油棕叶梗重组方材制备工艺

以油棕叶梗为原材料、酚醛树脂为胶黏剂，采用正交试验方法研究重组方材密度、施胶量、热压时间和热压温度对油棕叶梗重组方材力学性能的影响。结果表明，密度对油棕叶梗重组方材性能的影响较大，密度和施胶量越大，重组方材力学性能越好；热压温度和热压时间对油棕叶梗重组方材性能的影响比较复杂。综合考虑确定油棕叶梗重组方材的较优制备工艺条件为:密度0.7 g/cm³，施胶量12%，热压温度180℃，热压时间40 min；较优工艺条件下油棕叶梗重组方材的弹性模量为7 185 MPa，静曲强度为68.7 MPa，顺纹抗压强度为35 MPa，内结合强度为0.21 MPa。密度为0.7 g/cm³的油棕叶梗重组方材的弹性模量、静曲强度、顺纹抗压强度高于了杉木的性能。     

角钢⁃集成材L形组合柱的受压性能研究

为提高装配式木结构中异形柱的力学性能,设计了一种用热压等边角钢和SPF集成材为原料,环氧树脂胶黏剂连接制作的角钢-集成材L形组合柱,作为框架结构或框架剪力墙结构的角柱。以角钢边宽度对L形柱正截面承载力的影响进行了轴压试验研究,并进行ANSYS有限元模拟,以判断模拟预测的准确性。结果表明:角钢-集成材L形组合柱相对于同截面面积的木柱而言承载能力上升37.0%~51.4%,刚度上升36.5%~72.8%,同时L形柱有良好的延性;适当增加L形柱中的角钢边宽度可以使承载能力有效提高,但是其短边处的集成材易产生破裂,增加试件的脆性破坏;集成材之间的环氧树脂胶合界面在破坏前后都性能良好,在材料弹性阶段钢材和木材有效共同受力,承载力计算时需要考虑钢材的塑形增强作用;ANSYS有限元模拟的角钢-集成材L形组合柱弹性模量结果和试验结果一致,误差在10%以内,模拟结果基本可靠。研究成果对于预测角钢-集成材L形组合柱在实际预制装配时的安全可靠性提供了理论依据。     

重组竹材用酚醛树脂渗透性能研究

对四种重组竹材用酚醛树脂在不同胶液固体含量、浸胶温度和浸胶时间等条件下进行竹材浸胶试验。结果表明：胶液固体含量增加时,竹材浸胶量先增大后减小,固体含量25%时浸胶量最大,达到22.6%;浸胶温度升高浸胶量增加,浸胶温度55℃为宜;浸胶时间对浸胶量影响不呈现规律性,浸胶时间需要在60 min以上;树脂分子量大小对渗透性有一定影响,分子量偏小、分布相对较窄且均匀时,渗透性较好。     

基于C语言的结构用集成材木梁抗弯刚度模型研究

基于平行轴定理,采用变换截面法建立结构用集成材木梁的抗弯刚度C语言可执行程序模型,并通过足尺木梁的抗弯力学性能试验验证模型的有效性。本试验根据木材抗弯弹性模量测定方法国家标准（GB/T 1936.2—2009）中的相关要求,测定层板木材的抗弯弹性模量并将其导入C语言程序模型,得到梁体抗弯刚度的模型理论值。依据结构用集成材国家标准（GB/T 26899—2011）对木梁进行四点抗弯测试并实时采集梁体跨中挠度、荷载数据,得到梁体抗弯刚度的实测值。对比梁体抗弯刚度的模型理论值与实测值,得出其平均相对误差率为3.89%。结构用集成材木梁抗弯刚度模型的建立应充分考虑梁体自身的构造缺陷,以综合层板的力学性能变异性及尺寸效应等影响因素,合理引入修正系数,提高模型的准确度与适用性。     

桉木单板层积材家具角部“L型构件”接合强度研究

以速生桉木单板层积材为基材,榫接合连接、螺钉连接的L型构件为研究对象,通过对桉木层积材家具接合构件进行抗拉和抗弯力学性能试验,观察、分析8种不同榫接合方式对"L型构件"接合强度的影响。研究结果表明,榫接合强度与接合面积有关,接合面积大则接合强度高;桉木单板层积材本身强度对榫接合无影响;采用偏心连接件、倒刺螺母螺杆连接件的接合强度较低,接合部位不够牢固,在家具的使用过程中容易产生松动。     

落叶松层板分级质量评价

对落叶松胶合木用层板进行目测分级并测定其弹性模量和静曲强度,研究各等级层板的弹性模量和静曲强度及其相互之间的关系,探讨层板目测分级和机械弹性模量分级的科学性、合理性。结果表明:根据层板缺陷进行目测分级,等级高的层板其弹性模量和静曲强度的平均值和5%分位值高,目测分级能够基本反映其材质性能,具有一定的科学性与合理性;但目测分级层板弹性模量和静曲强度值的离散度很大,目测分级所能达到的准确与可靠程度决定其不能替代机械弹性模量分级。机械弹性模量分级层板的静曲强度与弹性模量呈正相关性,但各等级层板的静曲强度与弹性模量的相关系数大不相同,其静曲强度值的离散度也比较大,说明该分级方法还有改善的余地。更加科学、可靠的胶合木层板分级方法还有待进一步的探索研究。     

小径木白桦锯材不同加热方式下含水率的变化

讨论小径木白桦锯材在连续加热和间歇加热方式下含水率的变化规律.结果表明:小径木白桦锯材的干燥速率在含水率15%以后明显降低,前期干燥过程锯材的干燥速率比后期的高2～3倍;间歇加热方式有利于内部水分向外扩散,间歇时间对干燥速率的影响很小;干燥过程中锯材厚度方向上的含水率梯度呈不对称分布,这与小径木的心材占较大比例有一定关系;间歇加热减少了锯材内含水率梯度的变化值,同时减少了应力的产生,从而提高了干燥质量.     

Genetic evaluation of Prosopis alba (algarrobo) in Argentina for cloning elite trees

Algarrobo (Prosopis alba) is an important nitrogen-fixing tree adapted to the semiarid regions of northwestern Argentina. The tree provides fuelwood and dimensionally stable lumber for flooring and furniture; its pods that have a high sugar content are consumed by livestock and humans. P. alba has been one of the most heavily harvested species. This paper reports on the evaluation of a nine-year-old Prosopis alba progeny trial containing 57 half-sibling families of eight provenances in northwestern Argentina (of the 1,596 trees planted, 1,289 survived in 1999). Considering the multiple uses of P. alba, the selection criteria included: total biomass production (from basal diameter using regression equations), height, rate of pod production, and pod sensory characteristics. The family-narrow-sense-heritability was 0.487 for height. 0.548 for biomass production, and 0.244 for pod production. In 1998, 12 of the 1,289 trees were more than 4 m tall and had more than 1.75 kg pods per tree; and their pods had a sweet or very sweet non-astringent taste. Scions from these 12 trees were successfully grafted onto unselected P. alba rootstock. These are currently being used to produce rooted cuttings. The pod production, biomass, and height of the 12 clones ranged from 6.55 to 14.4, 1.57 to 13.5, and 1.29 to 1.70 times the respective population means. The genetic gains of 13.5%, 77%, and 147% for height, biomass, and pod production respectively are greater than genetic gains for other tree species and are probably due to the great genetic variability in the local population and the lack of any prior genetic improvement program.This revised version was published online in November 2005 with corrections to the Cover Date.     

模态分析在板材不同位置孔洞缺陷检测中的应用

采用模态分析技术对落叶松板材试件进行振动测试,获取了试件的频响函数,并运用单模态法对频响函数进行了参数辨识,得到了试件的前四阶固有频率和前三阶模态振型.研究表明,含有孔洞试件的固有频率与标准试件相比略低一些,但差别不大.试件在含有孔洞的节点处模态振型会发生突变,因而可运用模态分析技术判定孔洞在试件上的具体位置,对板材孔洞缺陷进行定量检测.     

Fire-resistant performance of a laminated veneer lumber joint with metal plate connectors protected with graphite phenolic sphere sheeting

Creep under fire of laminated veneer lumber (LVL) joined with metal connectors was studied. The fire-resistant performance of LVL butt joints connected with metal plates protected with graphite phenolic sphere (GPS) sheeting was discussed. The GPS sheeting was overlaid on the joint in different sizes and locations. The joint was exposed to a burner with a top flame temperature of 800°C and loaded with a load of 200 N to test for creep under fire. The results showed that the fire-resistant performance of the joint was markedly improved by the sheeting. The size and location of the GPS sheet significantly affected the time to rupture of the specimen, which was six times longer than that without GPS. Temperature measurements at the joint showed that the GPS sheeting distributed the heat along the surface and delayed failure. Thermographic images and analyses clarified the improvement in fire-resistant properties due to GPS.