Prehydrolysis of beechwood

Summary The kinetics of the isothermal prehydrolysis of beechwood at 160°C and 170°C were investigated. It was shown that the hydrolysis of the hemicellulose portion was realised in two phases. The depth and rate of the first rapid prehydrolysis phase and the second slow phase depend on the temperature used. The lignin content in the prehydrolysed chips increased with the duration of the prehydrolysis due to the easily removable hemicellulose portion. The maximum amount of lignin extracted was gained after 45–60 minutes of isothermal prehydrolysis at 160°C with the yield decrease to 82–80 per cent and at 170°C with the yield decrease to 70–68 per cent. At the temperature of 160°C the amount of the lignin portion extracted was about 5 per cent and at 170°C at about 10 per cent of the whole lignin content in wood. The extraction of the whole hemicellulose portion present in wood was attained at 160°C after 5 hours prehydrolysis time, at 170°C after 80 minutes.By the prehydrolysis of hardwood to 30 per cent loss of the wood substance highly purified dissolving pulp was prepared by AQ catalysed sodium pulping. The pulp attained was characterised by a high alpha-cellulose content over 97 per cent and a low solubility in solutions of alkali. The sulphur-free delignification together with the low consumption of active chlorine (1.5–1.7 per cent) cause less environmental pollution.