剪力连接件是保证GFRP混凝土组合梁/板中两种不同材料共同工作的重要构造,设计了矩形肋和T形肋两类GFRP肋式剪力连接件,进行了3组共8个GFRP肋式剪力连接件的推出试验,包括：矩形肋开孔、T形肋开孔、T形肋不开孔3组GFRP肋式剪力连接件,得到了其破坏形态、极限承载力、荷载滑移曲线及荷载应变变化规律,重点研究肋内开孔及肋的截面形式对GFRP肋式剪力连接件受力性能的影响。试验结果表明：GFRP肋式剪力连接件的破坏形态均为混凝土劈裂破坏;对比矩形肋开孔试件,T形肋开孔试件强度高、延性好;对比T形肋不开孔试件,T形肋开孔试件强度与延性均能提高。基于试验结果,建立了考虑肋内开孔及肋截面形式影响的GFRP肋式剪力连接件极限承载力计算公式,拟合得到了GFRP肋式剪力连接件的荷载滑移曲线上升段的理论模型,建立了其抗剪刚度计算公式。     

T形板肋对预制带肋底板混凝土叠合板弯曲疲劳性能的影响

为研究T形板肋对预制带肋底板混凝土叠合板弯曲疲劳性能的影响,对3块T形肋底板叠合板和1块整浇板进行弯曲疲劳性能对比试验,主要考察T形板肋与疲劳荷载幅值对试件疲劳破坏形态及疲劳损伤程度的影响,得到了在不同疲劳循环加载次数下的跨中动位移、混凝土应变、预应力筋应变、残余变形等,分析了在不同疲劳循环加载次数下的刚度退化情况、荷载-应变分布规律、裂缝分布规律及剩余承载力等。研究结果表明,经历200万次疲劳循环加载后,T形肋底板叠合板无明显的刚度和强度退化,增设T形板肋的叠合板能达到与整浇板相同的弯曲疲劳性能;T形肋底板叠合板正截面弯曲疲劳强度计算可采用普通预应力混凝土受弯构件正截面疲劳应力验算的4个假定,最终以此建立了其正截面弯曲疲劳强度验算方法。     

高速铁路隧道基底软岩动力累积损伤特性

利用相似材料模拟高速铁路隧道基底软岩,采用荷载控制和非对称正弦波循环加载方式对软岩试件进行动三轴疲劳与损伤检测综合试验。通过试验结果分析,建立了软岩3参数多项式疲劳寿命计算模型和4参数多项式累积损伤参量计算模型,获得了软岩疲劳损伤特性,即：软岩疲劳破坏表现为端部拉-剪复合破坏和中部压-剪复合破坏两种模式;疲劳破坏全过程表现为初始微孔隙压密、裂纹发生与稳定扩展以及损伤裂纹加速发展3个发展阶段;软岩疲劳寿命主要取决于本身强度和动应力水平,强度愈高、动力应力水平愈低,其疲劳寿命就越长;当动应力水平相同时,软岩疲劳寿命与其弹性模量呈线性增长关系。     

索承式桥梁吊索钢丝腐蚀疲劳寿命评估

根据吊索镀锌钢丝腐蚀疲劳破坏特点，把镀锌钢丝腐蚀疲劳纹形成和扩展过程分解成镀锌层腐蚀失效、蚀坑萌生、蚀坑形成、短裂纹扩展、长裂纹扩展和断裂破坏等阶段，建立各阶段时间表达式，得到镀锌钢丝疲劳寿命表达式，提出基于断裂力学的吊索钢丝腐蚀疲劳寿命评估研究结果方法。通过算例分析复杂运营条件下腐蚀环境和应力幅等因素对吊索钢丝腐蚀疲劳寿命的影响，研究结果表明：吊索钢丝腐蚀疲劳寿命主要由钢丝镀锌层腐蚀、蚀坑发展和短裂纹扩展等3个阶段组成，为了准确地评估吊索腐蚀疲劳寿命，需要掌握大桥的运营环境和交通荷载。     

冻融环境下钢筋与粉煤灰混凝土的粘结性能

通过对内贴应变片钢筋的直接拔出试验,分析冻融作用下粉煤灰掺量对钢筋与粉煤灰混凝土间粘结性能的影响,得出冻融循环作用对钢筋与粉煤灰混凝土之间粘结性能的影响规律。试验结果表明：钢筋与粉煤灰混凝土的粘结强度随粉煤灰掺量的增加而降低;当粉煤灰掺量一定时,随着冻融循环次数的增加,混凝土强度有所下降,钢筋与粉煤灰混凝土间极限粘结强度降低;当粉煤灰掺量较大,达到40%时,随冻融次数的增加,钢筋粉煤灰混凝土试件极限粘结强度的下降幅度明显减缓,极限粘结强度对应的滑移量增大。表明掺入较多粉煤灰可使试件的冻融损伤现象得到缓解,冻融环境下钢筋混凝土的粘结性能得到提高。     

冷却剂参数对铣槽喷管低周疲劳寿命的影响

采用有限体积流固耦合计算方法、非线性有限元热结构耦合分析方法和局部应变法研究大面积比铣槽喷管三维再生冷却槽道在循环工作条件下的热结构变形与低周疲劳寿命,并对比分析了冷却剂质量流量与入口温度对铣槽喷管疲劳使用寿命的影响。计算结果表明,铣槽喷管热结构响应呈现复杂的三维效应,应变较大位置主要分布在与肋连接的内衬区域,喷管中部的残余应变量最大;冷却槽道低周疲劳寿命分布和热结构响应基本一致,最小寿命位于喷管中部与肋相连的内衬区域燃气侧;随冷却剂质量流量增加,铣槽喷管低周疲劳寿命不断提高;随冷却剂入口温度增加喷管尾部低周疲劳寿命值不断降低,而喷管中前部的低周疲劳寿命值却不断提高,当冷却剂入口温度为280K左右时,本文的铣槽喷管总体使用寿命达到最大。      

油菜秸秆灰分混凝土与钢筋之间粘结性能研究

为了探究油菜秸秆灰分的掺入对钢筋-混凝土之间粘结性能的影响。对3种不同油菜秸秆灰分掺量的钢筋-油菜秸秆灰分混凝土试件进行中心拉拔试验,并与钢筋-普通混凝土粘结性能作对比试验。结果表明:钢筋-油菜秸秆灰分混凝土粘结强度与混凝土抗压强度呈正相关。当水胶比一定时,随着油菜秸秆灰分掺量的增加,钢筋-油菜秸秆灰分混凝土的粘结强度降低。水胶比为0.47时的钢筋-油菜秸秆灰分粘结性能与普通混凝土最为接近,为最优配合比。由试验结果可知,在承重要求较低的普通钢筋混凝土结构中,采用适量油菜秸秆灰分等量替代水泥,对于节省水泥生产能源和科学合理利用农业废弃物两方面均具有重要意义。     

高强钢绞线网加固混凝土粘结性能试验研究

通过高强钢绞线网聚合物砂浆加固层与混凝土结构的剥离破坏试验，对加固层与混凝土界面的剥离破坏特征进行了研究。探讨了单侧加固、植筋加固及U型加固等不同的加固方式对加固层抗剪承载力及抗剪强度的影响。试验结果表明，采用U型加固等增加粘结面积的方式能有效提高加固层粘结面抗剪承载力，但同时会削弱加固层的抗剪强度，而在界面上植入抗剪钢筋后，能同时提高聚合物砂浆加固层的抗剪承载力及抗剪强度。根据试验结果，提出了最小植筋率的建议值。     

配置500 MPa纵筋钢筋混凝土框架顶层端节点抗震性能试验研究

按照《混凝土结构设计规范》(GB 50010—2010)设计了6个配置500 MPa纵筋的钢筋混凝土框架顶层端节点,并进行了低周反复加载抗震性能试验,验证了规范规定的抗震措施对配置500 MPa钢筋的顶层端节点的有效性,分析了配置500 MPa级钢筋的顶层端节点的受力特点、节点区的破坏形态以及节点的综合抗震性能,并与受力条件基本相同的配置HRB335级纵筋节点的受力性能进行了对比,对采用不同延性指标评价配置不同强度钢筋节点的延性性能差异进行了讨论。     

改性竹筋混凝土受弯构件力学性能试验研究

针对竹筋混凝土结构存在的问题,提出了多种对竹筋的改性方法。在此基础上,对12根采用不同配筋和不同改性方法的受弯构件(11根竹筋混凝土梁和1根钢筋混凝土梁)进行了试验研究,分析了不同改性方法和不同配筋率竹筋混凝土受弯构件的力学性能、破坏形态及其影响因素。研究结果表明：竹筋能有效提高混凝土受弯构件的承载能力;经过适当方法改性后的竹筋能确保竹筋和混凝土之间的有效粘结,其正截面强度计算可以采用平截面假定;竹筋混凝土受弯构件的破坏均为脆性破坏,其破坏形态与其截面配筋率有关。     

Reinforced Concrete Beam's Stiffness Degeneration Regulation and its Calculation Formula Under the Action of Fatigue Load

Fatigue failure is a fatal damage for the reinforced concrete structure bearing fatigue load repeatedly. That how to estimate or describe the degree of fatigue damage is a challenge in areas of structure damage and lifespan estimation. Structure's stiffness degenerates irreversibly along with the damage progress. There is a certain inherent relevance between stiffness degeneration and fatigue damage. A series of fatigue tests were carried out to study stiffness degeneration regulation due to its simplicity and feasibility. According to the test results, reinforced concrete beam's stiffness degeneration presents a three-stage rules obviously, and the stiffness degeneration curves accord with "S" style. Based on the stiffness degeneration regulation, the reinforced concrete beams' stiffness degeneration calculation formula is obtained by fitting experimental data. The formula has a perfect goodness of contact area with 10 test beams' experimental results, and it can describes reinforced concrete beams' stiffness degeneration perfectly. The formula can be used to forecast the deformation developing. Meanwhile, the residual life of the structure can be used to decision structure's fatigue fracture and the degree of performance degradation.     

Experimental Analysis for Steel Box Concrete Composite Beam of Arch Bridge

A new steel concrete composite structure was proposed which composed of steel box beam, PC beam and PBH Shear connection. Bend test was carried out for the performance study of deformation and stress. It was found that Material advantages of steel and concrete were fully used and crack of concrete and local instability of steel box were avoided. And the deformation between steel box and concrete can be smoothed with PBH shear connection. As the calculated values showed good agreements with the test results, the proposed formulas can be reliably applied to the practice analysis. With the different parameters analysis, mechanic performance of the composite was obtained.     

Simulation Analysis of Flexural Performance of Reinforced Concrete Beam in Salt-frost Environment

Considering the damage of concrete mechanical properties and bonding behavior between the steel bar and concrete after the freezing and thawing function in the numerical simulation, the nonlinear analysis on flexural performance of reinforced concrete beam which experiences different salt-frost cycles is conducted, and the evolution law of resistance performance of reinforced concrete beam is studied. It is shown that, in the salt-frost environment, the decrease of concrete mechanical properties is the main reason that causes the degeneration of RC beam on flexural performance, while the reduction of bonding property has an unobvious effect on the beam resistance performance. When the salt-frost cycles reach a certain level, the beam failure pattern would change from the under-reinforced failure to over-reinforced failure. The freeze-thaw damage of bonding property in the beam-ends anchorage zone has a certain effect on the beam resistance behavior, especially for the more serious freeze-thaw degree, the resistance performance of the beam reduces about 4% than the perfect anchor beam.     

冻融损伤对再生混凝土耐久性及与钢筋粘结性能分析

制作掺入引气剂和未掺入引气剂的100%粗骨料取代率的再生混凝土RC1和RC2两组试件以及掺入引气剂和未掺入引气剂的普通混凝土NC1和NC2两组试件,并分别对经过不同次数冻融循环试件的抗压强度、质量损失率、动弹性模量损失率进行研究。结果表明,冻融后各组试件的抗压强度、质量损失率及动弹性模量损失率均降低,对于添加引气剂的NC1和RC1两组试件损失较小,其中RC1组试件在200次冻融后抗压强度损失接近40%,质量损失率达0.5%,动弹性模量损失率38.5%。100%取代率并加入引气剂的ZRC组试件冻融后进行中心拨出实验,发生劈裂破坏和钢筋拔出破坏2种形式。再生粗骨料混凝土与钢筋的极限粘结应力均随冻融次数的增加而降低,200次冻融后极限粘结应力下降33.5,荷载滑移曲线既有上升段也有下降段。     

Experimental study on the mechanical behavior of eccentrically loaded steel tubular columns filled with structural steel and concrete

Considered strength classes of concrete, ratio of structural steel to concrete, ratio of steel tube to concrete and eccentricity ratio of load, 6 test specimens of steel tubular columns filled with structural and concrete are designed. The damage phenomena of specimens are described in detail and the failure mechanism is analyzed. The results show the initial failure of the specimens are began from the yield of steel tube, the ultimate failure are ended from the buckling of steel tube caused by the expansion of core concrete. Due to the existence of structural steel, the ductility of specimens is superior to steel tubular columns. Before the yield of steel tube, the plane cross-section assumption of specimens can be put into use. The ultimate bearing capacity of specimens is increased with the increase of strength classes of concrete, ratio of structural steel to concrete and ratio of steel tube to concrete. But the ultimate bearing capacity and ductility are decreased with the increase of eccentricity ratio.