Microstructures and tensile properties of commercial AZ31B magnesium alloy sheets |
| |
引用本文: | HUANG Guang shengb,LI Hong chengb,ZHANG Leib and SONG Bob.Microstructures and tensile properties of commercial AZ31B magnesium alloy sheets[J].保鲜与加工,2009(4):367-370. |
| |
作者姓名: | HUANG Guang shengb LI Hong chengb ZHANG Leib and SONG Bob |
| |
作者单位: | National Engineering Research Center for Magnesium Alloys; College of Materials Science and Engineering, Chongqing University, Chongqing 400030, P. R. China;National Engineering Research Center for Magnesium Alloys; College of Materials Science and Engineering, Chongqing University, Chongqing 400030, P. R. China;National Engineering Research Center for Magnesium Alloys; College of Materials Science and Engineering, Chongqing University, Chongqing 400030, P. R. China;National Engineering Research Center for Magnesium Alloys; College of Materials Science and Engineering, Chongqing University, Chongqing 400030, P. R. China |
| |
摘 要: | Uniaxial loading tests are performed on 0.8 mm thick sheets of commercial AZ31B magnesium alloy in the temperature range from room temperature to 400 ℃. The microstructures and tensile properties are studied. The results reveal that there are few twins in the deformation microstructures created when deformation occurres in temperatures ranging from room temperature to 100 ℃, and dynamic recrystallization take place at deformation temperatures exceeding 200 ℃. Commercial AZ31B magnesium alloy sheets have a preferable strength and ductility at room temperature. The ductility of the sheets is improved as the deformation temperature increases. Some characteristics of low temperature superplasticity or high strain rate superplasticity exist.
|
关 键 词: | magnesium alloys sheet tensile properties microstructure |