聚酯与松香物质的量之比为1∶1.30,反应温度215℃,反应时间2.8 h,封端率达62.75%。红外光谱验证了目标产物的存在。性能研究表明,产物具有很好的钙皂分散力、消泡和抑泡力、乳化性和乳化稳定性。     

松香酯中性施胶剂组成与性能的有机概念图分析

讨论了松香酯在中性施胶剂中施胶剂结构与施胶性能的关系，以有机要领图理论分析了施胶剂组成对施胶剂效率的影响，采用三元图表示施胶剂Ｉ／Ｏ值与施胶剂性能间的关联规律，阐述了松香酯的施胶机理。     

松香酸酯用于中性施胶的研究

合成了４种松香酯用于中性施胶。探讨了松香酯结构与施胶性能的关系,研究了施胶条件对香酯施胶效能的影响。松香酯在中,碱性条件下表现了优良的施胶效率。