Preparation of phenol formaldehyde resin from phenolated wood |
| |
摘 要: |
|
关 键 词: | 酚化木材 酚醛树脂 胶合强度 胶合耐久性 酚类释放量 |
Preparation of phenol formaldehyde resin from phenolated wood |
| |
Authors: | Gai-yun Li Te-fu Qin Shin-ichiro Tohmura Atsushi Ikeda |
| |
Institution: | (1) Research Institute of Wood Industry, Chinese Academy of Forestry, 100091 Beijing, P. R. China;(2) Department of Wood Composite Materials, Forestry and Forest Products Research Institute, 305-8687 Tsukuba, JAPAN;(3) Expert of Research Project on Man-Made Forestry Timber Dispatched by Japan International Cooperation Agency, Japan |
| |
Abstract: | The technique for preparing phenol formaldehyde resin from phenolated wood (PWF) and its characters were studied and analyzed.
Poplar (Populus spp) wood meal was liquefied by phenol in the presence of sulfuric acid as a catalyst. After the liquefied products were cooled,
alkaline catalyst and formaldehyde were added. The mixture was kept at (60±2)°C for 1h and then was heated to (85±2)°C for
1h. The influence of molar ratio of formaldehyde to phenol (F/P) was investigated. The results showed when the molar ratio
of formaldehyde to phenol was over 1.8, the PWF adhesives had high bond quality, bond durability and extremely low aldehydes
emissions.
Foundation item: The research was supported by Sino-Japanese Technical Cooperation Project (2-1-b) and the key technologies R & D Program
for the 10th Five-Year Plan (325-11).
Biography: LI Gai-yun (1974-), female, Assistant professor in Research Institute of Wood Industry, Chinese Academy of Forestry, Beijing
100091, P. R. China
Responsible editor: Zhu Hong |
| |
Keywords: | Phenolated wood Phenol formaldehyde (PF) adhesives Bond quality Bond durability Aldehyde emission |