 共查询到20条相似文献,搜索用时 93 毫秒
1.
对普通木质刨花板、麦秸刨花板及稻草刨花板进行了密度、含水率、吸水厚度膨胀率、静曲强度和弹性模量、内结合强度、表面结合强度及握钉力的测试,结果表明,麦秸刨花板在强度方面不及木质刨花板,稻草刨花板在抗弯性能上也无法满足要求,两种秸秆板的握钉力都较差。产生上述差距的关键原因是板坯的密度,另外,与原料形态、加工工艺、机械设备等也有关系。  相似文献   

2.
改性UF麦秸均质刨花板的工艺研究   总被引:2,自引:1,他引:1  
张洋  华毓坤 《林产工业》2001,28(6):15-18
通过试验确定了麦秸均质刨花板的主要工艺参数。其结果表明:10mm厚麦秸均质刨花板的较优工艺参数为热压温度150℃、热压时间8min、表层麦秸刨花的施胶量为10%、芯层麦秸刨花的施胶量为8%、板密度0.75g/cm3、表芯层刨花比例为3:7。按照以上工艺条件压制的麦秸均质刨花板性能已达到均质刨花板的要求。  相似文献   

3.
异氰酸酯胶麦秸刨花板密度对力学性能的影响   总被引:1,自引:1,他引:0  
着重讨论了密度对异氰酸酯胶麦秸刨花板各项力学性能的影响。得出试验结论,密度与各项力学性能呈多项式回归关系;当施胶量为4%时,密度为0.6g/cm3的麦秸刨花板的力学性能完全满足国家标准要求;生产0.6g/cm3的麦秸刨花板,在技术上是可靠的,在经济上是合理的。  相似文献   

4.
以麦秸、木材碎料和无机胶黏剂制备麦秸/木材三层结构刨花板。研究麦秸与木材配比、板材密度、热压时间和温度对板材性能的影响。结果表明:随麦秸配比增加,板材抗弯性能降低,内结合强度增大,吸水厚度膨胀率(TS)减小;随密度增加和热压时间延长,板材力学性能增大,TS降低;随热压温度升高,板材力学性能先增大后减小,TS呈相反趋势。优化制板工艺为:碎料配比5:5,密度1.2g/cm~3,热压时间30min,温度100℃。  相似文献   

5.
麦秸刨花板热压工艺对成品基本特性影响的研究   总被引:3,自引:0,他引:3  
张洋  华冬  李健  刘兴凯 《林产工业》2000,27(2):23-24
研究了麦秸刨花板的热压工艺对其成品基本特性的影响。试验结果表明采用自行研制的改性脲醛胶,当热压温 度150℃,热压时间50s/mm板厚时,压制的密度为0.75s/cm3的麦秸刨花板可以达到GB/T4897-92标准中A类刨花 板优等品的要求。  相似文献   

6.
以麦秸和环保阻燃无机胶黏剂为原料,采用正交试验法对常温高压条件下无机胶黏麦秸板制备工艺进行优化,同时采用热重法和锥形量热法对麦秸板的热稳定性和燃烧性能进行测试与表征。结果表明:以密度为1.05g/cm~3、胶黏剂与麦秸比例为1.9:1和改性剂与麦秸比例为0.25:1的工艺条件制备的麦秸板:物理力学性能指标均高于国标GB/T21723—2008《麦(稻)秸秆刨花板》;热稳定性显著提高,最终质量残余率提高了53.2%;HRR、THR、SPR、TSP均大幅降低。无机胶黏麦秸板具有优异的阻燃抑烟性能。  相似文献   

7.
喷蒸真空热压水溶性酚醛胶杨木大片刨花板   总被引:3,自引:0,他引:3  
我国防水人造板生产目前普遍采用酚醛树脂胶(PF),热压周期长,生产效率低。笔者采用南京林业大学饱和蒸汽喷蒸试验压机,压制水溶性PF胶杨木大片刨花板。结果表明,采用喷蒸真空热压(SIVP)技术,热压时间可缩短到传统热压的35%左右;板的吸水厚度膨胀率(TS)缩小33%;在相同施胶量下,板的内结合强度(IB)提高的15%,同时甲醛释放量降低约24%;但板的抗弯性能有较大幅度的下降;此外,板材芯层最低密度值比传统热压的板增高,断面密度分布趋于均匀。  相似文献   

8.
为实现刨花板轻量化,通过向芯层引入聚苯乙烯(EPS)泡沫颗粒,制备平均密度为500 kg/m^3的刨花板,探索表芯层刨花构成对板材的剖面密度分布和物理力学性能的影响。结果表明:以杨木细刨花为表层、桉木粗刨花和EPS泡沫颗粒混合物为芯层制备的复合轻质刨花板,其表芯层密度差异最为显著,力学性能达到GB/T 4897-2015《刨花板》中干燥状态下使用的家具型(P2型)刨花板的要求。  相似文献   

9.
麦秸特性与麦秸刨花板制板工艺的研究   总被引:3,自引:0,他引:3  
麦秸特性与麦秸刨花板制板工艺的研究张冬梅韩广萍何灵芝(黑龙江省林产工业研究所)麦秸表面硅质含量较高,并与其它非木材原料有很大不同,而且麦秸的自身强度低于木材,只有通过采用特殊的胶粘剂才能生产出达到国家标准(GB/T4897-92)的麦秸刨花板产品。本...  相似文献   

10.
麦秸刨花板的耐水性能研究   总被引:3,自引:0,他引:3  
张洋 《木材工业》2002,16(1):17-19
本文研究了用MDI与UF两种胶粘剂以不同比率混合后制造的麦秸刨花板的耐水性能。结果表明:随着胶粘剂中MDI比率的增加,麦秸刨花板的耐水性能提高,但改善的程度逐渐趋缓;在一定范围内,提高麦秸刨花板的密度,可以降低其吸水厚度膨胀率。  相似文献   

11.
阻燃麦秸刨花板性能的研究   总被引:2,自引:0,他引:2  
王戈  刘振国 《木材工业》2001,15(5):10-13
根据麦秸板的特点,选择4种复配的阻燃剂,利用正交试验法进行制板试验,根据氧指数和烟密度指标评价其阻燃性能,同时测定板的各项物理力学性能的变化。结果表明,经过阻燃处理,麦秸板的阻燃能力有明显提高,但一些物理力学性能有所降低;研究还给出了阻燃麦秸板的较佳工艺参数。  相似文献   

12.
艾军  陆仁书 《木材工业》2001,15(2):9-10,13
研究了麦秆在不同预热处理条件下,其纤维化学性质以及制得的中密度纤维板的性能,同时结合施胶量对不同预热处理麦秆纤维板性能的影响,探讨了在麦秆纤维/脲醛树脂胶中密度纤维板生产中施胶量对板性能影响的重要性。结果表明,采用预热温度为160℃左右、预热时间5~7min的处理条件获得的麦秆纤维在16%左右的施胶量时,可获得满足GB/T 11718-1999标准的麦秆纤维/脲醛树脂胶中密度纤维板。  相似文献   

13.
一诺稻/麦秸板生产工艺及应用前景   总被引:1,自引:0,他引:1  
何磊  郭星恺 《木材工业》2004,18(5):34-36
本文介绍了一诺(INO)天然纤维联合公司生产稻/麦秸板的工艺技术及设备特点,分析了一诺板在欧洲的发展动向及在我国的开发前景,并针对我国国情提出了发展稻/麦草等非木材人造板的建议。  相似文献   

14.
介绍了定向刨花板的试验方法和过程;并应用概率设计理论求出了定向刨花板主方向的弹性模量,对定向刨花板产品进行了试验研究并与实验室产品进行了分析比较;分析了影响定向刨花板产品质量的主要因素。解决了定向刨花板弹性模量的理论求解公式的实验验证问题,论证了理论推导结果的正确性,尝试将现代设计方法和微观力学理论应用于人造板的力学性能分析和研究中,以推动定向刨花板的计算机仿真工作的开展。  相似文献   

15.
China is one of the major production countries forwood-based panel products, and its production wasranked in the second place in the world in 2003. Onthe other hand, however, China is also a country withshortage of forest resources. As the main raw material,wood supply is becoming a serious problem with thefast growing of panel production. Fortunately, thereare plenty of agricultural residues in China, and thisgives the possibility to use agri-based fibers instead ofwood. Many wood-based pane…  相似文献   

16.
There is a growing desire to improve the properties and use of nonwood plant materials as supplements to wood materials for wood cement-bonded boards (WCBs). This study was conducted to determine the comparative properties of WCBs containing various amounts of discontinuous inorganic fiber materials, such as alkali-resistant glass fiber, normal glass fiber, mineral wool, and nonwood plant materials such as retted flax straw and wheat straw particles. Tested cement-bonded boards were made at wood/additive compositions of 100/0, 90/10, 80/20, 70/30, 60/40, and 50/50 (weight percentages). Seventy-eight laboratory-scale WCBs were produced. Various board properties, such as the modulus of rupture (MOR), internal bonding strength (IB), water absorption (WA), thickness swelling (TS), and linear expansion (LE), were studied. The test results showed that three types of discontinuous inorganic fiber used as reinforcing materials in composites significantly enhanced and modified the performance of WCBs. The mechanical properties and dimensional stability of cement-bonded board were significantly improved with increasing amounts of the additives. MOR and IB were increased; and WA, TS, and LE of boards were reduced by combination with the inorganic fiber materials. The results also indicated that combination with retted flax straw particles only slightly increased the MOR of boards, and wheat straw particles led to marked decreases in all the mechanical properties and the dimensional stability of WCBs.Part of this report was presented at the 50th Annual Meeting of the Japan Wood Research Society, Kyoto, April 2000  相似文献   

17.
一年生植物作为石膏刨花板原料的适应性   总被引:3,自引:0,他引:3  
本文叙述了使用德国及中国建筑石膏和甘蔗渣、竹材、棉秆、麦秸、稻草等一年生植物生产石膏刨花板的适应性,分析了石膏的成分和性能,测定了缓凝剂和植物原料对石膏水化的影响。制板时采用不同的配方和板的密度,以评价一年生植物的使用价值。在所使用的原料中,甘蔗渣是良好的石膏刨花板原料。  相似文献   

18.
选用农作物秸秆-麦秸粉和热塑性塑料-高密度聚乙烯(HDPE)为原料,添加马来酸酐接枝聚乙烯(MAPE)为改性剂,利用单双螺杆挤出机组,采用熔融挤出方式制备麦秸塑料复合材料。在其它条件固定的情况下,研究双螺杆挤出机温度、转速和麦秸粉含量等因素对麦秸塑料复合材料冲击强度的影响,设计二次正交旋转回归组合试验方案对双螺杆挤出工艺进行优化。麦秸塑料复合材料的冲击强度与双螺杆挤出机的温度和转速以及原料中麦秸粉添加比例存在一定的相关性,通过试验建立了麦秸塑料复合材料冲击强度(y)对双螺杆挤出机温度(x1)、转速(x2)、麦秸粉比例(x3)三个试验因素之间的正交回归模型方程:y=17.98106—0.82505x1^2-0.94349x2^2-1.00182x3^2;;从模型推知,当温度为160℃、双螺杆转速为30rpm和麦秸粉用量为60%时,冲击强度达到最大值17.98kJ/m2,实验验证结果与模型值相符。研究结果对提高麦秸塑料复合材料冲击强度和优化工艺参数具有重要的指导意义和应用价值。  相似文献   

19.
Abstract

Considering ongoing global deforestation and the increased demand for raw materials in all wood-processing sectors it is necessary to seek and employ alternative resources. Agricultural residues are potential sources of alternative lignocellulose-based raw materials. Research on substitute materials for wood panel production mainly focused on physical and mechanical properties of boards while much remains to be learned about machining. Therefore, studies were carried out to analyse the relationship between ash and silica content and their impact on tool wear. Ash and silica contents of agricultural residues were determined following ISO 3340. Particle morphology and elemental composition of selected materials were analysed using scanning electron microscopy and energy-dispersive X-ray analysis. Tool wear tests were carried out using particleboards made from wheat straw, canola straw and spruce. Analyses of various plant materials displayed no correlation between ash and silica content. Bio-mineralised silica structures in wheat and canola were different compared to coarse silica found in wood-based particleboard. Tool wear caused by these agricultural residues was just moderately increased compared to wood, despite the fact that their silica contents were many times higher. Furthermore, the impact of abrasive substances on wear behaviour was influenced by the density of the panels.  相似文献   

20.
以麦秸碎料为主要原料,采用漆酶水浴与干法两种不同处理方法压制麦秸无胶碎料板,研究热压温度、热压压力和热压时间对板材物理力学性能的影响。试验结果表明:影响麦秸无胶碎料板物理力学性能的主要因素是热压温度;水浴处理方法压制碎料板的物理力学性能优于干法压制的碎料板;漆酶水浴处理方法较优的热压工艺参数为漆酶用量43.6U/g,含水率10%,热压温度170℃,热压压力3~4MPa,热压时间20~25min。  相似文献   