| 人工林峦大杉木材的物理力学性质 |
| |
| 引用本文： | 余光,高楠,张纪卯,陈文荣,余进,林智勇.人工林峦大杉木材的物理力学性质[J].西南林学院学报,2014(1):106-109. |
| |
| 作者姓名： | 余光 高楠 张纪卯 陈文荣 余进 林智勇 |
| |
| 作者单位： | [1]福建省林业科学研究院,福建福州350012 [2]福建省森林培育与林产品加工利用重点实验室,福建福州350012 [3]福建省国有来舟林业试验场,福建南平353004 |
| |
| 基金项目： | 福建省公益类科研院所基本科研专项（2011R1013-2）资助;福建省属公益类科研院所基本科研专项[2012]资助.致谢：参加本项研究并协助外业调查工作的还有来舟林业试验场陈巧女、连书钗,陈文荣等,借此致谢! |
| |
| 摘 要： | 对福建省引种的24年生峦大杉的木材物理力学性质进行检测，结果表明：峦大杉木材的气干密度为0．344g／cm3、弦向全干干缩率6．020％、弦向湿胀性6．440％、吸水性237．810％、顺纹抗压强度6．004MPa、抗弯弹性模量7250．810MPa、抗弯强度59．840MPa、顺纹抗拉强度62．800MPa；峦大杉的材质与杉木相近，应用方面可参考杉木，在木构件加工时，其安全系数可使用杉木的量值。
|
| 关 键 词： | 峦大杉 木材 物理性质 力学性质 杉木 差异比较 |
Study on Physical and Mechanical Properties of Cunninghamia konishii Wood |
| |
| YU Guang,GAO NanI ZHANG,Jl-mao,CHEN Wen-rong,YU Jin,LIN Zhi-yong.Study on Physical and Mechanical Properties of Cunninghamia konishii Wood[J].Journal of Southwest Forestry College,2014(1):106-109. |
| |
| Authors: | YU Guang GAO NanI ZHANG Jl-mao CHEN Wen-rong YU Jin LIN Zhi-yong |
| |
| Institution: | 1. Forestry Academy of Fujian Province, Fuzhou Fujian 350012, China;2. Fujian Provincial Key Laboratory of Silviculture and Forest Product Processing and Utilization, Fuzhou Fujian 350012, China; 3. Laizhou National Forestry Experimental Farm, Nanpig Fujian 353004, China) |
| |
| Abstract: | The wood physical and mechanical properties of 24 year old Cunninghamia konishii trees introduced and grown in Fujian Province were tested. The results indicated that the air-dried wood density of C. konishii was 0. 344 g/cm3 , the tangential shrinkage ratio was 6.02%, the tangential wet-swelling ratio was 6.44% , the water absorption rate was 237.81%, the compression strength parallel to grain was 6. 004 MPa, the bend elastic modulus was 7 250.81 MPa, the bending strength was 59.84 MPa, and the tensile strength parallel to grain was 62. 8 MPa. The test results showed that the wood properties of C. konishii were quite similar with those of C. lanceolata. The usage of C. konishii can be referred to C. lanceolata. The safety coefficient of C. lanceolata wood could be applied to C. konishii wood while being processed as timber component. |
| |
| Keywords: | Cunninghamia konishii wood physical properties mechanical properties Cunninghamia lanceo-lata difference comparison |