UFC和大豆蛋白制备环保脲醛树脂

采用脲醛预缩液(UFC)制备甲醛和尿素物质的量之比为1.3∶1的脲醛树脂,并在"碱-酸-碱"制备工艺的3个阶段分别加入大豆蛋白(SPI)降解液进行改性。对改性后脲醛树脂的性能进行对比分析,并借助核磁共振(13C-NMR)和动态热机械性能(DMA)分析改性后脲醛树脂的结构特征及热机械性能。结果表明,与普通脲醛树脂相比,UFC制备脲醛树脂的胶合强度提高了16%,游离甲醛降低了33%;而采用UFC和SPI降解液制备脲醛树脂,树脂胶合强度变化不大,当SPI降解液加入量为10%时,其游离甲醛可降低50%。13C-NMR分析表明,在第3个阶段加入SPI降解液,可以降低脲醛树脂中的醚键含量并提高桥键含量,使树脂具有较高的交联度和较低的游离甲醛。DMA测试结果表明,在第3个阶段加入SPI降解液所制备的脲醛树脂具有较高的热机械性能和热稳定性。     

无机硅化物接枝脲醛树脂木材胶粘剂

介绍了一种新型无机硅化物接枝脲醛树脂胶粘剂制备方法及性能,并与普通脲醛树脂进行了对比实验。该接枝脲醛树脂游离甲醛含量较低,胶合强度优良,耐水性、耐热性、耐燃性良好,适用于人造板的制造。     

高浓度甲醛制备脲醛树脂及其性能分析

以高浓度甲醛和尿素为主要原料合成脲醛树脂,借助核磁共振(13C-NMR)和动态热机械性能(DMA)分析树脂结构组成及热机械性能。结果表明,以高浓度甲醛制备的脲醛树脂具有较高的固含量,其制备的刨花板内结合强度达1.27 MPa,较普通甲醛制备的明显提高,增幅为50%。13C-NMR和DMA测试结果表明,高浓度甲醛制备脲醛树脂羟甲基含量为31.0%,而普通甲醛制备树脂羟甲基含量只为23.7%,表明前者甲醛加成反应进行更彻底;而其醚键含量较普通甲醛制备的树脂提高了一倍,同时缩聚度提高,保证了足够的机械强度。     

纳米蒙脱土改性脲醛树脂制备胶合板研究

采用纳米层蒙脱土（MMT）改性脲醛树脂制备胶合板,研究MMT在脲醛树脂合成过程中的加入方式、种类以及加入比例对胶合强度和甲醛释放量的影响.结果表明：MMT在脲醛树脂合成中加入第一批尿素（U1）,其干湿强度达到最高,游离甲醛含量最低,且都满足国家标准.对于5种不同处理MMT改性脲醛树脂进行试验,结果显示加入纳米蒙脱土后,胶合板的胶合强度均比脲醛树脂有所提高,游离甲醛有所降低,并达到E0级国家标准.综合强度和成本问题编号为DK-1N的MMT制备的胶合板,其干湿强度分别达到了3.74 MPa和1.79 MPa,板材的游离甲醛含量为0.494 mg/100 g.     

豚草提取物脲醛树脂微胶囊主要影响因子的研究

以豚草提取物为囊芯物质,以脲醛树脂为囊壁材料,探讨原位聚合法制备豚草提取物脲醛树脂微胶囊的适宜条件,结果表明:制备豚草提取物脲醛树脂微胶囊的适宜条件为:脲醛树脂预聚体制备时间1.0~1.5 h,尿素与甲醛质量比1.0:1.5~1.0:2.5,芯壁比1:2,成囊pH1.5~2.5,成囊时间60~90 min,搅拌速度200~400 r·min-1。制备的微胶囊包封率与载药量均达到80%以上,微胶囊外部形态规则,表面较光滑。     

硅灰石矿物粉改性脲醛树脂胶黏剂的研究

用未改性硅灰石[Ca_3(Si_3O_9)]矿物粉和硅烷类改性硅灰石矿物粉改性脲醛树脂胶黏剂,研究了硅灰石对脲醛树脂胶黏剂性能的影响和改性脲醛树脂制备的刨花板的胶合性能。研究结果表明,硅灰石矿物粉及其添加量对UF胶的固体含量、pH值、黏度、接触角、固化时间均有一定的影响,所制备的刨花板与用原胶相比胶合性能有不同程度的降低,随着硅灰石添加量的增加,刨花板的吸水厚度膨胀率增加,内结合强度有一定程度下降,但可以达到刨花板国家标准的要求。硅灰石矿物粉作为脲醛树脂胶黏剂改性剂是可行的。     

纳米结晶纤维素改善脲醛树脂胶黏剂游离甲醛的研究

为了降低脲醛树脂胶黏剂的游离甲醛释放量,以俄罗斯落叶松浆粕为原料,利用酸水解,硅烷偶联剂改性等制备获得表面改性纳米结晶纤维素(M-NCC),并将M-NCC作为吸附材料用于脲醛树脂基材制备胶合板,研究M-NCC对脲醛树脂胶黏剂游离甲醛的吸附效果和机理。结果表明:透射电镜(TEM)检测可知,制备的NCC颗粒长度约为100~200 nm、直径约为20~30 nm,结晶度为57.3%,相比原始纤维素提高了41.1%;硅烷偶联剂3-(2-氨乙基)-氨丙基甲基二甲氧基硅烷(MCPS)使NCC的浸润性显著增强,当MCPS用量为8%时M-NCC接枝率达到27.2%,M-NCC对脲醛树脂的接触角为65.7°,下降32.7%;由扫描电镜(SEM)照片可观测到,表面改性显著改善了低浓度NCC颗粒在脲醛树脂基材中的分散状态,当M-NCC质量分数2%时,纳米颗粒的分散性能明显下降;M-NCC可有效吸附脲醛树脂基材中的游离甲醛,当M-NCC质量分数1.5%时可致游离甲醛比对照组(0.51 mg/L)下降50.9%。     

固化剂对高浓度甲醛制备的低摩尔UF树脂性能的影响

以高浓度甲醛制备摩尔比1.1∶1的脲醛树脂,选用三种不同固化剂(NH_4Cl,HCOOH,NH_4Cl+尿素)对树脂的胶接性能和耐热性能进行分析和评价,并借助13C-NMR和DMA进行表征。研究结果表明:高浓度甲醛制备的脲醛树脂具有较高的黏度和固含量,游离甲醛含量很低,仅为0.075%。较普通脲醛树脂,其羟甲基含量、缩聚度和交联度分别提高了6.33%、5.87%和58.19%。以NH_4Cl、HCOOH作为固化剂时,树脂具有较高的胶合强度,较普通脲醛树脂分别提高了74%和78%。仅以甲酸作为固化剂时,树脂具有较优的耐热性能。     

“生物质材料的环境友好型高效阻燃技术”成果通过鉴定

2012年1月11日,国家林业局科技司组织对中国林科院木工所完成的"生物质材料的环境友好型高效阻燃技术"成果进行了鉴定。"生物质材料的环境友好型高效阻燃技术"是在科技部国际科技合作项目的支持下取得的。该技术在阻燃三聚氰胺改性脲醛树脂制备技术和阻燃木质表面装饰层积材制备技术方面均取得重要突破。开发的阻燃三聚氰胺改性脲醛树脂     

不同胶黏剂制备刨花模压托盘的性能

采用3种胶黏剂以不同施胶量制备刨花模压托盘,性能测试结果表明:MDI胶制备刨花模压托盘的综合性能最好,几乎无甲醛检出,为无醛添加级别;其次是酚醛树脂胶制备的刨花模压托盘,脲醛树脂胶制备的刨花模压托盘的综合性能相对较差。MDI胶制备的托盘性能优良,在医药、电子、食品等行业或潮湿环境的货物运输及仓储中具有竞争优势,而脲醛树脂胶和酚醛树脂胶制备的托盘多用于一般货物运输以及化工、能源等行业。     

低甲醛释放脲醛树脂胶粘剂研究进展

对脲醛树脂的合成、固化以及甲醛释放机理的研究进展进行了概述，并简要综述了国内外近几十年来对于树脂改性所做的工作，重点从合成过程中和树脂固化后如何降低甲醛量这两方面介绍其改性机理的研究进展。     

Formaldehyde emission and high-temperature stability of cured urea-formaldehyde resins

A test method for measuring formaldehyde from urea-formaldehyde (UF) resins at high temperature was developed and used to assess the influence of the reaction pH on the formaldehyde emission and heat stability of the cured resins. Additionally, solid-state¹³C CP/MAS nuclear magnetic resonance (NMR) techniques were used to investigate the structure of cured UF resins before and after high temperature heating. Formaldehyde emissions during the cure were related to the UF resins' methylol group content. The heat stability of cured UF resins synthesized under strongly acidic conditions was much higher than that of the other resins, which were prepared in weakly acidic and alkaline media. Solid-state¹³C CP/MAS NMR spectra showed that formaldehyde emission from cured UF resins after heating is mainly ascribable to decreased methylol groups and dimethylene ether linkages. Significantly, it was revealed that uron structures characteristically found in the cured UF resin synthesized under strongly acidic medium indicated high heat stability.Parts of this paper were presented at the 44th annual meeting of the Japan Wood Research Society, Nara, April 1994; and at the 52nd annual meeting of the Forest Products Society, Merida, Mexico, June 1998     

Penetration of urea–formaldehyde resins with different formaldehyde/urea mole ratios into softwood tissues

In order to understand the impact of formaldehyde/urea (F/U) mole ratio on penetration characteristics of urea–formaldehyde (UF) resin into softwood tissues, a quantitative measurement of UF resin penetration into radiata pine (Pinus radiata) tissues from the bond-line was undertaken. Four different F/U mole ratios (1.6, 1.4, 1.2, and 1.0) of UF resins with different viscosities and two levels of hardener (NH₄Cl) for two extreme F/U mole ratios (1.6 and 1.0) were studied. Firstly, field emission scanning electron microscope and confocal laser scanning microscopy were used to localize UF resins in the bond-line for the qualitative evaluation of resin penetration. Then light microscopy was employed to quantitatively measure the resin penetration and bond-line thickness. A decrease in the F/U mole ratio of UF resin that proportionately decreased the resin viscosity resulted in an increase in the average resin penetration and a decrease in the bond-line thickness. Higher hardener level provided a greater resin penetration with all F/U mole ratio UF resins. These results demonstrated that F/U mole ratio had an impact on the penetration and bond-line thickness of UF resins, owing to differences in the reactivity of resins, with higher F/U mole ratio resins being more reactive.     

脲醛树脂研究进展

本文对脲醛树脂的甲醛释放、合成与反应机理、低摩尔比脲醛树脂的合成、树脂化学构造分析、固化机理进行了综述。并介绍了脲醛树脂合成方法与树脂化学构造的关系,以及强酸性条件下合成低摩尔比脲醛树脂固化机理的最新研究成果。     

稻草中密度纤维板用改性脲醛树脂的研究

对比三聚氰胺、二甲基硅油、硅树脂和偶联剂KH-550四种改性剂改性的脲醛(UF)树脂性能的差别及其对稻草中密度纤维板性能的影响,并进行经济评价,最终确定适用于稻草纤维板的改性UF树脂的工艺条件,同时借助于红外光谱(FT-IR)和差热扫描分析(DSC)研究最佳改性UF树脂的结构和固化特性.结果表明,三聚氰胺改性脲醛(MUF)树脂不论是对树脂性能、板性能改善还是从成本分析方面均为稻草纤维板最佳的胶黏剂,FT-IR显示出与未加三聚氰胺相比,加入三聚氰胺后树脂的羟甲基含量降低了10 %,DSC分析则表明其峰值温度有较大幅度的提高,但放出的热量较少.加入三聚氰胺改性的UF树脂其表面张力变小.     

脲醛树脂分子量分布与胶合性能关系的研究（续）：分次加尿素对脲醛树？…

主要探讨分次加尿素对脲醛树脂分子量分布及胶合性能的影响。研究结果表明：在脲醛树脂合成吕，分次加入尿素，不仅可起到降低胶中游离醛的作用，同时还可起到分子量的调解作用。尤其是加入第２次尿素时，对胶中大分子部分可起到降解重排、减少胶中醚键含量的作用，从而达到低毒的目的。加入第２次尿素时，可能会改变脲醛树脂的反应机理。     

脲醛树脂结构研究进展

在过去的２０余年里,为获得结构更合理、性能更优异的脲醛树脂,人们使用近代分析手段对脲醛树脂结构进行了广泛的研究,付立叶变换红外光谱（ＦＴＩＲ）和１３Ｃ核磁共振（１３ＣＮＭＲ）是目前脲醛树脂结构研究的最主要方法,其中１３ＣＮＭＲ是在分子水平描述脲醛树脂结构的最完善、最有效的工具。本文综述近２０年脲醛树脂结构研究进展,内容包括结构研究方法、内容和结果。     

Properties of wheat straw particleboards bonded with different types of resin

Wheat straw particleboard bonded with a urea–formaldehyde (UF) resin, usually employed in the manufacture of wood-based particleboards, or with a resin based on epoxidised oil was manufactured using a compression molding machine. The effects of resin type on internal bond strength, flexural modulus, and thickness swelling were examined. The properties of boards using UF resins were poor. Internal bond strength and thickness swelling, linked to adhesion quality, were especially low. The high compatibility between straw particles and oil-based resin was explained in terms of straw surface free energy. In straw, this parameter exhibits a much lower polar component than wood species and leads to higher compatibility with resins based on oil than with water-soluble systems like UF.     

低毒快速固化酚醛树脂胶研制及应用

用复合催化剂和先进缩聚工艺制得的快速固化酚醛树脂胶具有低毒和快速固化的优点添加5％～10％固化剂 可使酚醛树脂胶的热压温度、热压时间与脲醛树脂胶相近。该胶适用于制造室外级胶合板、刨花板、中纤板。     

一种脲醛树脂胶粘剂的设计

鉴于对文献的分析和实验验证,本文提出一种脲醛树脂胶粘剂的设计原则。即:1)脲醛树脂最终摩尔比应取1.40～1.20:1,这样可以使制成的板材具有足够的胶接强度;2)为了使人造板的甲醛释放量达到10mg/100g(穿孔法)以下,树脂中的游离尿素应在10%以上;3)在脲醛树脂的分子中引入尿素的环状衍生物,如三嗪环或Uron。环状化合物含量最好在10%左右。按此原则合成了三种树脂,在试验室按标准刨花板和中密度纤维板工艺制成板材,其甲醛释放量在10mg/100g左右,板材物理力学性能均超过国家标准和企业标准。