木材纤维与回收聚丙烯的热压复合工艺研究

研究了热压时间、热压温度、聚丙烯和偶联剂加入量等工艺因子对木材纤维和回收聚丙烯复合材料性能的影响。确定了压制密度为0．80g／cm3、10mm厚的木塑复合材料的最佳工艺条件为:热压温度175℃、热压时间8min、塑料加入量40％、偶联剂的加入量4％。在此条件下压制的木塑复合板材,物理力学性能中的内结合强度和吸水厚度膨胀率与中密度板的国家标准相比达到优等水平,静曲强度和弹性模量基本满足中密度板的国家标准要求。     

东莞峡口大桥加固设计

该文通过东莞市峡口大桥的加固工程,针对该桥检测评估结果提出了有针对性的加固设计方案及措施.经有关部门检测,加固效果良好.     

三倍体毛白杨的木材构造与材性的研究

对三倍体毛白杨的木材构造特征、纤维形态、基本密度进行了观察记载和测定，发现其生长轮宽度达2.5～3.0cm，纤维平均长度大于同年轮的其它杨木，基本密度小于毛白杨成熟材，木纤维的含量较高，同时纤维的壁腔比较小，所以三倍体毛白杨是一种较好的造纸和纤维工业原料。     

油棕丝纤维板热磨机螺旋进料器的设计分析

介绍了油棕丝的特点、油棕丝螺旋进料器主要参数的计算及关键元件的设计分析。     

防霉中密度纤维板的研制

在湿度较大的地区和潮湿的场所,中密度纤维板(下称中纤板)因长期受潮而产生霉变,使其性能受损,更为严重的是污染了居住环境。因此,研究如何防止中纤板霉变,使其具有防霉性能应作为一项重要的课题。笔者通过对防霉剂选择、优化热压工艺参数、防霉效果测试等方面进行了试验研究,确定了适当的防霉剂及其添加量,得出了压制防霉中纤板的优化热压工艺。     

Effects of five additive materials on mechanical and dimensional properties of wood cement-bonded boards

There is a growing desire to improve the properties and use of nonwood plant materials as supplements to wood materials for wood cement-bonded boards (WCBs). This study was conducted to determine the comparative properties of WCBs containing various amounts of discontinuous inorganic fiber materials, such as alkali-resistant glass fiber, normal glass fiber, mineral wool, and nonwood plant materials such as retted flax straw and wheat straw particles. Tested cement-bonded boards were made at wood/additive compositions of 100/0, 90/10, 80/20, 70/30, 60/40, and 50/50 (weight percentages). Seventy-eight laboratory-scale WCBs were produced. Various board properties, such as the modulus of rupture (MOR), internal bonding strength (IB), water absorption (WA), thickness swelling (TS), and linear expansion (LE), were studied. The test results showed that three types of discontinuous inorganic fiber used as reinforcing materials in composites significantly enhanced and modified the performance of WCBs. The mechanical properties and dimensional stability of cement-bonded board were significantly improved with increasing amounts of the additives. MOR and IB were increased; and WA, TS, and LE of boards were reduced by combination with the inorganic fiber materials. The results also indicated that combination with retted flax straw particles only slightly increased the MOR of boards, and wheat straw particles led to marked decreases in all the mechanical properties and the dimensional stability of WCBs.Part of this report was presented at the 50th Annual Meeting of the Japan Wood Research Society, Kyoto, April 2000     

Effect of maleic anhydride grafted styrene-ethylene-butylene-styrene （MA-SEBS） on impact fracture behavior of polypropylene / wood fiber composites

MA-SEBS as compatibilizer and impact modifier was incorporated into Polypropylene/Wood Fiber （PP/WF） to enhance interface adhesion and impact strength of the composite. The effect of MA-SEBS content on the impact fracture behavior of PP/WF composites was studied. The impact properties of composites with 8% MA-SEBS reached the maximum value. And further increasing of MA-SEBS content to 10% did not improve the fracture toughness, but improved the stiffness of composites by DMA analysis. This was attributed to the improved PP/WF adhesion. As the MA-SEBS content is more than 8%, the molecule interaction of PP and WF was expected to much stronger than lower MA-SEBS. Scanning electron microscopy （SEM） was performed to analyze the impact fracture surface and showed a stronger affinity for the wood surfaces.     

竹纤维--一种纺织新材料

竹纤维是一种新型的绿色环保纤维,它具有良好的服用性能,是一种有着广泛应用前景的纺织纤维,该文介绍了竹纤维的种类、结构特点以及竹纤维织物的一些特性.     

Characterization of the morphological,physical, and mechanical properties of seven nonwood plant fiber bundles

The morphological, physical, and mechanical properties of the nonwood plant fiber bundles of ramie, pineapple, sansevieria, kenaf, abaca, sisal, and coconut fiber bundles were investigated. All fibers except those of coconut fiber had noncircular cross-sectional shapes. The crosssectional area of the fiber bundles was evaluated by an improved method using scanning electron microscope images. The coefficient factor defined as the ratio of the cross-sectional area determined by diameter measurement, to the cross-sectional area determined by image analysis was between 0.92 and 0.96 for all fibers. This indicated that the area determined by diameter measurement was available. The densities of the fiber bundles decreased with increasing diameters. The diameters of each fiber species had small variation of around 3.4%-9.8% within a specimen. The tensile strength and Young’s modulus of ramie, pineapple, and sansevieria fiber bundles showed excellent values in comparison with the other fibers. The tensile strength and Young’s modulus showed a decreasing trend with increasing diameter of fiber bundles.