铝合金温室拱形ETFE膜屋面抗风性能分析

为分析铝合金结构拱形ETFE(乙烯-四氟乙烯热塑性聚合物)膜屋面的抗风性能,提高其设计的安全性,该文根据单轴拉伸试验数据,确定了ETFE薄膜材料的力学参数和应力应变关系;基于几何非线性有限元理论,推导了膜单元的基本方程;利用大型通用有限元软件ANSYS,采用支座提升法对骨架式拱形ETFE屋面进行了找形分析,建立了用于荷载分析的计算模型;对拱形ETFE屋面在风荷载工况下进行了算例分析,计算了膜面主应力分布和变形特征;分析了不同膜面预应力水平对承载性的影响。分析结果表明,风荷载主要影响ETFE膜屋面第一主应力的分布,适当增加膜面预应力可以显著提高其整体刚度和承载力。研究结论为铝合金温室拱形ETFE屋面的抗风计算分析和施工提供了参考。     

The effect of Ce addition on As cast microstructures of AZ31 magnesium alloy

Various opinions still exist regarding the grain refinement of magnesium alloys resulting from Ce addition. We investigate effect of Ce addition on the as cast microstructures of AZ31 magnesium alloy. The research results indicate that adding from 0.5 wt% to 1.5 wt% Ce to AZ31 magnesium alloy does not effectively refine the alloy grains; instead, the opposite effect results, causing obvious grain coarsening. The coarsening trend is related to the amount of Ce. After adding 0.5 wt% Ce to AZ31 magnesium alloy, the average alloy grain size increases from 60 μm to 164 μm. Furthermore, increasing the amount of Ce added from 0.5 wt% to 1.5 wt% causes the average grain size to decrease gradually. The average grain size of AZ31 magnesium alloy with and additional 1.5 wt% Ce still exceeds that of the AZ31 magnesium alloy without additional Ce, however.     

铍—二溴羟基苯基荧光酮Brij—35的显色反应

研究了铍－二溴羟基苯基荧光酮－Ｂｒｉｊ－３５胶束显色反应的最佳形成条件，在ｐＨ８．３－９．５的弱碱性介质中，配合物最大吸收波长是５４８ｎｍ，其表观摩尔吸光系数是１．４２×１０＾５Ｌ．ｍｏｌ＾－１，ｃｍ＾－１，铍量在０－１．６μｇＢｅ／２５ｍＬ范围内遵守比尔定律。     

AgNi合金表面成分均匀性的研究

报导了AES对室温下AgNi两相合全表面成分均匀性的研究结果.发现无论是未经理的自然表面,或是经离子轰击后的清洁表面,或是轰击后仃放长时间的表面,都表现出较明显的成分不均匀性.并发现该系统Ag是择优溅射元素.     

AZ31镁合金薄板的交流钨极氩弧焊

探讨了氩弧焊工艺参数对镁合金焊接接头质量的影响，采用金相显微镜，对AZ31镁合金薄板TIG焊接接头进行了微观组织观察、用X-射线衍射仪等分析测试手段对相组成和力学性能进行了分析，结果发现：焊接电流为40A和45A时，焊接接头的力学性能最好，(σb为205MPa)，为母材强度的80％左右，断裂总是发生在热影响区，焊缝区组织呈细小的等轴晶，主要存在α-Mg和Mg17Al12两种相，热影响区组织较粗大。     

非晶态Ni—Si—B系合金结构驰豫的电阻法研究

本文通过精密测定非晶态Ｎｉ－Ｓｉ－Ｂ系合金的电阻率在不同温度下等时退火后的变化，研究了该合金的结构驰豫过程，得到其电阻率变化随退火温度而作振荡性起伏的关系曲线，并利用作者提出的结构缺陷形成机制对该振荡性曲线作出了比较合理的微观机理解释。     

细晶AZ61镁合金板材的CO2激光焊接性能

采用CO2激光器对2 mm厚的AZ61镁合金细晶板材分别进行了填充焊和自熔焊实验.研究了细晶镁合金板材的焊接性和填充带合金化稀土元素Ce对接头组织及力学性能的影响.结果表明，细晶板材的焊接接头热影响区不明显，组织较母材变化不大，半熔化区范围窄、液化程度低，未进行合金化的自熔焊焊缝组织较粗大，焊缝晶粒尺寸约15 μm，而填充焊焊缝组织为平均晶粒尺寸是5 μm的等轴晶，即合金化稀土元素Ce可细化焊缝组织，而且稀土元素Ce的加入能抑制柱状树枝晶区而扩大等轴晶区域范围.填带焊接头的平均抗拉强度和伸长率较自熔焊接头分别提高了6%和12%.     

Investigation on microstructure and mechanical properties ofnano ceramic coating on AZ31 magnesium alloys

In order to improve the wear resisting property of magnesium alloy’s surface coating, Al2O3 nano ceramic coating on the surface of AZ31 magnesium alloy is prepared using the magnetron sputtering process. Influences of temperature, power and time on hardness of surface layer are discussed by orthogonal method. Morphology, phases and composition of coatings are analyzed by SEM, XRD and EDS. The results show that the time and power are important factors to affect hardness and wear resistance. The process parameters of 80 ℃,200 W and 3 h are the optimal sputtering process. Through this process, the thickness of nano Al2O3 coating on AZ31 is about 2 to 10 μm and the grain size is about 30 nm. The surface hardness of ceramic coating reaches up to 1 360 MPa, and increases more than 77.31% of the substrate hardness of nano Al2O3 coating.     

化学沉积Ni-Fe-P及Ni-Fe-P-B合金膜的结构和显微硬度

利用X射线衍射方法研究了不同Na2H2PO2的质量浓度以及热处理温度条件下化学镀三元Ni-Fe-P和四元Ni-P-B镀层的结构，在温度为200-700℃范围内加热镀层产生结构变化，当热处理温度等于或低于400℃时，镀层的显微硬度随温度增加，这与从Ni-P-B镀层非晶基底中析出（Fe,Ni)固溶体，Ni3P相以及从Ni-P-B镀层（Fe,Ni）固溶体基底中析出Fe2B等相有关，热处理温度大于或等于500℃时，NiP,Fe3P,Fe2B等相析出，同时随温度增加颗粒逐渐粗化，引起镀层软化，在Ni-Fe-P镀层中加入KBH4，经300℃热处理引起镀层显微硬度增加，低于300℃热处理对镀层硬度影响不明显，该现象可由B与Ni-Fe固溶体基底形成了晶化相加以证实。