Synthesis and Properties of Fumaropimaric Acid Modified RTV Silicone Rubber北大核心CSCD

Fumaropimaric acid modified aminopropyltriethoxysilane(FA) was prepared by derivative reaction with rosin as raw material and the structure of the product was confirmed by FT-IR, 1H NMR and 13C NMR. Fumaropimaric acid modified room temperature vulcanized(RTV)silicone rubber was prepared by the dealcoholization condensation reaction of crosslinking agent(FA) and hydroxyl end-blocked dimethylsiloxane(PDMS). And the effects of hydrogenated phenanthrene ring of rosin on the morphology, mechanical and thermal properties of fumaropimaric acid modified RTV silicone rubber were studied, it was found that fumaropimaric acid modified RTV silicone rubber had better the mechanical and thermal properties compared to the unmodified silicone rubber. The tensile strength and elongation at break were 1.22 MPa and 315%; and The 10% mass loss temperature increased to 472 ℃ (SRFA-1), the greatest rate of mass loss temperature increased to 569 ℃, and the residual rate was 3.88%, respectively. © 2018, Editorial Board of «Chemistry and Industry of Forest Products». All right reserved.