Role of potassium permanganate and urea on the improvement of the mechanical properties of jute polypropylene composites

Jute fabrics (hessian cloth) reinforced polypropylene (PP) matrix composites (45 wt% fiber) were fabricated by compression molding. Jute fabrics were treated with 2-hydroxyethyl methacrylate (HEMA) using ultraviolet radiation in order to improve the mechanical properties of the composites. Concentration of HEMA, soaking time and radiation dose were optimized. It was found that 15% HEMA in methanol along with photoinitiator Darocur-1173 (2 %), 10 min soaking time and 20th pass of radiation rendered better performance. Urea of different concentrations (0.5–2 %) was incorporated with 15 % HEMA to monitor its effect on the properties and 1 % urea revealed the best results. For the improvement of the properties, jute fabrics were treated with potassium permanganate (KMnO₄) solution in acetone of different concentrations (0.02, 0.03, 0.05, and 0.5 %) at different soaking times (1, 2, 3, and 5 min) before the composite fabrication. Optimized jute fabrics (jute fabrics treated with 0.03 % KMnO₄) were again treated with HEMA (15 %) solution along with urea (1 %) and promising improvement of mechanical properties of the composites was observed. Scanning electron microscopy, water uptake, soil degradation and thermal aging of the treated and untreated composites were also performed.     

Preparation of selective ion adsorbent by photo curing with acrylic and phosphoric acid on jute yarn

Jute yarns were cured with acrylic acid (AA) and phosphoric acid (PA) using UV radiation in order to prepare selective ion adsorbent. A series of formulations were prepared in methanol containing varying percentages of (10–70 %) of AA and 2 % photo-initiator (PI) (Darocur-4043). jute yarns were soaked in this formulation for various soaking times (10–30 min) and cured under UV radiation of different intensities (20–50 UV passes). Concentration of AA, soaking time and intensity of UV radiation were optimized based on polymer loading (PL). The maximum PL (21 %) was observed for 50 % AA solution for 20 min soaking time at 40 UV passes. Various formulations were prepared using 5–15 % (w/w) of phosphoric acid, 50 % AA and 2 % PI in methanol. Then jute yarns were soaked in this solution for 20 min and irradiated at 40th UV pass. The concentration of PA was again optimized for maximum PL. It was found that the formulation containing 10 % PA, 50 % AA, 38 % methanol and 2 % PI showed 70.95 % of PL. To investigate the adsorbent behavior, a 10 ppm CuSO₄ solution was prepared and then grafted yarns were soaked in the solutions for 30–300 min at different conditions. After withdrawing the yarns, the remaining copper in the solution were measured by atomic absorption spectrophotometer (AAS). It was revealed that copper was successfully removed by using the grafted jute yarns.     

Effect of mercerization on mechanical, thermal and degradation characteristics of jute fabric-reinforced polypropylene composites

Jute fabric reinforced polypropylene composites were fabricated by compression molding technique. Fiber content in the composites was optimized at 45 % by weight of fiber by evaluating the mechanical parameters such as tensile strength, tensile modulus, bending strength, bending modulus. Surface treatment of jute fabrics was carried out by mercerizing jute fabrics with aqueous solutions of NaOH (5, 10 and 20 %) at different soaking times (30, 60 and 90 mins) and temperatures (0, 30 and 70 °C). The effect of mercerization on weight and dimension of jute fabrics was studied. Mechanical properties of mercerized jute-PP composites were measured and found highest at 20 % NaOH at 0 °C for 60 min soaking time. Thermal analytical data from thermogravimetric and differential thermal analysis showed that mercerized jute-PP composite achieved higher thermal stability compared to PP, jute fabrics and control composite. Degradation characteristics of the composites were studied in soil, water and simulated weathering conditions. Water uptake of the composites was also investigated.     

Effect of the low and radio frequency oxygen plasma treatment of jute fiber on mechanical properties of jute fiber/polyester composite

We investigated the surface modification of jute fiber by oxygen plasma treatments. Jute fibers were treated in different plasma reactors (radio frequency “RF” and low frequency “LF” plasma reactors) using O₂ for different plasma powers to increase the interface adhesion between jute fiber and polyester matrix. The influence of various plasma reactors on mechanical properties of jute fiber-reinforced polyester composites was reported. Tensile, flexure, short beam shear tests were used to determine the mechanical properties of the composites. The interlaminar shear strength increased from 11.5 MPa for the untreated jute fiber/polyester composite to 19.8 and 26.3 MPa for LF and RF oxygen plasma treated jute fiber/polyester composites, respectively. O₂ plasma treatment also improved the tensile and flexural strengths of jute fiber/ polyester composites for both plasma systems. It is clear that O₂ plasma treatment of jute fibers by using RF plasma system instead of using LF plasma system brings about greater improvement on the mechanical properties of jute/polyester composites.     

Mechanical and electrical properties of photocured jute fabric with 2-hydroxy ethylacrylate

Jute fabric (hessian cloth) was grafted with 2-hydroxy ethylacrylate (HEA) and aliphatic urethane diacrylate oligomer (M-1200) under UV radiation at different intensities (16, 20, 30, 40, 50, and 60 pass) in order to improve the mechanical and electrical properties. The concentrations of the monomer (HEA), and oligomer (M1200), radiation dose, and soaking time were optimized with respect to mechanical property such as tensile strength (TS) of the treated and untreated hessian cloth. The 73 % HEA, 25 % oligomer (M-1200) and 2 % photoinitiator (Darocur-1116) in 1 minute soaking time showed the highest TS at 50th UV pass. The electrical properties such as dielectric constant and loss tangent of both treated and untreated sample were measured at frequency 10 kHz with the variation of temperature. It was observed that dielectric constant and loss tangent increased with increasing temperature up to the transition temperature and then decreased.     

Impact of succinic anhydride on the properties of jute fiber/polypropylene biocomposites

Chemical treatment is an often-followed route to improve the physical and mechanical properties of natural fiber reinforced polymer matrix composites. In this study, the effect of chemical treatment on physical and mechanical properties of jute fiber reinforced polypropylene (PP) biocomposites with different fiber loading (5, 10, 15, and 20 wt%) were investigated. Before being manufactured jute fiber/PP composite, raw jute fiber was chemically treated with succinic anhydride for the chemical reaction with cellulose hydroxyl group of fiber and to increase adhesion and compatibility to the polymer matrix. Jute fiber/PP composites were fabricated using high voltage hot compression technique. Fourier Transform Infrared spectroscopy (FTIR) and Scanning Electron Microscopy (SEM) tests were employed to evaluate the morphological properties of composite. Succinic anhydride underwent a chemical reaction with raw jute fiber which was confirmed through FTIR results. SEM micrographs of the fractured surface area were taken to study the fiber/matrix interface adhesion and compatibility. Reduced fiber agglomeration and improved interfacial bonding was observed under SEM in the case of treated jute fiber/PP composites. The mechanical properties of jute/PP composite in terms of Tensile strength and Young’s modulus was found to be increased with fiber loading up to 15 wt% and decreased at 20 wt%. Conversely, flexural strength and flexural modulus increased with fiber loading up to 10 wt% and start decreasing at 15 wt%. The treated jute/PP composite samples had higher hardness (Rockwell) and lower water absorption value compared to that of the untreated ones.     

Jute yarn as reinforcement for polypropylene based commingled eco-composites: Effect of fibre content and chemical modifications on accelerated ageing and tear properties

Bidirectional PP/jute yarn eco-composites were fabricated via environment friendly commingling technique and its long term durability/life time was monitored as an effect of accelerated solar ageing on its mechanical properties (tensile & flexural). Accelerated solar ageing promoted the thermal oxidation of PP thus resulting in deterioration of its properties, however; MAPP and KMnO₄ treated commingled composites showed much better stability towards thermal oxidation brought about by the solar concentrator, compared to untreated sample and neat polypropylene. This increased resistivity of treated composites (especially MAPP and KMnO₄) towards thermal oxidation brought about by the solar concentrator is due to the increased interfacial adhesion between the matrix and jute yarn owing to chemical modifications. The significance of effective stress transfer between the PP matrix and reinforcing jute yarns is evident from the increased tear resistance of PP/jute yarn commingled composites with increasing fibre content and also with different chemical treatments.     

Mechanical and water absorption properties of woven jute/banana hybrid composites

This work aims to predict the mechanical properties of woven jute/banana hybrid composite. Woven fabrics are arranged in three layers of different sequence. Resin used in this work is Epoxy LY556 with hardener HY951. Composite specimen are prepared by hand-layup techniques. The effect of layering sequence on the mechanical properties namely tensile, flexural and impact was analysed. It is found that the tensile and flexural strength of hybrid composite (Banana/Jute/Banana) is higher than that of individual composites. Similarly, the impact strength of Jute/Banana/Jute hybrid composite is better than other types of composite. It is found that the moisture absorption of woven banana fiber composite is lesser than the hybrid composite. Fractography study of the fractured specimen is carried out using scanning electron microscope to analyse the fracture behaviour of the hybrid composite.     

Mechanical,thermal and interfacial properties of green composites from basalt and hybrid woven fabrics

Composites based on pure Basalt and Basalt/Jute fabrics were fabricated. The mechanical properties of the composites such as flexural modulus, tensile modulus and impact strength were measured depending upon weave, fiber contents and resin. Dynamic mechanical analysis of all composites were done. From the results it is found that pure basalt fiber combination maintains higher values in all mechanical tests. Thermo-gravimetric (TG/DTG) composites showed that thermal degradation temperatures of composites shifted to higher temperature regions compared to pure jute fabrics. Addition of basalt fiber improved the thermal stability of the composite considerably. Scanning electron microscopic images of tensile fractured composite samples illustrated that better fiber-matrix interfacial interaction occurred in hybrid composites. The thermal conductivity of composites are also investigated and thermal model is used to check their correlation.     

A study on mechanical,thermal and environmental degradation characteristics of N,N-dimethylaniline treated jute fabric-reinforced polypropylene composites

The mechanical and thermal behavior of compression molded jute/polypropylene (PP) composites were studied by evaluating tensile strength (TS), bending strength (BS), tensile modulus (TM), bending modulus (BM), impact strength (IS), thermogravimetric (TG/DTG) and differential thermal analysis (DTA). A chemical modification was made to jute fabrics using N,N-Dimethylaniline (DMA) in order to improve the interfacial adhesion between the fabrics and matrix. It was found that jute fabrics on treatment with N,N-Dimethylaniline (DMA) significantly improved the mechanical properties of the composites. Thermal analytical data of PP, both treated and untreated jute fabrics as well as composites revealed that DMA treatment increased the thermal stability of the fabrics and composite. DMA treatment also reduced the hydrophilic nature of the composite. DMA treated jute composite was found less degradable than control composite under water, soil and simulated weathering conditions.     

黄麻PHBV复合材料的耐湿热性能研究

用非织造布技术制作了黄麻/PHBV针刺毡，热压处理后制成黄麻/PHBV复合材料，通过对复合材料的室温、高温干态和湿态力学性能研究，用扫描电镜(SEM)对复合材料的界面进行了表征，显示应用纤维改性技术使复合材料耐湿热性能得到明显提高。     

Banana fiber-reinforced polypropylene composites: A study of the physico-mechanical properties

Banana fiber-reinforced polypropylene (PP) matrix composites were prepared by compression molding and their mechanical properties were evaluated. Banana fibers and matrices were irradiated with UV radiation at different intensities. Mechanical properties of irradiated banana fibers and matrices based composites were found to increase significantly compared to untreated counterparts. Optimized banana fibers were treated with 2-hydroxyethyl methacrylate (HEMA) solution and were cured in an oven at different temperatures for different curing times and then composites were fabricated. Monomer concentration, curing temperature and curing time were optimized with the extent of polymer loading and mechanical properties and showed better mechanical properties over untreated composites. Water uptake and simulating weathering test of the composites were also investigated.     

Surface treatments of jute fabric: The influence of surface characteristics on jute fabrics and mechanical properties of jute/polyester composites

In this study, jute fabrics were modified by alkali, micro-emulsion silicon (MS) and fluorocarbon based agents (FA) in order to enhance the interfacial adhesion between the polyester matrix and the jute fiber. X-ray photoelectron spectroscopy (XPS) and contact angle measurements were used to characterize fiber surfaces. The effects of various surface treatments on the mechanical and morphological of jute/polyester composites were also studied. All surface treatments were shown to improve the tensile, flexural strengths and interlaminar shear strengths of the composites. Moreover, the maximum improvement in the mechanical properties was obtained for the FA treated jute/polyester composites. SEM micrographs of the tensile fracture surface of jute/unsaturated polyester composites also exhibited improvement of interfacial and interlaminar shear strengths by the alkali, MS and FA treatments of jute fibers.     

Tensile response and fracture and failure behavior of jute fabrics-flyash-vinylester hybrid composites

In this work, hybrid materials consisting on a vinylester matrix simultaneaously reinforced with jute woven fabrics and flyash particles were prepared. The tensile response and the fracture and failure behavior of these hybrid composites were investigated. Thermal stability of these materials was also studied. The aim was to obtain an environmentally friendly hybrid material with a good balance of tensile and fracture properties at relatively low cost. The effect of a novel treatment for the jute fabrics on the hybrids mechanical and fracture properties was investigated. The best balance of tensile and fracture properties was obtained for the hybrid consisting of fabrics treated with alkali under stress and fly ashes which also exhibited relatively high thermal stability.     

Characterization of plant and animal based natural fibers reinforced polypropylene composites and their comparative study

Natural fibers are largely divided into two categories depending on their origin: plant based and animal based. Plant based natural jute fiber reinforced polypropylene (PP) matrix composites (20 wt% fiber) were fabricated by compression molding. Bending strength (BS), bending modulus (BM), tensile strength (TS), Young’s modulus (YM), and impact strength (IS) of the composites were found 44.2 MPa, 2200 MPa, 41.3 MPa, 750 MPa and 12 kJ/m², respectively. Animal based natural B. mori silk fiber reinforced polypropylene (PP) matrix composites (20 wt% fiber) were fabricated in the same way and the mechanical properties were compared over the silk based composites. TS, YM, BS, BM, IS of silk fiber reinforced polypropylene composites were found 55.6 MPa, 760 MPa, 57.1 MPa, 3320 MPa and 17 kJ/m² respectively. Degradation of composites in soil was measured upto twelve weeks. It was found that plant based jute fiber/PP composite losses its strength more than animal based silk fiber/PP composite for the same period of time. The comparative study makes it clear that mechanical properties of silk/PP composites are greater than those values of jute/PP composites. But jute/PP composites are more degradable than silk/PP composites i.e., silk/PP composites retain their strength for a longer period than jute/PP composites.     

Mechanical properties of uniaxial natural fabric Grewia tilifolia reinforced epoxy based composites: Effects of chemical treatment

The effects of chemical treatment on the mechanical, morphological, and chemical resistance properties of uniaxial natural fabrics, Grewia tilifolia/epoxy composites, were studied. In order to enhance the interfacial bonding between the epoxy matrix and the Grewia tilifolia fabrics, two different types of treatment: alkali treatment (5 % NaOH) and (3-aminopropyl)-triethoxysilane coupling agent (CA), were used. The epoxy composites containing 0–15 wt% of Grewia tilifolia fabric were prepared by hand lay-up technique, at room temperature. The tensile and flexural properties of the untreated, alkali-treated and coupling agent treated Grewia tilifolia reinforced epoxy composites were determined as a function of fabric loading. The 9 % wt Grewia tilifolia fabric reinforced epoxy composites showed improved tensile and flexural modulii when compared to the neat epoxy matrix. Significant improvement in the mechanical properties was obtained when both alkali and coupling agent treated fabrics were used as reinforcement. Morphological studies demonstrated that better adhesion between the fabrics and the matrix was achieved especially when the alkali-treated and coupling agent treated Grewia tilifolia fabrics were used in the composites. For the water absorption and chemical resistance studies, various solvents, acids and alkalis were used on the epoxy composites. This study has shown that Grewia tilifolia fabric/epoxy composites are promising candidates for structural applications, where high strength and stiffness are required.     

Green composites from maleated castor oil and jute fibres

Castor oil was converted to maleated castor oil (MACO) without any catalyst. MACO was characterized with FTIR, NMR, molecular weight and viscosity measurement. Tung oil (20 wt%) was added to MACO as reactive diluent. Non-woven jute felts were used as reinforcing material. The MACO was polymerized and crosslinked in situ during composite fabrication. The curing behavior of MACO with free radical catalyst was investigated by differential scanning calorimetry (DSC). The MACO/jute composites were tested for their flexural properties, impact strength and dynamic mechanical properties and compared with similar unsaturated polyester resin/jute composites. The flexural moduli of both the composites were nearly similar. The impact strength of MACO/jute composites was 42% higher than that of UPE/jute composites. The damping property of the MACO/jute composites was higher than that of UPE/jute composites over a wide range of temperature.     

Hybrid effect in the mechanical properties of jute/rockwool hybrid fibres reinforced phenol formaldehyde composites

This research work was concerned with the evaluation of the effect of fibre content on the mechanical properties of composites. Composites were fabricated using jute/phenol formaldehyde (PF), rockwool/PF, and jute/rockwool hybrid PF with varying fibre loadings. Jute and rockwool fibre reinforced PF composites were fabricated with varying fibre loadings (16, 25, 34, 42, 50, and 60 vol.%). The jute/rockwool hybrid PF composites were manufactured at various ratios of jute/rockwool fibres such as 1:0, 0.92:0.08, 0.82:0.18, 0.70:0.30, 0.54:0.46, 0.28:0.72, and 0:1. Total fibre content of the hybrid composites was 42 vol.%. The results showed that tensile strength of the composite increased with increasing fibre content up to 42 vol.% over which it decreased for jute and rockwool fibre reinforced PF composites. Flexural strength of the composite was noted to peak at a fibre loading of 42 vol.% for jute/PF composites, and 34 vol.% for rockwool/PF composites. Impact strength of jute/PF composites increased with increasing fibre loading but that of rockwool/PF composites decreased at higher (>34 vol.%) fibre loadings. Tensile, flexural, and impact strengths of jute/PF composites were found to be higher than those of rockwool/PF composites. The maximum hardness values were obtained 42 vol.% for jute/PF composite, and 34 vol.% for rockwool/PF composite. Further increase in fibre loading adversely affected the hardness of both composites. For jute/rockwool hybrid PF composites, tensile and impact strengths decreased with increasing rockwool fibre loading. The maximum flexural strength of jute/rockwool hybrid PF composites was obtained at a 0.82:0.18 jute/rockwool fibre ratio while maximum hardness was observed at a 0.28:0.72 jute/rockwool fibre ratio. The fractured surfaces of the composites were analysed using scanning electron microscope in order to have an insight into the failure mechanism and fibre/matrix interface adhesion.     

Effect of ionizing and non-ionizing preirradiations on physico-mechanical properties of coir fiber grafting with methylacrylate

Coir fibers were modified with methyl acrylate (MA) mixed with methanol (MeOH) under thermal curing method at different temperatures (40?C80 °C) for different curing times (20?C60 min). A series of solutions of different concentrations of MA in methanol along with 2 % benzoyl peroxide, were prepared. Monomer concentration, curing temperature, and curing time were optimized with the extent of grafting of monomer and mechanical properties of cured fiber and found to be 30 % MA, 60 °C and 40 min curing time registered as better performance (Grafting (Gr) = 5.7 %, tensile strength (TS) = 72 %, elongation at break (Eb) = 88 %) than those of untreated fiber. For further improvement of the properties, untreated coir fibers were pretreated with gamma and UV radiations at different doses and then pretreated fibers were soaked in the optimized monomer and cured under optimum conditions. Coir fiber pretreated with UV radiation and grafted with optimized monomer showed the best properties such as Gr (7.12 %), TS (132 %), and Eb (153 %) over raw fiber. Water uptake and simulated weathering test of untreated and treated coir fibers were studied.     

Investigation of jute-lignin-poly (3-hydroxybutyrate) hybrid biodegradable composites with low water absorption

This study developed a novel PHB-lignin-jute biodegradable composite with preferable mechanical properties and low water absorption. The appearances of fracture surface of composites were analyzed by scanning electron microscope. The result suggested a Gaussian-like distribution of the size particles supporting the presence of lignin with a radius smaller than 0.5 μm. According to X-ray diffraction, the presence of lignin and jute fibers was decreased the crystallization of PHB. Moreover, the glass transition temperature of PHB increased, and the endotherm during glass transition was decreased. The maximum tensile strength and modulus of composites were obtained with 30 wt% jute fiber contents and 4 wt% lignin contents. The presence of jute fibers was largely increased the water absorption of composites. However, the presence of lignin was effectively decreased the water absorption of composites at saturation levels.