载银壳聚糖处理对薄木抗菌性能影响的研究

采用载银壳聚糖对桦木薄木进行浸渍处理,分析了壳聚糖、载银壳聚糖、银离子浓度对处理后薄木的抗菌性和抗拉强度以及耐水性能的影响。研究结果表明：薄木经载银壳聚糖处理后,其抗菌性、横向抗拉强度及耐水性能都得到了显著增强。     

竹篾帘搭接对结构用竹篾层积材力学性能的影响

竹篾帘拼长是制备超长竹篾层积材(LBSL)的必要手段,竹篾帘端头搭接是拼长的方式之一。对LBSL抗弯及抗拉性能的测试结果表明:搭接长度和位置对板材力学性能影响显著;增加搭接长度有利于提高其抗弯和抗拉性能,当搭接长度大于10mm时,板材的力学性能趋于稳定;搭接接头位于芯层时,板材性能优于接头位于表层。LBSL生产组坯工序要保证竹篾帘搭接长度,同时尽量避免板坯表层出现搭接。     

添加糖对鱿鱼肉糜的热凝胶性影响

[目的]研究添加糖的种类对鱿鱼肉糜热凝胶性的影响。[方法]在鱿鱼肉糜中分别添加葡萄糖、乳糖、麦芽糖、淀粉,分析热凝胶的弹性、强度和保水性。[结果]添加糖能够有效提高鱿鱼肉糜热凝胶弹性,其中加乳糖（2．5％）组的热凝胶弹性最好;加乳糖后鱿鱼肉糜热凝胶强度最高,达到363．87g／cm2,比空白组279．04g／cm2（未加糖）提高了30．40％;加糖能提高鱿鱼肉糜的热凝胶保水性,淀粉组和乳糖组的热凝胶失水率分别为28．08％和31．20％,显著低于空白组失水率43．50％。[结论]添加糖能够有效改善鱿鱼肉糜的热凝胶性能。综合考虑热凝胶弹性、强度和保水性,确定乳糖为适合的添加糖。     

水稻植质钵盘高强度结构设计与性能试验

针对水稻植质钵盘应用过程中存在的问题,对水稻植质钵盘结构进行改进设计。阐述水稻植质钵盘设计思想,探讨水稻植质钵盘结构改进设计思路及结构设计依据,分析改进前后的水稻植质钵盘结构强度,同时分别以改进前的水稻植质钵盘(CK1)、日本塑料钵盘(CK2)和平育秧盘(CK3)为水稻育秧载体,通过多年田间对比试验探讨改进后的水稻植质钵盘(CK)对水稻生产的影响。试验结果表明:改进后的水稻植质钵盘正应力较改进前水稻植质钵盘提高15.09%;CK和CK1秧苗移栽后均无缓苗期,CK2和CK3秧苗均需一定缓苗期;在生育期和收获期,CK和CK1秧苗素质均无显著差异,但均优于CK2和CK3秧苗素质;CK生产投入均低于CK1和CK2生产投入,但高于CK3生产投入;CK和CK1土壤有机质含量相同,在0~10 cm、10~20 cm和20~30 cm土层,CK土壤有机质含量分别较CK2和CK3土壤有机质含量提高7.06%、10.08%,2.53%、3.34%,0.48%、0.11%;CK和CK1对土壤容重影响程度相同,与CK2和CK3相比较,在相同土层,CK能够促使土壤容重减小;CK和CK1产量持平,较CK2和CK3,产量分别提高10.59%和13.54%。     

碳酸丙烯酯固化剂对酚醛树脂固化性能的影响

在自制的酚醛树脂（PF树脂）中加入不同固化剂,考察固化剂对酚醛树脂固化时间的影响,筛选出固化速度最快的固化剂碳酸丙烯酯,同时研究了碳酸丙烯酯用量与树脂固化时间、适用期、胶合强度之间的关系,并优化出添加最佳用量的碳酸丙烯酯优化树脂的热压工艺．结果表明,当碳酸丙烯酯用量为树脂胶液量的2％时,酚醛树脂的固化时间缩短了64．4％,适用期240min．利用添加2％碳酸丙烯酯的酚醛树脂,通过不同热压工艺生产胶合板,当热压时间为1．0min·mm-1时,热压温度从105℃降到95℃;当热压温度为105℃时,热压时间从1．0min·mm-1缩短至0．7min·mm-1,两者均可减少能耗,降低生产成本．差示扫描量热法分析结果表明,添加2％碳酸丙烯酯的酚醛树脂固化起始温度为49．6℃,峰顶温度为109．2℃,固化温度较低．     

环境温度对拖拉机压敏胶标签剥离强度的影响

考察了温度变化对拖拉机用压敏胶平面标签180°剥离强度的影响,并模拟季节变化及现场粘贴情况,对压敏胶标签的剥离强度进行分析。结果表明,不同品种的压敏胶标签由于压敏胶粘剂自身特性的不同,达到最佳剥离性能的粘贴环境温度也不同。拖拉机压敏胶标签粘贴时,可根据环境温度的不同,选择合适的压敏胶标签,或适当控制被粘贴面温度,以达到理想的粘贴效果。     

液态地膜拉伸强度和透湿性的试验研究

以可再生资源木质素磺酸钙(木钙)、聚乙烯醇(PVA)、硅溶胶为基料,采用311A最优设计,合成不同基料比例的PVA-木钙-硅溶胶复合型液态地膜原液。利用延流成膜法,将原液制备成风干片状膜,测试和分析不同基料膜的拉伸强度和透湿性。结果表明:1)聚乙烯醇对增强液态地膜拉伸强度起主要作用,聚乙烯醇与木钙、木钙与硅溶胶的交互作用对增强拉伸强度具有正向相互促进作用。基料添加量为:聚乙烯醇54.28~70.36g、硅溶胶6.67~12.83g、木钙11.90~41.63g时液态地膜力学性能较好。2)硅溶胶对降低液态地膜透湿性起主要作用,木钙和硅溶胶对降低液态地膜透湿性具有正向相互促进作用。基料添加量为:聚乙烯醇44.55~55.45g、硅溶胶10.91~19.09g、木钙43.78~50.62g时液态地膜透湿性较小。不同性能优化值范围不同,在实际应用中可根据对不同性能的要求选择基料配方。     

Physical and mechanical properties and colour changes of fast-growing Gympie messmate wood subjected to two-step steam-heat treatments

This study aimed to evaluate physical and mechanical properties and colour changes of fast-growing Gympie messmate wood subjected to two-step steam-heat treatments. To achieve this, Gympie messmate wood was thermally treated under different conditions. Combined steam (127°C and ～0,1471 MPa) and heat treatments in an oven (180–240°C for 4 hours) were performed. Physical and mechanical properties were evaluated by weight loss, equilibrium moisture content, specific gravity, volumetric and linear swelling and static bending tests, while colour changes were studied using CIEL*a*b* technique. The main findings showed that the steam pre-treatment in autoclave influenced most of the technological properties evaluated, mainly for heat treatments performed in low temperatures (180–200°C). The most significant changes after thermal treatments were observed for dimensional stability, which increased as a function of temperature of treatment. On the other hand, mechanical strength of thermally modified wood was significantly affected, while stiffness did not change. Colour modifications due to the application of two-step steam-heat treatments confirm the possibility to using these samples for aesthetic purposes.     

玉米生长期土壤抗剪强度变化特征及其影响因素

采用野外实测与室内分析相结合的方法,对玉米各生育期土壤抗剪强度变化特征及其影响因素进行了研究。结果表明:随着玉米生育期推进,0~5 cm土层土壤抗剪强度持续增加,于成熟期达最大;5~10 cm和10~15 cm土层表现为先增加后减小,在抽雄期达最大;15~20 cm土层抗剪强度总体较大。玉米对0~5 cm、5~10 cm和10~15 cm土层土壤抗剪强度的增强效应较好,其增强率在抽雄期最高。抗剪强度与土壤含水率呈线性函数关系,与土壤容重呈极显著线性正相关;含根量、根长和根系体积等根系参数与土壤抗剪强度呈极显著正相关,土壤抗剪强度增强值与0~1 mm根长增加值呈极显著正相关。土壤抗剪强度随玉米生育期推进逐渐增强,含水率、容重和玉米根系对土壤抗剪强度具有较大影响,采用一定耕作和水保措施增加土壤表层含水率和容重,同时选取含0~1 mm根径较多的玉米品种对该区域水土流失防治具有重要意义。     

竹粉含量及粒径对竹塑复合材料性能的影响

以竹粉和高密度聚乙烯为原料,通过混炼、平板热压制备竹粉/HDPE复合材料,研究竹粉含量和粒径大小对复合材料的吸湿、吸水性以及力学性质的影响.试验结果表明:随着竹粉添加量的增加,竹塑复合材料的吸湿、吸水性能也逐渐增大,同时,当竹粉粒径变小时,复合材料的吸湿、吸水性能也增大;复合材料的冲击强度随着竹粉含量的增加而减小,而拉伸强度与弯曲强度随着竹粉含量增加而增大,但当竹粉含量超过50％,这些强度反而降低;随着竹粉粒径增大,抗冲击强度逐渐降低,而拉伸强度与弯曲强度增大,但当粒径超过180μm时,这两个强度则开始下降.