Ba(OH)_2加入温度对酚醛树脂胶黏剂性能的影响

采用Ba(OH)_2和NaOH复合催化剂,通过两步甲醛加入法工艺制备酚醛树脂胶黏剂。考察了Ba(OH)_2加入温度对酚醛树脂颜色、黏度、水溶倍数和固化时间的影响,并采用FTIR和DSC对胶黏剂进行了表征。结果表明,随着Ba(OH)_2加入温度升高,所制得胶黏剂的黏度逐渐降低,水溶倍数逐渐增大,固化时间逐渐延长。FTIR测试结果表明,胶黏剂中高活性的邻-邻结构随着Ba(OH)_2加入温度升高而逐渐减少,这正是黏度、水溶倍数和固化时间变化的原因所在。DSC测试结果显示,固化温度和放热量随着Ba(OH)_2加入温度的升高而逐渐增大,表明固化速率降低。综合考虑各项性能,应在60℃时加入Ba(OH)_2制备酚醛树脂。     

胶合板用硅镁系环保无机胶黏剂制备与阻燃性能研究

以硅酸钠、硅酸铝、氧化镁和硅烷偶联剂为原料,制备胶合板用硅镁系硅酸盐无机胶黏剂。采用单因素试验和正交试验考察了主要成分用量对胶黏剂的胶合性能的影响,并采用锥形量热分析技术和热重法分别测试其阻燃抑烟性能以及耐热性能。结果表明,当硅酸钠的质量分数为92.5%,硅酸铝的质量分数为4.7%,氧化镁的质量分数为2.8%,硅烷偶联剂的百分比含量为0.6%(相对于硅酸钠的质量而言)时,改性胶黏剂的综合性能最好,其胶合强度达到0.85MPa,阻燃抑烟性能效果显著,热释放总量和热释放速率明显降低。     

雾滴图像粘连特征改进判断及分离计数方法优化

雾滴在靶标上常出现粘连的情况，为准确测量雾滴尺寸、掌握雾滴分布规律，需要判断雾滴是否粘连，并用图像处理技术将粘连雾滴分开。首先提出判断雾滴是否粘连的改进方法，该方法结合雾滴的形状因子和面积阈值对粘连雾滴进行判断和特征提取，并用极限腐蚀法和迭代开运算法对粘连雾滴进行计数处理，其次调用迭代开运算标记的分水岭算法分割，最后对分割后雾滴的连通域进行标记及形状圆整。试验结果表明：该方法可实现粘连雾滴的自动判断和特征提取，弱粘连准确率100%，强粘连可达97.2%以上。该算法获得的雾滴粒径参数与激光粒度仪试验测量结果接近，其尺寸测量准确度较Deposit Scan软件计算平均提高了7.67%。基于相同的样本，与人工计数标定结果对比表明，该方法获得的雾滴个数快速且精准度达97.06%以上。     

多层瓦楞纸淀粉胶的性能

分别以玉米淀粉、小麦淀粉、马铃薯淀粉为原料,采用二步法按不同配比制备多层瓦楞纸生产线用淀粉胶黏剂,并对其性能进行研究。结果表明,糊化温度随淀粉胶质量分数和NaOH质量分数的增大而降低;SteinHall黏度随NaOH质量分数增大先减小,当NaOH质量分数超过0.7%时,Stein-Hall黏度迅速增大。在同一温度时,Brabender黏度从大到小依次为马铃薯淀粉胶、小麦淀粉胶、玉米淀粉胶;经过同一放置时间时,Brabender黏度从大到小依次为马铃薯淀粉胶、玉米淀粉胶、小麦淀粉胶。     

天然黑荆树皮单宁-糠醇木材胶黏剂的研究

通过天然黑荆树皮单宁与来自玉米及小麦剩余提取物的糠醇在酸性条件下反应，制备出一种新型无污染的热固性生物质木材胶黏剂。通过基质辅助激光解吸电离飞行时间质谱( MALDI￣TOF￣MS)及傅里叶红外光谱( FT￣IR)对树脂的结构进行表征；采用静态热机械性能分析( TMA)对树脂的玻璃转化温度及弹性模量进行表征；通过制备胶合板的胶合强度对树脂的胶合性能进行表征。结果表明：在酸性条件下，糠醇中的羟甲基能够且主要与单宁结构单体A环上的6或8号位上的C连接而缩聚成具有一定粘度的大分子化合物。同时，与基于脲醛树脂改性尿素—甲醛—糠醇树脂相比较，单宁—糠醇树脂具有更高的弹性模量及玻璃转化温度，且基于单宁—糠醇树脂制备胶合板的胶合性能优于尿素—甲醛—糠醇树脂。     

制备工艺对标签胶性能影响的研究

以脱脂大豆粉(SF)为原料制备豆粉标签胶,主要研究了制备工艺(包括液料比、尿素加量、交联剂加量、处理时间和处理温度)对豆粉标签胶黏度、粘接性能和耐水性能的影响,并借助红外光谱对标签胶进行分析与表征。研究结果表明,豆粉标签胶的最佳制备工艺为:m(水):m(SF)为3.0:1.0,尿素加量100%,交联剂加量4.5%(占SF质量),处理温度70℃,处理时间1.0 h。此条件制备的豆粉标签胶黏度为32450mPa.s,粘接力177 N,耐常温水性(20±2)℃≥104h,远高于标签胶行业标准规定的72 h要求。FT-IR分析表明,加入交联剂后,大豆蛋白在波数为1 168 cm~(-1)处产生新特征峰,这可能是该研究豆粉标签胶具有较佳耐水性能原因所在。     

A New Method for Measuring Bonding Shear Properties of Adhesives on Steel Substrates

Single-lap-joint adhesively bonded metal specimen which is the national standard experimental method in use has an extremely non-uniform distribution of shear stresses along the joint, and tensile stress concentration of high values is produced on the steel substrate interfaces. Therefore the test result, which is not the real bonding shear strength between adhesive and steel substrates, can only be used as a test index for qualities of adhesives not the strength criterion for load is capacity evaluation. The combined bonding disc specimen is adopted for measuring bonding shear properties of adhesive on steel substrates, has a very uniform distribution of shear stresses in adhesive and along the bonding surfaces of steel substrates, of which the uniform coefficient is greater than 0.97. Furthermore, when adhesive joint is treated as an arc and steel substrates are chamfered at both ends of the joint, tensile stresses on the bonding surfaces can be reduced to less than 20 MPa which can hardly cause tensile failure. Thus, the results of combined bonding disc specimens can actually represent the real bonding shear strength or bonding shear-compression strength between adhesive and steel substrates, which can be used as strength criterion for load capacity evaluation of bonding members.     

竹粉填充对脲醛树脂胶黏剂性能的影响

为探索竹粉替代面粉填充脲醛树脂胶黏剂的可行性，减少面粉在非食品工业的消耗，充分利用竹材加工剩余物，以竹粉作为脲醛树脂胶黏剂的填充剂，研究了竹粉的添加量、粒度对脲醛树脂胶黏剂的粘度、胶合性能和甲醛释放量的影响，以及竹粉在胶液中的分散情况，并采用傅里叶变换红外光谱对添加了竹粉的脲醛树脂胶黏剂进行了分析。结果表明：竹粉在脲醛树脂胶液中易分散，且随竹粉粒度的减小，竹粉分散越均匀；竹粉粒度、添加量对脲醛树脂胶黏剂的胶合强度有较显著的影响，但对甲醛释放量的影响不显著；当添加量为脲醛树脂胶黏剂( UF)胶液质量15％的220－240目竹粉时，竹粉填充不影响其胶合强度和甲醛释放量。     

脲醛树脂胶黏剂用添加剂的研究与应用进展

依据化学组成成分及降低游离甲醛含量的作用机理不同,将脲醛树脂胶黏剂用添加剂分为有机添加剂、纳米材料及无机矿物质添加剂,综述了脲醛树脂用添加剂的研究与应用进展。     

聚氨酯木材胶粘剂的研究(Ⅰ)——化学组成对粘接力学性能的影响

以多亚甲基多苯基多异氰酸酯（PAPI）和聚醚多元醇为原料合成了一种单组分、室温湿固化的端异氰酸酯聚氨酯胶粘剂。本研究考察了物料的化学组成对胶粘剂粘接木材的力学性能产生的影响。实验表明，与改性二苯基二异氰酸酯（MDI）相比，PAPI合成的胶粘剂对木材粘接干压剪强度提高了60％；将相对分子质量（Mw）为800、1000和2000的聚氧化乙烯二醇（PED）、Mw为300和3000的聚氧化丙烯三醇（N303和N330）以及聚四氢呋喃一氧化丙烯二醇（NG220）按优化的比例复合使用，以改性胺和有机锡复合催化，可有效提高粘接木材的干和湿压剪强度、固化速率以及木破率。Fr-IR光谱证实聚醚多元醇的-OH与PAPI的-NCO反应生成了氨基甲酸酯（-NHCOO-），但N—H和G=O均以氢键形式存在。